Thermal, structural, and optical properties of γ-irradiated poly(vinyl alcohol)/poly(ethylene glycol) thin film

MODIFICATION INDUCED BY PROTON IRRADIATION IN BAYFOL UV1 7-2 NUCLEAR TRACK DETECTOR

Bayfol is a class of polymeric solid state nuclear track detector which has many applications in various radiation detection fields. It is a Makrofol polycarbonate/polyester blend. Samples from Bayfol film have been irradiated with different fluences (1011-1014 p/cm2) of 1 MeV protons at the University of Surrey Ion Beam Center, UK. The resultant effect of proton irradiation on the structural and optical properties of the Bayfol samples has been investigated using X-ray diffraction, Fourier Transform Infrared and UV spectroscopy. The optical energy gap was decreased from 4.24 to 4.03 eV with increasing the proton fluence from 1011 to 1013 p/cm2, and was accompanied by an increase in the Urbach energy from 0.79 to 1.29 eV. This could be correlated to the results obtained from XRD and FTIR spectroscopy. Further, the non-irradiated Bayfol is nearly colorless. It showed significant sensitivity to color by proton irradiation, associated with an increase in the red and yellow color components. The variation of optical and color parameters with the proton fluence indicate that the dynamic range of Bayfol UV1 7-2 is in the fluence range from 1011 to 1013 p/cm2.

Preparation of Miscible PVA/PEG Blends and Effect of Graphene Concentration on Thermal, Crystallization, Morphological, and Mechanical Properties of PVA/PEG (10 wt%) Blend

Water-soluble polymers such as poly(vinyl alcohol) (PVA) and poly(ethylene glycol) (PEG) and their nanocomposites with graphene were prepared by using a solution mixing and casting technique. The effect of different PEG loadings was investigated to determine the optimum blend ratio. The films were characterized using Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), and thermogravimetric analyzer (TGA) methods. Also, the mechanical properties including tensile strength and elongation at break were measured using a universal tensile testing machine. FTIR results confirmed the formation of the H-bond between PEG and PVA. DSC studies revealed that PEG has a significant plasticization effect on PVA as seen by the drop in the glass transition temperature (Tg). The blend with 10 wt% PEG loading was found to be the optimum blend because of good compatibility as shown by FTIR and SEM results and improved thermal properties. PVA/PEG (10%) nanocomposites were prepared using graphene as a nanofiller. It was found that the elongation at break increased by 62% from 147% for the PVA/PEG (10%) blend to 209% for the nanocomposite with graphene loading of 0.2 wt%. The experimental values of tensile strength were compared using the predictive model of Nicolais and Narkis.