Breathable and Flexible Piezoelectric ZnO@PVDF Fibrous Nanogenerator for Wearable Applications

A novel breathable piezoelectric membrane has been developed by growing zinc oxide (ZnO) nanorods on the surface of electrospun poly(vinylidene fluoride) (PVDF) nanofibers using a low-temperature hydrothermal method. Significant improvement in the piezoelectric response of the PVDF membrane was achieved without compromising breathability and flexibility. PVDF is one of the most frequently used piezoelectric polymers due to its high durability and reasonable piezoelectric coefficient values. However, further enhancement of its piezoelectric response is highly desirable for sensor and energy-harvester applications. Previous studies have demonstrated that piezoelectric ceramic and polymer composites can have remarkable piezoelectric properties and flexibility. However, devices made of such composites lack breathability and some present health risks in wearable applications for containing heavy metals. Unlike other piezoelectric ceramics, ZnO is non-toxic material and has been widely used in many applications including cosmetics. The fabrication of ZnO@PVDF porous electrospun membrane involves a simple low-temperature ZnO growth in aqueous solution, which does not weaken the polarization of PVDF created during electrospinning in the high electric field.

Fabrication of Transparent Nanohybrids with Heat Resistance Using High-Density Amorphous Formation and Uniform Dispersion of Nanodiamond

A new technology for the production of transparent material using a "crystalline" polymer is proposed in the present study. Further, transparent and flexible crystalline polymer nanohybrid film containing well-dispersed nanodiamond filler was fabricated. Partially fluorinated crystalline polymer with switchboard-type lamellae results in high transparency as a consequence of the formation of a high-density amorphous structure based on high-temperature drawing just below the melting point at 110 °C. Although the formation of nanohybrid materials composed of fluorinated-polymer/organo-modified nanocarbon is generally difficult, we confirmed the formation, via melt-compounding, using atomic force microscopy and wide-angle X-ray diffraction. Even though the polymer matrix/nanodiamond hybrid has remarkable aggregation properties, a well-dispersed state was achieved because of improvement in wettability obtained through surface modification of filler. The resulting nanohybrid demonstrates transparency, increased thermal degradation temperature, and enhanced mechanical properties, which seem to be derived from the nucleation effect caused by the adsorption of the terminal polymer chain onto the organic modifier.