Park JH, Hwang SH. A Polyolefin Elastomer Encapsulant Modified by an Ethylene-Propylene-Diene Terpolymer for Photovoltaic Applications.
ACS OMEGA 2024;
9:3858-3865. [PMID:
38284050 PMCID:
PMC10809238 DOI:
10.1021/acsomega.3c07969]
[Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Grants] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 10/11/2023] [Revised: 12/20/2023] [Accepted: 12/26/2023] [Indexed: 01/30/2024]
Abstract
In this study, a newly designed adhesion promoter, a modified ethylene-propylene-diene terpolymer (m-EPDM), was constructed via a simple thiol-ene click reaction between the ethylene-propylene-diene terpolymer (EPDM) and 3-mercaptopropyltrimethoxysilane (MPTS) to employ polyolefin elastomer (POE) encapsulants in photovoltaic modules. The grafting reaction of MPTS on an EPDM backbone (thiol-ene click reaction) was verified using 1H NMR, 29Si NMR, and SEM/EDX. The thermal and mechanical characteristics of the POE compounds did not significantly change with an increasing m-EPDM content irrespective of the cross-linking state. Interestingly, the adhesion strength to the glass substrate increased linearly with an increasing m-EPDM content until 9 phr. Also, the POE compounds containing more than 12 phr m-EPDM showed cohesion failure of the encapsulant layer, remaining as a residue of the encapsulant layer on the glass surface after peel testing. The damp-heat test was conducted to evaluate the long-term durability of the photovoltaic module encapsulated with m-EPDM, and no significant power loss was found even after 1000 h under the test conditions.
Collapse