Comparative thermal degradation studies on glycolide/trimethylene carbonate and lactide/trimethylene carbonate copolymers

Incorporation of biguanide compounds into poly(GL)-b-poly(GL-co-TMC-co-CL)-b-poly(GL) monofilament surgical sutures

A new biodegradable coating was developed for bioabsorbable monofilament sutures. Specifically, a random copolymer having 35wt-% and 65wt-% of lactide and trimethylene carbonate units showed appropriate flexibility, stickiness and degradation rate, as well as capability to produce a complete and uniform coating. Monofilament sutures of polyglycolide-b-poly(glycolide-co-trimethylene carbonate-co-ε-caprolactone)-b-polyglycolide were loaded with chlorhexidine (CHX) and poly(hexamethylene biguanide) (PHMB) to explore the possibility to achieve antimicrobial activity without adverse cytotoxic effects. To this end, two processes based on single drug adsorption onto the suture surface and incorporation into the coating copolymer were used and subsequently evaluated. Although the second process could be considered more complex, clear benefits were observed in terms of drug loading efficiency, antimicrobial effect and even lack of cytotoxicity. In general, drugs could be loaded in an amount leading to a clear bacteriostatic effect for both Gram-negative and Gram-positive bacteria without causing significant cytotoxicity. Release profiles of PHMB and CHX were clearly different. Specifically, adsorption of the drug onto the fiber surface which prevented complete release was detected for PHMB. This polymer had advantages derived from its high molecular size, which hindered penetration into cells, thus resulting in lower cytotoxicity. Furthermore, bacterial growth kinetics measurements and bacterial adhesion assays showed greater effectiveness of this polymer.

In vivo degradation of copolymers prepared from L-lactide, 1,3-trimethylene carbonate and glycolide as coronary stent materials

A series of high molecular weight polymers were prepared by ring opening polymerization of L-lactide (L-LA), 1,3-trimethylene carbonate (TMC) and glycolide using stannous octoate as catalyst. The resulting polymers were characterized by gel permeation chromatography, (1)H nuclear magnetic resonance, differential scanning calorimeter and tensile tests. All the polymers present high molecular weights. Compared with PLLA and PTLA copolymers, the terpolymers exhibit interesting properties such as improved toughness and lowered crystallinity with only slightly reduced mechanical strength. In vivo degradation was performed by subcutaneous implantation in rats to evaluate the potential of the copolymers as bioresorbable coronary stent material. The results show that all the polymers conserved to a large extent their mechanical properties during the first 90 days, except the strain at break which exhibited a strong decrease. Meanwhile, significant molecular weight decrease and weight loss are detected in the case of terpolymers. Therefore, the PTLGA terpolymers present a good potential for the development of totally bioresorbable coronary stents.

Heteroleptic tin(II) initiators for the ring-opening (co)polymerization of lactide and trimethylene carbonate: mechanistic insights from experiments and computations

The tin(II) complexes {LO(x)}Sn(X) ({LO(x)}(-) =aminophenolate ancillary) containing amido (1-4), chloro (5), or lactyl (6) coligands (X) promote the ring-opening polymerization (ROP) of cyclic esters. Complex 6, which models the first insertion of L-lactide, initiates the living ROP of L-LA on its own, but the amido derivatives 1-4 require the addition of alcohol to do so. Upon addition of one to ten equivalents of iPrOH, precatalysts 1-4 promote the ROP of trimethylene carbonate (TMC); yet, hardly any activity is observed if tert-butyl (R)-lactate is used instead of iPrOH. Strong inhibition of the reactivity of TMC is also detected for the simultaneous copolymerization of L-LA and TMC, or for the block copolymerization of TMC after that of L-LA. Experimental and computational data for the {LO(x)}Sn(OR)complexes (OR=lactyl or lactidyl) replicating the active species during the tin(II)-mediated ROP of L-LA demonstrate that the formation of a five-membered chelate is largely favored over that of an eight-membered one, and that it constitutes the resting state of the catalyst during this (co)polymerization. Comprehensive DFT calculations show that, out of the four possible monomer insertion sequences during simultaneous copolymerization of L-LA and TMC: 1) TMC then TMC, 2) TMC then L-LA, 3) L-LA then L-LA, and 4) L-LA then TMC, the first three are possible. By contrast, insertion of L-LA followed by that of TMC (i.e., insertion sequence 4) is endothermic by +1.1 kcal mol(-1), which compares unfavorably with consecutive insertions of two L-LA units (i.e., insertion sequence 3) (-10.2 kcal mol(-1)). The copolymerization of L-LA and TMC thus proceeds under thermodynamic control.