Poly(Acrylonitrile-Butadiene-Styrene) as a Special β-Nucleating Agent on the Toughness of Isotactic Polypropylene

The influence of poly(acrylonitrile–butadiene–styrene) (ABS) as a special β-nucleating agent on the impact and tensile properties of isotactic polypropylene (iPP) were investigated by dynamic rheological measurements, wide-angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC), scanning electron microscopy (SEM), and mechanical properties tests. It is found that the β nucleation efficiency of ABS is closely related to its concentration, dispersibility, and molding method for the iPP/ABS blends. The content of β-crystal (K_β) rises with the incorporation of ABS and shows a maximum with the introduction of 1% ABS for compression-molded blends and 2% ABS for injection-molded blends, respectively, which is followed by a decrease in K_β. The addition of a small amount of ABS has a significant reinforcing and toughening effect on iPP. Compared with the compression-molded samples, the ABS dispersed phase in injection-molded samples has a smaller particle size and a larger specific surface area, which are favorable for stress transmission and higher β nucleation efficiency, and therefore, better tensile and impact properties can be expected.

An Effective α/β Nucleating Agent Compoundfor the Preparation of Polypropylene

The crystallization behavior and mechanical properties were investigated by mixing the traditional α-form nucleating agent (sodium benzoate, SB) and commercialized β-form nucleating agent (TMB-5) in isotactic polypropylene (iPP). Mechanical properties were evaluated by universal testing machines. X-ray diffraction (XRD) and differential scanning calorimetry (DSC) were conducted to illustrate the crystallization behavior. Polarized optical microscopy (POM) was adopted to observe the crystal morphologies. The experimental results show that the weight ratio of two types of nucleating agents determines the final crystal structure and mechanical properties of iPP. When the weight ratio of [SB] : [TMB-5] is 4 : 1, the impact strength and flexural modulus of iPP reach a maximum value. Compared with the single component β-form nucleating agent, the compound nucleating agent exhibits significant synergistic effect and shows better mechanical properties. It is expected that this new nucleation system will have potential industrial applications.