Synthesis, characterization, and cytotoxicity of PCL–PEG–PCL diacrylate and agarose interpenetrating network hydrogels for cartilage tissue engineering

A light-responsive wound dressing hydrogel: Gelatin based self-healing interpenetrated network with metal-ligand interaction by ferric citrate

Interpenetrated network (IPN) hydrogels with desired mechanical properties were prepared based on gelatin. A copolymer of dimethyl aminoethyl methacrylate (DMAEMA) with 2-Acrylamido-2-methylpropane sulfonic acid (AMPS) in gelatin was chemically cross-linked with methylene bis acrylamide (MBA) to form a semi-IPN hydrogel. Also, IPN hydrogel is fabricated from the AMPS-co-DMAEMA and gelatin in the presence of ferric ions with both chemical and physical cross-linkers. According to the compression test, the metal-ligand interaction has a remarkable impact on the mechanical strength of hydrogel. Ferric ions caused a decrease in the pores size confirmed by the SEM images of hydrogels, resulting in preserving its mechanical stability during the swelling test due to a more robust structure of hydrogel. Ferric to ferrous ions reduction is observed under visible light irradiation, which results in a light-sensitive hydrogel with a higher rate of biodegradation compared to semi-IPN hydrogels. MTT assay results implied that the synthesized hydrogels are non-toxic for the L-929 cell line. Also, for more detailed investigations, histological studies are conducted as in vivo tests. With regards to the improvements of mechanical properties harnessed in IPN hydrogels by ferric ions along with the extraordinary self-healing capability, IPNs would be considered an appropriate option for tissue engineering.

Novel Trends in Hydrogel Development for Biomedical Applications: A Review

Nowadays, there are still numerous challenges for well-known biomedical applications, such as tissue engineering (TE), wound healing and controlled drug delivery, which must be faced and solved. Hydrogels have been proposed as excellent candidates for these applications, as they have promising properties for the mentioned applications, including biocompatibility, biodegradability, great absorption capacity and tunable mechanical properties. However, depending on the material or the manufacturing method, the resulting hydrogel may not be up to the specific task for which it is designed, thus there are different approaches proposed to enhance hydrogel performance for the requirements of the application in question. The main purpose of this review article was to summarize the most recent trends of hydrogel technology, going through the most used polymeric materials and the most popular hydrogel synthesis methods in recent years, including different strategies of enhancing hydrogels’ properties, such as cross-linking and the manufacture of composite hydrogels. In addition, the secondary objective of this review was to briefly discuss other novel applications of hydrogels that have been proposed in the past few years which have drawn a lot of attention.

Chemical Immobilization of Carboxymethyl Chitosan on Polycaprolactone Nanofibers as Osteochondral Scaffolds

Carboxymethyl chitosan (CMC) as a bio-based osteochondral inductive material was chemically immobilized on the surface of polycaprolactone (PCL) nanofibers to fabricate scaffolds for osteochondral tissue engineering applications. The chemical immobilization process included the aminolysis of ester bonds and bonding of the primary amines with glutaraldehyde as a coupling agent. The SEM and FTIR results confirmed the successfulness of the CMC immobilization. The fabricated scaffolds presented cell viabilities of > 82% and supported the attachment and proliferation of the human bone marrow mesenchymal stem cells (hBM-MSCs). The CMC-immobilized scaffolds concentration dependently induced the diverse osteochondral differentiation pathways for the hBM-MSCs without using any external differential agents. According to the Alcian Blue and Alizarin Red staining and immunocytochemistry results, scaffolds with a higher content of CMC presented more chondro-inductivity and less osteoinductivity. Thus, the CMC-immobilized scaffolds can be employed as great potential candidates for osteochondral tissue engineering applications.