Melting Temperature Depression of Polymer Single Crystals: Application to the Eco-Design of Tie-Layers in Polyolefinic-Based Multilayered Films

In this paper, we describe a method for determining polymer compatibility, which will aid in establishing the requirements of polyolefinic materials for the eco-design of multilayer films for mechanical recycling while avoiding the use of reactive tie layers. Our ultimate goal is to define the molecular characteristics of the polyolefinic structural layer that improve compatibility with the tie layer during mechanical recycling. We have investigated the melting temperature depression of single crystals of various polyethylenes embedded in commercial polymeric matrices with various functionalities (ester, acrylate, acetate and methacrylic acid sodium ionomer), which can be potentially used as tie layers. We demonstrate how the concentration and molecular architecture of the matrices affect the melting temperature of the embedded single crystals differently depending on the latter's molecular architecture. The main finding indicates that the tie layers are more compatible with linear polyethylene than with branched polyethylenes. Indeed, our results show that the heterogeneous Ziegler-Natta linear low-density polyethylene is incompatible with all of the tie layers tested. The depression of melting temperatures observed are in excellent agreement with the results obtained by investigating the rheological behaviour and morphological features of solution-mixed blends in which segmental interactions between polymeric chains have been, in theory, maximized. Because Ziegler-Natta linear density polyethylene is one of the most commonly used polymers as a structural layer in multi-layer applications, the findings of this study are useful as they clearly show the unsuitability of this type of polyethylene for recycling from an eco-design standpoint. The specific molecular requirements for polyethylene layers (branching content less than 0.5/100 carbon atoms) can be specified for use in packaging, guiding the eco-design and valorisation of recycled multi-layered films containing this material.

Ethylene Methyl Acrylate Copolymer Toughened Poly(lactic acid) Blends: Phase Morphologies, Mechanical and Rheological Properties

The ethylene methyl acrylate copolymer (EMA), for the first time, was melt blended with poly(lactic acid) (PLA) by a twin-screw extruder to toughen PLA. The phase morphologies, mechanical, and rheological properties of the PLA/EMA blends with six weight ratios were investigated. The results showed that the addition of EMA improves the toughness of PLA at the expense of the tensile strength, flexural strength and modulus to a certain degree, and results in the transition from brittle fracture of PLA into ductile fracture. The droplet-matrix morphology is observed in the PLA/EMA blends, in which the mean diameter of EMA droplets increases and its distribution widens gradually with increasing the EMA content. The PLA/EMA blends with three weight ratios (90/10, 80/20, and 70/30) display different characteristic linear viscoelastic properties in the low frequency region, which were investigated in terms of their complex viscosity, storage modulus, and Cole-Cole plots. The interfacial tension between the PLA and EMA is calculated using the Palierne model conducted on the 80/20 PLA/EMA blend, and the calculated result is 3.3 mN/m.