Flame retardancy and crack resistance of transparent intumescent fire-resistive coatings

Crack-Resistant Amino Resin Flame-Retardant Coatings Using Waterborne Polyurethane as a Co-Binder Resin

Surface cracking is a major issue in amino resin-based flame-retardant coatings, which can be reduced by mixing flexible resins into the coatings. In this study, flexible waterborne polyurethane (WPU) was added into a melamine-modified, urea-formaldehyde, resin-based intumescent flame retardant (MUF-IFR) coating. A molecular chain of WPU was inserted into the MUF network and formed a WPU/MUF-semi-IPN structure. The cracking resistance of the coating was gradually enhanced with the increase in WPU content. When the WPU content exceeded 25% of the total resin, there were no cracks in the coatings after crack-resistance tests. The coatings before and after toughening showed good transparency on wood surfaces. The influence of WPU on char formation and flame retardant properties were explored by TGA, SEM, and cone calorimetry. The results showed that the decomposition of WPU occurred before char formation, which decreased the integrity of the coating and damaged the compactness of the char. Therefore, the addition of WPU reduced the expansion height and the barrier capacity of the char as well as the flame retardant properties of the coating. When the amount of WPU was 25% of the total resin, compared to the non-WPU coating, the average heat release rate in 300 s (AveHRR_300s) and the total heat release at 300 s (THR_300s) of the samples were increased by 45.8% and 35.7%, respectively. However, compared to the naked wood, the peak heat release rate (pHRR₁), AveHRR_300s, and THR_300s of the samples with the coating containing 25% WPU were decreased by 64.2%, 39.0%, and 39.7%, respectively. Therefore, the thermal stability of WPU affected char formation. The amount of WPU added should be chosen to be the amount that was added just before the coating cracked.

Comparative Study of Fire Resistance and Char Formation of Intumescent Fire-Retardant Coatings Reinforced with Three Types of Shell Bio-Fillers

Three types of shell bio-fillers, including eggshell (CES), conch shell (CHS) and clamshell (CMS), were prepared by cleaning, ultrasonication and pulverizing processes of biowastes, and then applied to intumescent fire-retardant coatings. The effects of shell bio-fillers with different polymorphs on the fire resistance and char-forming of intumescent fire-retardant coatings were investigated by cone calorimeter test, fire protection tests, smoke density test, thermogravimetric analysis (TG), and the fire resistance and char-forming mechanism of bio-fillers in intumescent fire-retardant coatings were proposed. The results show that three kinds of bio-fillers exert an excellent synergistic effect on enhancing the fire resistance and char-forming properties of the intumescent fire-retardant coatings, while clamshell has the best synergistic efficiency among the bio-fillers. Especially, IFRC-CMS coating containing 3 wt% clamshell shows the best fire protection performance and lowest smoke production and heat release, which offers an equilibrium backside temperature of 134.6 °C at 900 s, a flame-spread rating of 14.4, and a smoke density rating value of 22.8%. The synergistic efficiency of bio-fillers in the intumescent coatings depends on the polymorphs of CaCO₃ in bio-fillers, and aragonite CaCO₃ shows a higher synergistic efficiency compared to calcite CaCO₃ and the mixture of aragonite and calcite CaCO₃. The CMS composed of aragonite shows the best synergistic effect, CHS composed of aragonite and calcite comes second, and CES composed of calcite has the weakest synergistic effect.

Fire Resistance, Thermal and Anti-Ageing Properties of Transparent Fire-Retardant Coatings Modified with Different Molecular Weights of Polyethylene Glycol Borate

Four kinds of polyethylene glycol borate (PEG-BA) with different molecular weights were grafted into cyclic phosphate ester (PEA) to obtain flexible phosphate esters (PPBs), and then applied in amino resin to obtain a series of transparent intumescent fire-retardant coatings. The comprehensive properties of the transparent coatings containing different molecular weights of PEG-BA were investigated by various analytical instruments. The transparency and mechanical analyses indicate that the presence of PEG-BA slightly decreases the optical transparency of the coatings but improves the flexibility and adhesion classification of the coatings. The results from fire protection and cone calorimeter tests show that low molecular weight of PEG-BA exerts a positive flame-retarded effect in the coatings, while high molecular weight of PEG800-BA behaves against flame-retarded effect. Thermogravimetric and char residue analyses show that the incorporation of low molecular weight of PEG-BA clearly increases the thermal stability and residual weight of the coatings and generates a more compact and stable intumescent char on the surface of the coatings, thus resulting in superior synergistic flame-retarded effect. In particular, MPPB1 coating containing PEG200-BA exerts the best flame-retarded effect and highest residual weight of 36.3% at 700 °C, which has 57.6% reduction in flame spread rate and 23.9% reduction in total heat release compared to those of MPPB0 without PEG-BA. Accelerated ageing test shows that low molecular weight of PEG-BA promotes to enhance the durability of structural stability and fire resistance of the coatings, while PEG800-BA with high molecular weight weakens the ageing resistance. In summary, the fire-resistant and anti-ageing efficiencies of PEG-BA in the coatings depend on its molecular weight, which present the order of PEG200-BA > PEG400-BA > PEG600-BA > PEG800-BA.

Comparative Study of Fire Resistance and Anti-Ageing Properties of Intumescent Fire-Retardant Coatings Reinforced with Conch Shell Bio-Filler

Conch shell bio-filler (CSBF) was prepared by washing, ultrasonicating, and pulverizing of conch shells and then was applied in waterborne intumescent fire-retardant coatings. The influence of CSBF on fire resistance and anti-ageing properties of intumescent fire-retardant coatings were studied by using different analytical methods. The fire protection and smoke density tests showed that when the mass fraction of CSBF was 3%, the resulting FRC3 coating had the optimum synergistic flame-retardant and smoke-suppression effects concomitant with a flame-spread rating of 10.7, equilibrium backside temperature of 152.4 °C at 900 s, and smoke-density rating value of 10.4%, which were attributed to the establishment of a more dense and stable intumescent char layer against heat and mass transfer. Thermogravimetric analysis indicated that the presence of CSBF increased the thermal stability and char-forming performance of the coatings, and the char residue of FRC3 rose to 34.6% at 800 °C from 28.6% of FRC0 without CSBF. The accelerated ageing test suggested that the incorporation of CSBF reduced the migration and decomposition of the flame retardants and the yellowing, blistering, and powdering phenomenon, thus improving the structural stability of the coating, resulting in better durability of flame retardancy and smoke-suppression performance.