Preparation and characterization of interpenetrating polymer network silicone hydrogels with high oxygen permeability

Bioinspired Lubricity from Surface Gel Layers

Surface gel layers on commercially available contact lenses have been shown to reduce frictional shear stresses and mitigate damage during sliding contact with fragile epithelial cell layers in vitro. Spencer and co-workers recently demonstrated that surface gel layers could arise from oxygen-inhibited free-radical polymerization. In this study, polyacrylamide hydrogel shell probes (7.5 wt % acrylamide, 0.3 wt % N,N'-methylenebisacrylamide) were polymerized in three hemispherical molds listed in order of decreasing surface energy and increasing oxygen permeability: borosilicate glass, polyether ether ketone (PEEK), and polytetrafluoroethylene (PTFE). Hydrogel probes polymerized in PEEK and PTFE molds exhibited 100× lower elastic moduli at the surface (E PEEK * = 80 ± 31 and E PTFE * = 106 ± 26 Pa, respectively) than those polymerized in glass molds (E glass * = 31,560 ± 1,570 Pa), in agreement with previous investigations by Spencer and co-workers. Biotribological experiments revealed that hydrogel probes with surface gel layers reduced frictional shear stresses against cells (τPEEK = 35 ± 15 and τPTFE = 22 ± 16 Pa) more than those without (τglass = 68 ± 15 Pa) and offered greater protection against cell damage when sliding against human telomerase-immortalized corneal epithelial (hTCEpi) cell monolayers. Our work demonstrates that the "mold effect" resulting in oxygen-inhibition polymerization creates hydrogels with surface gel layers that reduce shear stresses in sliding contact with cell monolayers, similar to the protection offered by gradient mucin gel networks across epithelial cell layers.

A Novel Approach to Increase the Oxygen Permeability of Soft Contact Lenses by Incorporating Silica Sol

This study presents a novel approach to increase the oxygen permeability of hydrogel by the addition of silica sol. Herein, 2-hydroxyethyl methacrylate (HEMA) was copolymerized with N-vinyl-2-pyrrolidone (NVP) after mixing with silica sol. The resultant hydrogel was subject to characterizations including Fourier-transform infrared (FTIR), equilibrium water content (EWC), contact angle, optical transmittance, oxygen permeability (Dk), tensile test, anti-deposition of proteins, and cytotoxicity. The results showed that with the increase of silica content, the Dk values and Young’s moduli increased, the optical transmittance decreased slightly, whereas the EWC and contact angle, and protein deposition were not much affected. Moreover, the cytotoxicity of the resultant poly(HEMA-co-NVP)-SNPs indicated that the presence of silica sol was non-toxic and caused no effect to the growth of L929 cells. Thus, this approach increased the Dk of soft contact lenses without affecting their hydrophilicity.

The Ophthalmic Performance of Hydrogel Contact Lenses Loaded with Silicone Nanoparticles

In this study, silicone nanoparticles (SiNPs) were prepared from polydimethylsiloxane (PDMS) and tetraethyl orthosilicate (TEOS) via the sol-gel process. The resultant SiNPs were characterized by dynamic light scattering (DLS), transmission electron microscope (TEM), and scanning electron microscope (SEM). These SiNPs were then blended with 2-hydroxyethylmethacrylate (HEMA) and 1-vinyl-2-pyrrolidinone (NVP) before polymerizing into hydrogel contact lenses. All hydrogels were subject to characterization, including equilibrium water content (EWC), contact angle, and oxygen permeability (Dk). The average diameter of SiNPs was 330 nm. The results indicated that, with the increase of SiNPs content, the oxygen permeability increased, while the EWC was affected insignificantly. The maximum oxygen permeability attained was 71 barrer for HEMA-NVP lens containing 1.2 wt% of SiNPs with an EWC of 73%. These results demonstrate that by loading a small amount of SiNPs, the Dk of conventional hydrogel lenses can be improved greatly. This approach would be a new method to produce oxygen-permeable contact lenses.

Synthesis and Characterization of Silicone Contact Lenses Based on TRIS-DMA-NVP-HEMA Hydrogels

In this study, silicone-based hydrogel contact lenses were prepared by the polymerization of 3-(methacryloyloxy)propyltris(trimethylsiloxy)silane (TRIS), N,N-dimethylacrylamide (DMA), 1-vinyl-2-pyrrolidinone (NVP), and 2-hydroxyethylmethacrylate (HEMA). The properties of silicone hydrogel lenses were analyzed based on the methods such as equilibrium water content, oxygen permeability, optical transparency, contact angle, mechanical test, protein adsorption, and cell toxicity. The results showed that the TRIS content in all formulations increased the oxygen permeability and decreased the equilibrium water content, while both DMA and NVP contributed the hydrophilicity of the hydrogels. The maximum value of oxygen permeability was 74.9 barrers, corresponding to an equilibrium water content of 44.5% as well as a contact angle of 82°. Moreover, L929 fibroblasts grew on all these hydrogels, suggesting non-cytotoxicity. In general, the silicone hydrogels in this work exhibited good oxygen permeability, stiffness, and optical transparency as well as anti-protein adsorption. Hence, these silicone hydrogel polymers would be feasible for making contact lens.