Sulfobetaine polymers for effective permeability into multicellular tumor spheroids (MCTSs)

Multicellular tumor spheroids (MCTSs) are attractive for drug screening before animal tests because they emulate an in vivo microenvironment. The permeability of the MCTSs and tumor tissues towards the candidate drugs is not sufficient even though the drugs can penetrate monolayer cultured cells; therefore, nanocarriers are required to enhance permeability and deliver drugs. In this study, we prepared zwitterionic polymers of sulfobetaine methacrylates and (meth)acrylamides with or without hydroxy groups between the zwitterions to serve as highly permeable nanocarriers. In the sulfobetaine polymers, poly(2-hydroxy-3-((3-methacrylamidopropyl)dimethylammonio)propane-1-sulfonate), P(OH-MAAmSB), the hydroxy group containing methacrylamide polymer exhibited little cytotoxicity and membrane translocation ability against monolayer cultured cells. Moreover, the excellent permeability of the hepatocyte MCTS enabled P(OH-MAAmSB) to permeate it and reach the center region (∼325 μm in diameter) at approximately 150 s, although poly(trimethyl-2-methacroyloxyethylammonium), a cationic polymer, penetrated just 1 to 2 layers from the periphery. The superior permeability of P(OH-MAAmSB) might be due to its good solubility and side chain conformation. P(OH-MAAmSB) is a promising nanocarrier with membrane translocation and permeability.

Unique Oil-in-Brine Pickering Emulsion Using Responsive Antipolyelectrolyte Functionalized Latex: A Versatile Emulsion Stabilizer

A simple and straightforward approach to synthesize oil-in-water (O/W) emulsions under high salinity and temperature using zwitterion-functionalized latexes are presented in this work. First, well-defined functionalized latexes were synthesized by emulsifier-free emulsion copolymerization in the presence of precursor sulfobetaine comonomer using brine as a continuous phase. The surface-functionalized latex particles were then characterized by DLS, SEM, TEM, XPS, and TGA. The functionalized latex exhibited antipolyelectrolyte behavior in high salinity brine and at high temperatures. The effects of salinity, temperature, and pH on the long-term stability of the particles were investigated. Further, to evaluate the potential in high salinity brine and high temperature, the saltphilic functionalized latexes were utilized to stabilize the oil/brine (O/W) interface without any other additives. The latex enabled the formation of a stable Pickering emulsion system with low solid content (<0.02% w/w) in the presence of 50% v/v n-decane. The functionalized latexes were self-assembled at the O/W interface as a spherical colloidosome in high salinity brine through hydrophobic interactions and irreversible adsorption. The supraparticles were imaged with SEM, providing an insight that the exterior of the emulsion droplets is stabilized by the saltphilic latex particles, forming a protective layer at the oil-water interface through electrostatic repulsion. The antipolyelectrolyte latex can be utilized as a novel emulsion stabilizer, which can provide a versatile alternative for applications in a complex environment such as high salinity, temperature, and low or high pH.

Polymaleimide-Based Polysulfobetaines Bearing Functional and Nonfunctional Hydrophobic Units and Its Aggregation Behavior in Aqueous Media

Copolymaleimide-based zwitterionic polysulfobetaines (PM-SBs) were prepared by a "top down" method for the first time. Interfacial studies of these polymers showed many interesting characteristics. These PM-SBs did not require any salt in the form of sodium chloride (NaCl) to dissolve in water and exhibited exceptional salt tolerance. PM-SBs showed very mild thermogelling behavior. The viscosity of 5 wt % aqueous solution of polymers increased with increasing concentration of salt without showing any limits within the salt concentrations studied [200g/L of NaCl (3.4 M)] in contrast to other reported zwitterionic polysulfobetaines. Dynamic light scattering (DLS) studies also indicated a structure-dependent particle size with varying concentrations of NaCl solution. The uniformity of particles of 5 wt % aqueous solution of PM-SBs increased with increasing concentration of NaCl. At 0.1 wt % concentration, even in the absence of NaCl, mild aggregation was noticed. The concentration of aggregated particles increased with the increasing concentration of NaCl. Because of the exceptionally high salt tolerance, these polymers are potentially suitable for applications in antifouling, oil field, personal care formulations, and water purification.

Preparation of Cross-Linkable Zwitterionic Polybenzoxazine with Sulfobetaine Groups and Corresponding Zwitterionic Thermosetting Resin for Antifouling Surface Coating

This work demonstrates a cross-linkable zwitterionic polymer, the corresponding zwitterionic thermosetting resin, and their application for antifouling surface coating. The tertiary amine-containing benzoxazine group is utilized as a precursor to react with 1,3-propane sultone to introduce sulfobetaine moiety to benzoxazine group. The reaction route provides an effective approach for preparation of sulfobetaine-functionalized benzoxazines and the corresponding sulfobetaine-functionalized thermosetting resins of benzoxazines. The sulfobetaine-functionalized polybenzoxazine has been utilized as a coating material for ceramic porous membranes to impart protein-repelling characteristic to the membrane surface. In a filtration test on a Bovine serum albumin (BSA) aqueous solution, the sulfobetaine resin modified membrane shows a 96.2% of rejection rate and a 1680 ± 9 Lm^2-h^-1 of permeation flux at the first cycle test. In cycled measurements with membrane washing, the membrane shows a total flux decline ratio (R_t) and a reversible flux decline ratio (R_r) of about 46.9% and 43.1%, respectively. A high ratio of reversible fouling (R_r/R_t) of 91.9% is found, which supports the statement that the sulfobetaine-functionalized polybenzoxazine is an effective material to impart antifouling characteristic to porous materials for bioseparation and filtration.

Molecular Design of Zwitterionic Polymer Interfaces: Searching for the Difference

The widespread occurrence of zwitterionic compounds in nature has incited their frequent use in designing biomimetic materials. Therefore, zwitterionic polymers are a thriving field. A particular interest for this particular polymer class has currently focused on their use in establishing neutral, low-fouling surfaces. After highlighting strategies to prepare model zwitterionic surfaces as well as those that are more suitable for practical purposes relying strongly on radical polymerization methods, we present recent efforts to diversify the structure of the hitherto quite limited variety of zwitterionic monomers and of the derived polymers. We identify key structural variables, consider their influence on essential properties such as overall hydrophilicity and long-term stability, and discuss promising targets for the synthesis of new variants.

Reversible Photo- and Thermoresponsive, Self-Assembling Azobenzene Containing Zwitterionic Polymers

Commercially available azo dyes bearing amino groups were grafted to zwitterionic copolymers composed of cyclic anhydride functionality. The zwitterionic copolymers were prepared for the first time by polymerizing sulfobetaine (SB) monomer with maleic anhydride (MA) under conventional free radical polymerization as well as reversible addition-fragmentation chain transfer (RAFT) polymerization. Poly(SB- co-MA) self-assembled in deionized water. Azobenzene grafted zwitterionic poly((SB- co-MA)- g-Azo) exhibited multiresponsive behavior. As confirmed by UV-vis spectroscopy, trans → cis isomerization of the azo group was responsible for the photo- and thermal responsive behavior. The photoisomerization was reversible, and no photoaging was detected during the repeated exposure to UV and visible light. The water-soluble nature of photoresponsive azo dye grafted copolymers makes it suitable for applications in biological systems.

Highly monodisperse zwitterion functionalized non-spherical polymer particles with tunable iridescence

A facile and simple synthetic route towards functionalized non-spherical polymer particles (NSP) with tunable morphologies and iridescence is presented. Monodisperse particles with unique zwitterionic functionality were synthesized via emulsifier-free emulsion polymerization in a single step process. The sulfobetaine comonomer was utilized to induce phase separation in the course of polymerization to achieve anisotropic NSP with controlled morphologies such as quasi-spherical with protruding structures like bulge, eye-ball, and snowman-like nanostructures. Both SEM and TEM analyses revealed anisotropic particles, and phase-separated protrusion morphology with a small increase in aspect ratio. By taking advantage of the monodisperse, colloidally stable NSPs, template free photonic crystal arrays were fabricated through a bottom-up approach. The particles readily self-assemble and exhibit a photonic bandgap with vivid structural colors that arise from ordered structures of different morphologies. Additionally, the salt-responsive photonic crystals also possess tunable color-changing characteristics.

A convenient method to fabricate functional photonic crystal arrays using self-assembled non-spherical particles that form tunable iridescent polymer opal by changing size and morphologies, thereby producing new responsive photonic material.