Effect of multiple extrusions on the impact properties of polypropylene/clay nanocomposites

Comparison of Properties with Relevance for the Automotive Sector in Mechanically Recycled and Virgin Polypropylene

Polypropylene (PP) has a high recycling potential. However, the properties of mechanically recycled PP (R-PP) have not been fully compared to those of virgin PP (V-PP). Therefore, in this study, properties of R-PP and V-PP were compared using data from recyclers, virgin plastic suppliers, and the literature. The properties of recyclates could not be directly correlated either with the properties of the virgin polymers from which the recyclates were made or the recycling parameters. It was found that the MFR of R-PP was higher; MFR R-PP had a median value (m) of 11 g/10 min while MFR V-PP had a median value of 6.3 g/10 min (at 230 °C and with 2.16 kg). In terms of mechanical properties, in many cases R-PP exhibited stiffer and more brittle behavior, with a slightly higher Young’s modulus (ER-PP = 1400 and EV-PP = 1200 MPa), a reduced elongation at break (ɛbR-PP = 4 l.-% and ɛbV-PP = 83 l.-%), and notched charpy impact strength (NCISR-PP = 4.8 and NCISV-PP = 7.5 kJ/m2). However, the values for every property had a broad distribution. In addition to existing information from the literature, our research sheds fresh light on the variation of the characteristics of recycled polypropylenes presently on the market.

Influence of Processing Conditions on the Preparation of Clay-Based Nanocomposites by Twin-Screw Extrusion

This review paper is devoted to the preparation of clay-based thermoplastic nanocomposites by melt blending in a twin-screw extruder. The influence of the main processing parameters (screw speed, feed rate, barrel temperature, screw profile) on the state of the clay dispersion at the micro- and nanoscale is characterized. The change of dispersion state along the screws and the corresponding mechanisms are presented. The interest of process modelling to predict the state of dispersion is evaluated and, finally, the main modifications of the twin-screw extrusion process to improve the clay dispersion are reviewed.

Mechanical Recyclability of Polypropylene Composites Produced by Material Extrusion-Based Additive Manufacturing

Due to a lack of long-term experience with burgeoning material extrusion-based additive manufacturing technology, also known as fused filament fabrication (FFF), considerable amounts of expensive material will continue to be wasted until a defect-free 3D-printed component can be finalized. In order to lead this advanced manufacturing technique toward cleaner production and to save costs, this study addresses the ability to remanufacture a wide range of commercially available filaments. Most of them either tend to degrade by chain scission or crosslinking. Only polypropylene (PP)-based filaments appear to be particularly thermally stable and therefore suitable for multiple remanufacturing sequences. As the extrusion step exerts the largest influence on the material in terms of temperature and shear load, this study focused on the morphological, rheological, thermal, processing, tensile, and impact properties of a promising PP composite in the course of multiple consecutive extrusions as well as the impact of additional heat stabilizers. Even after 15 consecutive filament extrusions, the stabilized additively manufactured PP composite revealed an unaltered morphology and therefore the same tensile and impact strength as the initial material. As the viscosity of the material of the 15th extrusion was nearly identical to that of the 1st extrusion sequence, the processability both in terms of extrusion and FFF was outstanding, despite the tremendous amount of shear and thermal stress that was undergone. The present work provides key insights into one possible step toward more sustainable production through FFF.