Electron beam irradiation influencing the mechanical properties and water absorption of polycaprolactam (PA6) and polyhexamethylene adipamide (PA66)

It is known that polycaprolactam (PA6) and polyhexamethylene adipamide (PA66) are widely used industrial materials including in the irradiation industry. However, there is a lack of observation of irradiation effects on PA6 and PA66. In the current study, we firstly investigated mechanical and water absorption properties of PA6 and PA6 that were treated under irradiation doses of 200 kGy, 400 kGy, 800 kGy and 1600 kGy, respectively. The structure, mechanical properties and thermal properties of nylon after irradiation were characterized by mechanical property tests, Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The results indicated that the tensile strength of PA6 increased gradually while that of PA66 firstly increased and then decreased with the increase of irradiation dose. Additionally, the elongation at break of the two samples decreased obviously with the increase of irradiation dose. The water absorption of PA6 increased with the increase of irradiation dose; however, that of PA66 was almost constant regardless of irradiation. FTIR tests revealed that the carbonyl index of PA6 and PA66 increased with the increase of irradiation dose. SEM results illustrated that surface degradation of PA6 and PA66 occurred during the irradiation process.

Influence of compatibilizer on the properties of low-density polyethylene/polyamide 6 blends obtained by mechanical recycling of multilayer film waste

Polymeric wastes have caused increasing environmental problems, mainly in oceans that accumulate large amounts of non-degradable plastic waste. Particularly, waste of polymeric multilayer films for packaging presents low interest for mechanical recycling due to the poor properties and low commercial value of the recycled material generated as polymeric blends. Multilayer films of low-density polyethylene (LDPE) and polyamide 6 (PA6) is a typical material used for packaging applications. The aim of this study was to evaluate the action of the concentration of maleic anhydride grafted polyethylene (PE- g-MA) on the compatibilization of LDPE/PA6 blends generated from mechanical recycling of multilayer films containing both polymers. The action of the PE- g-MA on the properties of the LDPE/PA6 blends was evaluated by tensile tests, optical microscopy, melt flow rate, and scanning electron microscopy. The use of PE- g-MA at 2.5 wt% as a compatibilizer during reactive extrusion of the multilayer films waste has showed the best result for production of the respective recycled LDPE/PA6 blends.

Graphite nanoplatelets-modified PLA/PCL: Effect of blend ratio and nanofiller localization on structure and properties

Structure and properties of poly(lactic acid) (PLA)/poly (ɛ-caprolactone) (PCL) influenced by graphite nanoplatelets (GNP) were studied in dependence on blend composition. Electron microscopy indicates predominant localization of GNP in PCL. GNP-induced changes in viscosity hinder refinement of PCL inclusions, support PCL continuity in the co-continuous system, and lead to reduction of PLA inclusions size without GNP being present at the interface in the PCL-matrix blend. Negligible differences in crystallinity of both phases indicate that mechanical behaviour is mainly influenced by reinforcement and GNP-induced changes in morphology. Addition of 5 parts of GNP leads to ~40% and ~25% increase of stiffness in the PCL- and PLA-matrix systems, respectively, whereas the reinforcing effect is practically eliminated in the co-continuous systems due to GNP-induced lower continuity of PLA which enhances toughness. Impact resistance of the 80/20 blend shows increase with 5 parts content due to synergistic effect of PCL/GNP stacks, whereas minor increase in the blend of the ductile PCL matrix with brittle PLA inclusions is caused by GNP-modification of the component parameters. Results indicate high potential of GNP in preparing biocompatible systems with wide range of structure and properties.