Bio-Based PBT-DLA Copolyester as an Alternative Compatibilizer of PP/PBT Blends

The aim of this work was to assess whether synthesized random copolyester, poly(butylene terephthalate-r-butylene dilinoleate) (PBT–DLA), containing bio-based components, can effectively compatibilize polypropylene/poly(butylene terephthalate) (PP/PBT) blends. For comparison, a commercial petrochemical triblock copolymer, poly(styrene-b-ethylene/butylene-b-styrene) (SEBS) was used. The chemical structure and block distribution of PBT–DLA was determined using nuclear magnetic resonance spectroscopy and gel permeation chromatography. PP/PBT blends with different mass ratios were prepared via twin-screw extrusion with 5 wt% of each compatibilizer. Thermogravimetric analysis, differential scanning calorimetry, and dynamic mechanical analysis were used to assess changes in phase structure of PP/PBT blends. Static tensile testing demonstrated marked improvement in elongation at break, to ~18% and ~21% for PBT–DLA and SEBS, respectively. Importantly, the morphology of PP/PBT blends compatibilized with PBT–DLA copolymer showed that it is able to act as interphase modifier, being preferentially located at the interface. Therefore, we conclude that by using polycondensation and monomers from renewable resources, it is possible to obtain copolymers that efficiently modify blend miscibility, offering an alternative to widely used, rubber-like petrochemical styrene compatibilizers.

The Compatibilization Effects of Alkylated-grafted-Graphene Oxide on Polypropylene/Polystyrene Blends

Modified graphene oxide (GO) was synthesized by covalently grafted alkylated chains on GO sheets and their compatibilization effects on the morphologies and mechanical properties of immiscible polypropylene/polystyrene (PP/PS) blends were investigated. Alkylated-grafted-GO/PP/PS batches were fabricated by melt-mixing approach and displayed different morphologies with various modified GO loadings. When the content of alkylated-grafted-GO is 0.2 wt%, the tensile strength of obtained composite could reach 17.97 MPa, showing a 36.3% enhancement compared to that of pristine PP/PS, indicating the positive compatibilization of modified GO in polymer blends. Moreover, the mixing order also plays an important role in achieving the desired improvement in properties. Due to the preferential location of modified GO in PP phase, a favorable “transition zone” could be formed at the interfacial region of two polymers when alkylated-grafted-GO was premixed with PS and subsequently mixed with PP, leading to an improvement of compatibilization between two polymers and an enhancement of mechanical properties. However, serious phase separation and declined tensile strength were obtained with a reversed mixing sequence.