Structure and property of tetrafluoroethylene-propylene elastomer-OVPOSS composites

Preparation and Properties of High Hardness Ultraviolet Curable Polyethylene Terephthalates Surface Coatings Modified with Octavinyl-Polyhedral Oligomeric Silsesquioxane

Using organic coatings helps to protect PET (polyethylene terephthalates) surfaces, improve surface hardness, scratch resistance, and solvent resistance, prolong the service life of PET film, and to expand their scope of applications. There were some disadvantages, including poor flexibility and impact resistance in high-hardness coatings; organic coatings should also be modified to improve the toughness. Herein, a UV (ultraviolet curing) curable high-hardness organic coating used in PET surface protection was prepared and modified with inorganic nanoparticles, such as OVPOSS (octavinyl-polyhedral oligomeric silsesquioxane). The effects of the categories of nanoparticles on the coating performance were studied. UV-Vis spectra (ultraviolet visible light spectra), FT-IR (Fourier transform infrared spectrometer), TGA (thermogravimetric analysis), DMA (dynamic-mechanical), SEM (field emission scanning electron microscope), and AFM (atomic force microscope) were used to characterize the properties of the coatings. The results showed that the addition of eight-vinyl POSS to the organic coating significantly increased its glass transition temperature (Tg) from 100 to 120 °C, improved its storage modulus from 167.6 MPa to 258.9 MPa, and raised its impact resistance and flexibility. The SEM and AFM images displayed that the eight-vinyl POSS particles were dispersed homogeneously in the coating, arranged in an ordered network, and had good compatibility with organic components. The film displayed excellent properties, including 4 H of the pencil hardness, 100 g cm of impact resistance, excellent flexibility, and 90% of light transmittance, with the addition of 0.3 wt % OVPOSS. TGA analysis revealed that the coating had good thermal stability, with 5% weight loss temperature up to 335 °C.

Understanding Trap Effects on Electrical Treeing Phenomena in EPDM/POSS Composites

POSS (polyhedral oligomeric silsesquioxane) provides an interesting alternative nano-silica and has the potential of superior dielectric properties to restrain electrical degradation. By incorporating POSS into EPDM to suppress electrical tree, one of precursors to dielectric failure, is promising to improve the lifetime of insulation materials. This paper focuses on the electrical treeing phenomena in EPDM/OVPOSS (ethylene propylene diene monomer/octavinyl-POSS) composites based on their physicochemical properties and trap distributions. ATR-IR and SEM characteristics are investigated to observe the chemical structure and physical dispersion of EPDM/OVPOSS composites. Electrical treeing characteristics are studied by the needle-plane electrode, and the trap level distributions are characterized by surface potential decay (SPD) tests. The results show that the 3 wt% EPDM/OVPOSS is more effective to restrain the electrical tree growth than the neat EPDM in this paper. It is indicated that the EPDM/OVPOSS with a filler content of 3 wt% introduces the largest energy level and trap density of deep trapped charges, which suppress the transportation of charge carriers injected from the needle tip and further prevent the degradation of polymer molecules. The polarity effects are obvious during the electrical treeing process, which is dependent on the trap level differences between positive and negative voltage.

Crosslinking of low density polyethylene with octavinyl polyhedral oligomeric silsesquioxane as the crosslinker

We report a new strategy for the crosslinking of LDPE using octavinyl polyhedral oligomeric silsesquioxane as the crosslinker, which dramatically decreases the amount of dicumyl peroxide and thus avoids the chain scission, scorch, and production of small pores in the conventional peroxide crosslinking strategy.