Preparation of cationic starch microspheres and study on their absorption to anionic-type substance

Cationic starch microspheres (CSMs) were prepared from lab-made neutral starch-based microspheres using a cationic adsorbent, namely 3-chloro-2-hydroxypropyltrimethyl ammonium chloride, as the cationic etherifying agent. Detection by scanning electron microscopy, Fourier transform infrared spectroscopy (FTIR), and laser diffraction techniques revealed that CSMs had coarse surfaces with good sphericity and dispersibility. Differential thermal analysis showed the lower thermostability of the CSMs' main chains. Furthermore, scores of experiments confirmed that CSMs are capable of absorption to N-(phosphonomethyl) iminodiacetic acid (PMIDA), a type of anionic substance, which is the intermediate to the preparation of glyphosate, maximally up to 95.24 mg/g. Compared with the Freundlich isotherm model, the Langmuir isotherm model can better describe the absorption process. The kinetic study showed that the pseudo-second-order model demonstrated a better correlation of the experimental data in contrast with the pseudo-first-order model. It can be therefore concluded that the rate-limiting step was the chemical absorption rather than the mass transport.

Amylose-directed synthesis of CuS composite nanowires and microspheres

Reported are the synthesis and characterization of CuS composite nanowires and microspheres in the presence of amylose. The preparation involved first the complexation of amylose with Cu(2+) of CuCl(2) at 70°C. Cu(2+) complexation was confirmed by a conductivity reduction of CuCl(2) after amylose addition. Also, the aggregation state of the amylose changed after Cu(2+) as revealed by transmission electron microscopy (TEM) and dynamic light scattering (DLS). At the Cu(2+) to α-D-glucopyranosyl unit molar ratio r of 0.70 and 1.41, the amylose aggregated into microspheres that were approximately 150 and 250 nm in diameter. Adding sodium thiosulfate resulted in the production of an amorphous precipitate consisting presumably of CuS(2)O(3). At r=0.70 and 1.41, CuS(2)O(3) precipitated inside the template of Cu(2+)/amylose microspheres as nanoparticles, while a twisted nanowire-like structure was produced at r=0.92. CuS(2)O(3) decomposed under heating at 100 °C to yield crystalline CuS nanoparticles.