Chemical oxidation of high‐density polyethylene: Surface energy, functionality, and adhesion to liquid epoxy

Studying the combined influence of microplastics' intrinsic and extrinsic characteristics on their weathering behavior and heavy metal transport in storm runoff

The weathering and contaminant transport behavior of both primary (PMPs) and secondary microplastics (SMPs) are interrelated to their original physiochemical features and variations within the environment. This study examines the influence of PMPs' intrinsic characteristics (polymer structure and crystallinity) and SMPs' extrinsic features (surface oxidation and external sediments attachment) on the photodegradation kinetics, and subsequently Pb(II) and Zn(II) uptake from stormwater. For this purpose, high density polyethylene (HDPE) and low density polyethylene (LDPE) with different degrees of crystallinities were produced as PMPs, and their photodegradation behaviors were compared with original polymers. Furthermore, the SMPs generated by abrasion and surface oxidation of PMPs and the virgin PMPs underwent accelerated photodegradation, and the changes of their crystallinity, surface chemistry, and morphology were examined. Scanning electron microscopy (SEM) imaging and X-ray photoelectron (XPS) studies revealed the formation of cracks and different oxidized functionalities on MPs surface due to UV photodegradation. The vinyl and carbonyl indices calculated using Attenuated Total Reflectance Fourier Transform Infrared (ATR-FTIR) spectroscopy demonstrated an elevated photodegradation rate for SMPs compared to the PMPs. Moreover, the Differential Scanning Colorimetry (DSC) demonstrated an increasing percentage of crystallinity in all MPs due to the photodegradation. The percent crystallinity of HDPE pellets increased after photodegradation from 49.8 to 62.6 and it increased from 17.2 to 38.9 for LDPE pellets respectively. The greater level of increase in crystallinity for LDPE in comparison to HDPE upon photodegradation was referred to as LDPE's greater amorphous content and branched structure. A greater level of metal uptake was obtained for photodegraded LDPE pellets as 2526 μg/m² for Pb(II) and 2028 μg/m² for Zn(II) respectively.

Role of heat treatment in improving replication quality of PDMS double-casting

An efficient and eco-friendly method utilizing the heat treatment of the PDMS master is proposed for improving the replication quality of PDMS double-casting. The effects of heat treatment on interfacial adhesion are investigated in terms of uncured low molecular weight chains, surface energy, and surface roughness. The PDMS master treated at 150 °C for 72 h shows the highest replication quality of micropatterns with a diameter and height of 30 μm.

Improving Surface Functionality, Hydrophilicity, and Interfacial Adhesion Properties of High-Density Polyethylene with Activated Peroxides

Polyolefins have had limited application in advanced technologies due to their low surface energy, hydrophobicity, and weak interfacial adhesion with polar coatings. Herein, we propose the use of transition metals at their lowest oxidation state and inorganic peroxides to improve the functionality, surface free energy, hydrophilicity, and adhesion properties of high-density polyethylene (HDPE). Among the nine combinations of transition metals and peroxides used in this study, the combination of Co(II) and peroxymonosulfate (PMS) peroxide was the most effective for surface modification of HDPE, followed closely by the combination of Ru(III) and PMS. After chemical treatment, HDPE's surface functionality, composition, and energy were analyzed via Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and contact angle measurements. Hydroxyl, carbonyl, and carboxylic acid functional groups were detected on the surface, which explained the improved hydrophilicity of the modified HDPE surface; the contact angle of HDPE with DI water decreased from 94.31 to 51.95° after surface treatment. To investigate the effect of HDPE's surface functionality on its interfacial properties, its adhesion to a commercial epoxy coating was measured via pull-off strength test according to ASTM D54541. After only 20 min of surface treatment with Co(II)/PMS solution, the adhesion strength at the interface of HDPE and the epoxy coating increased by 193%, confirming the importance of polyolefins' surface functionality on their interfacial adhesion properties. The method outlined herein can improve HDPE's surface functionality by introducing sulfate radicals. It improves HDPE's hydrophilicity and adhesion properties without requiring strong acids or time-consuming pre- or post-treatment processes. This process has the potential to increase the use of polyolefins in various industries, such as for protective coatings, high performance lithium-ion battery separators, and acoustic sensors.