Effect of expandable graphite and ammonium polyphosphate on the thermal degradation and weathering of intumescent fire‐retardant coating

Enhanced Flame Retardancy of Styrene-Acrylic Emulsion Based Damping Composites Based on an APP/EG Flame-Retardant System

Developing flame-retarded styrene-acrylic emulsion (SAE) based damping composites is a challenging task because of their very high flammability. A promising approach is the synergistic combination of expandable graphite (EG) and ammonium polyphosphate (APP). In this study, the surface modification of APP was modified by commercial titanate coupling agent ndz-201 through ball milling, and the SAE-based composite material was prepared with SAE and different ratios of modified ammonium polyphosphate (MAPP) and EG. The surface of MAPP was successfully chemically modified by NDZ-201 through scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction analysis (XRD), Energy Dispersion Spectroscopy (EDS), and contact angle. The effects of different ratios of MAPP and EG on the dynamic and static mechanical properties and flame retardancy of composite materials were explored. The results showed that when MAPP:EG = 1:4, the limiting oxygen index (LOI) of the composite material was 52.5%, and the vertical burning test (UL-94) was at the V0 level. Its LOI increased by 141.9% compared to the composite materials without flame retardant. The optimized formulation of MAPP and EG in SAE-based damping composite materials showed a significant synergistic effect on the flame retardancy of the composite material.

Bio-based arginine surface-modified ammonium polyphosphate: an efficient intumescent flame retardant for epoxy resin

In this work, ammonium polyphosphate (APP) was surface-modified by bio-based arginine (Arg) for the first time to enhance its flame retardance for fire-safety epoxy resin (EP). The structure of Arg modified APP (Arg-APP) was characterized by Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), ¹H nuclear magnetic resonance (¹H-NMR), and scanning electron microscopy (SEM). The results illustrated that Arg was attached on the surface of APP through a cation exchange reaction. With Arg acting as the efficient carbon source, the char-forming ability of Arg-APP was significantly improved as illustrated by thermogravimetric analysis (TGA). The flame retardance of EP/APP and EP/Arg-APP composites was evaluated using the limit oxygen index (LOI), vertical burning tests (UL-94), and cone calorimeter tests (CCT). The results showed that at the same weight loading (15 wt%), Arg-APP had better flame retardance and smoke suppression performance compared with pristine APP, which can be attributed to Arg-APP constituting an integrated intumescent flame retardant (IFR) and facilitating formation of char residues with significantly expanded structures and higher carbonization degrees. When the weight loading of Arg-APP reached 25 wt%, the EP/Arg-APP composite could achieve an LOI value as high as 34.7%, pass V-0 requirements in UL-94 tests, and decrease the peak heat release rate and total smoke production by 83.5% and 61.1% compared with neat EP in CCT, respectively, indicating the superior flame retardance performance of Arg-APP. Finally, the effects of the flame retardant additives on the mechanical properties of EP were evaluated by the differential scanning calorimetry (DSC) tests and tensile-strain tests. At the same additive weight loading (15 wt%), the EP/Arg-APP composite showed higher glass-transition temperature and better tensile-strain properties compared with EP/APP composite, which can be attributed to the Arg shell structure improving the compatibility between APP and the organic substrate. In conclusion, this work presents a convenient and environmentally friendly method to improve the practical performance of APP.

Arginine modified ammonium polyphosphate was prepared through the cation-exchange reaction and applied as an intumescent flame retardant for epoxy resin.