Enhanced osteogenic differentiation and mineralization of human dental pulp stem cells using Prunus amygdalus amara (bitter almond) incorporated nanofibrous scaffold

Polyphenol extracts derived from plants are expected to have enhanced osteoblast proliferation and differentiation ability, which has gained much attention in tissue engineering applications. Herein, for the first time, we investigate the effects of Prunus amygdalus amara (bitter almond) (BA) extract loaded on poly (ε-caprolactone) (PCL)/gelatin (Gt) nanofibrous scaffolds on the osteoblast differentiation of human dental pulp stem cells (DPSCs). In this regard, BA (0, 5, 10, and 15% wt)-loaded PCL/Gt nanofibrous scaffolds were prepared by electrospinning with fiber diameters in the range of around 237-276 nm. Morphology, composition, porosity, hydrophilicity, and mechanical properties of the scaffolds were examined by FESEM, ATR-FTIR spectroscopy, BET, contact angle, and tensile tests, respectively. It was found that the addition of BA improved the tensile strength (up to 6.1 times), Young's modulus (up to 3 times), and strain at break (up to 3.2 times) compared to the neat PCL/Gt nanofibers. Evaluations of cell attachment, spreading, and proliferation were done by FESEM observation and MTT assay. Cytocompatibility studies support the biocompatible nature of BA loaded PCL/Gt scaffolds and free BA by demonstrating cell viability of more than 100% in all groups. The results of alkaline phosphatase activity and Alizarin Red assay revealed that osteogenic activity levels of BA loaded PCL/Gt scaffolds and free BA were significantly increased compared to the control group (p < 0.05, p < 0.01, p < 0.001). QRT-PCR results demonstrated that BA loaded PCL/Gt scaffolds and free BA led to a significant increase in osteoblast differentiation of DPSCs through the upregulation of osteogenic related genes compared to the control group (p < 0.05). Based on results, incorporation of BA extract in PCL/Gt scaffolds exhibited synergistic effects on the adhesion, proliferation, and osteogenesis differentiation of hDPSCs and was therefore assumed to be a favorable scaffold for bone tissue engineering applications.

Chain-End Functionalization of Poly(ε-caprolactone) for Chemical Binding with Gelatin: Binary Electrospun Scaffolds with Improved Physico-Mechanical Characteristics and Cell Adhesive Properties

Composite biocompatible scaffolds, obtained using the electrospinning (ES) technique, are highly promising for biomedical application thanks to their high surface area, porosity, adjustable fiber diameter, and permeability. However, the combination of synthetic biodegradable (such as poly(ε-caprolactone) PCL) and natural (such as gelatin Gt) polymers is complicated by the problem of low compatibility of the components. Previously, this problem was solved by PCL grafting and/or Gt cross-linking after ES molding. In the present study, composite fibrous scaffolds consisting of PCL and Gt were fabricated by the electrospinning (ES) method using non-functionalized PCL1 or NHS-functionalized PCL2 and hexafluoroisopropanol as a solvent. To provide covalent binding between PCL2 and Gt macromolecules, NHS-functionalized methyl glutarate was synthesized and studied in model reactions with components of spinning solution. It was found that selective formation of amide bonds, which provide complete covalent bonding of Gt in PCL/Gt composite, requires the presence of weak acid. With the use of the optimized ES method, fibrous mats with different PCL/Gt ratios were prepared. The sample morphology (SEM), hydrolytic resistance (FT-IR), cell adhesion and viability (MTT assay), cell penetration (fluorescent microscopy), and mechanical characteristics of the samples were studied. PCL2-based films with a Gt content of 20 wt% have demonstrated the best set of properties.