Metal–Organic Framework (MOF) Template Based Efficient Pt/ZrO 2 @C Catalysts for Selective Catalytic Reduction of H 2 Below 90 °C

Heterogeneous catalytic oxidation of glycerol over a UiO-66-derived ZrO2@C supported Au catalyst at room temperature

The catalytic conversion of biomass-derived glycerol into high-value-added products, such as glyceric acid (GLYA), using catalyst-supported Au nanoparticles (Au NPs) at room temperature presents a significant challenge. In this study, we constructed a series of supported Au catalysts, including Au/ZrO2@C, Au/C, Au/ZrO2, and Au/ZrO2-C, and investigated their effectiveness in selectively catalytic oxidizing glycerol to GLYA at room temperature. Among these catalysts, the Au/ZrO2@C catalyst exhibited the best catalytic performance, achieving a glycerol conversion rate of 73% and a GLYA selectivity of 79% under the optimized reaction conditions (reaction conditions: 30 mL 0.1 M glycerol, glycerol/Au = 750 mol mol-1, T = 25 °C, p(O2) = 10 bar, stirring speed = 600 rpm, time = 6 h). Physical adsorption, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), and other characterization methods were employed to analyze the texture properties of the catalyst. The findings indicated that the support structure, the strong metal-support interactions between Au NPs and the support, and the presence of small metallic Au NPs were the primary factors contributing to the catalyst's high activity and selectivity. Moreover, the reusability of the Au/ZrO2@C catalyst was investigated, and a probable reaction mechanism for the oxidation of glycerol was proposed.

Recent advances in core-shell structured catalysts for low-temperature NH3-SCR of NOx

Ammonia selective catalytic reduction (NH₃-SCR) of nitrogen oxides is an effective and well-established technology for NO_x removal, but current commercial denitrification catalysts based on V₂O₅-WO₃/TiO₂ have some obvious disadvantages, including narrow operating temperature windows, toxicity, poor hydrothermal stability, and unsatisfied SO₂/H₂O tolerance. To overcome these drawbacks, it is imperative to investigate new types of highly efficient catalysts. In order to design catalysts with outstanding selectivity, activity, and anti-poisoning ability, core-shell structured materials have been widely applied in the NH₃-SCR reaction, which exhibits numerous advantages including the large surface area, the strong synergy interaction of core-shell materials, the confinement effect, and the shielding effect from the shell layer to protect the core. This review summarizes recent developments of core-shell structured catalysts for NH₃-SCR, including basic classification, synthesis methods, and a detailed description of the performance and mechanisms of each type of catalyst. It is hoped that the review will stimulate future developments in NH₃-SCR technology, leading to novel catalyst designs with improved denitrification performance.

Highly efficient Hg2+ removal via a competitive strategy using a Co-based metal organic framework ZIF-67

The stronger coordination ability of mercury ions with organic ligands than the metal ions in metal organic framework (MOFs) provides an accessible way to separate mercury ions from solution using specific MOFs. In this study, a Co-based MOF (ZIF-67, Co(mIM)₂) was synthesized. It did not introduce specific functional groups, such as -SH and -NH₂, into its structure through complicated steps. It separate Hg²⁺ from wastewater with a new strategy, which utilized the stronger coordination ability of Hg²⁺ with the nitrogen atom on the imidazole ring of the organic ligand than the Co²⁺ ions. Hg²⁺ replaced Co²⁺ nodes from ZIF-67 and formed a more stable precipitate with mIM. The experimental results showed that this new strategy was efficient. ZIF-67 exhibited Hg²⁺ adsorption capacity of 1740 mg/g, much higher than the known MOFs sorbents. mIMs is the reaction center and ZIF-67 can improve its utilization. The sample color faded from purple to white due to the loss of cobalt ion. It is a great feature of ZIF-67 that allows users to judge whether the sorbent is deactivated intuitively. ZIF-67 can be sustainable recycled by adding organic ligands to the solution after treatment due to its simple synthesis method at room temperature. It's a high-efficient and sustainable sorbent for Hg²⁺ separation from wastewater.

Progress in Metal-Organic Framework Catalysts for Selective Catalytic Reduction of NOx: A Mini-Review

Nitrogen oxides released from the combustion of fossil fuels are one of the main air pollutants. Selective catalytic reduction technology is the most widely used nitrogen oxide removal technology in the industry. With the development of nanomaterials science, more and more novel nanomaterials are being used as catalysts for the selective reduction of nitrogen oxides. In recent years, metal-organic frameworks (MOFs), with large specific surface areas and abundant acid and metal sites, have been extensively studied in the selective catalytic reduction of nitrogen oxides. This review summarizes recent progress in monometallic MOFs, bimetallic MOFs, and MOF-derived catalysts for the selective catalytic reduction of nitrogen oxides and compares the reaction mechanisms of different catalysts. This article also suggests the advantages and disadvantages of MOF-based catalysts compared with traditional catalysts and points out promising research directions in this field.

Synthesis of metal–organic frameworks (MOFs) and their application in the selective catalytic reduction of NOx with NH3

This review summarizes the synthesis, applications for the NH3-SCR and methods for strengthening the water resistance and thermal stability of MOF catalysts.

Technologies for the nitrogen oxides reduction from flue gas: A review

The required energy of the global industry is mostly generated from fossil fuel sources, such as natural gas, gasoline, diesel, oil, and coal. Nitrogen oxides are one of the main air pollutants that are produced from the combustion of fossil fuels in stationary and mobile sources. Development of new technologies to decrease the NO_x emission from exhaust gases is essential due to the harmful effect of NO_x on the environment and human health. Compared with pre-combustion and combustion methods (with <50% NO_x removal efficiency), the post-combustion methods with higher efficiency (above 80%) have attracted more attention in NO_x elimination. This review describes the currently used technologies of NO_x abatement. Different available post-combustion methods of NO_x removal, including selective catalytic reduction (using different types of reducing reagents, including ammonia, hydrogen, hydrocarbons, and carbon monoxide), selective noncatalytic reduction, wet scrubbing, adsorption, electron beam, nonthermal plasma, and electrochemical reduction of NO_x, are discussed.

Zirconium Oxide Sulfate-Carbon (ZrOSO4@C) Derived from Carbonized UiO-66 for Selective Production of Dimethyl Ether

Methanol dehydration process to dimethyl ether (DME) has been considered as one of the main routes to produce clean fuel, that is, DME. Thus, efficient catalysts are highly required for selective production of DME. Herein, UiO-66 was used as a precursor for the synthesis of zirconium oxide sulfate embedded carbon (ZrOSO₄@C). The synthesis method involves a one-step carbonization of UiO-66 in the presence of sulfuric acid (10 wt %). Material characterizations using X-ray diffraction, X-ray photoelectron spectroscopy, Fourier transform infrared, and Raman spectroscopy approve the formation of the high crystalline phase of ZrOSO₄@C. Nitrogen adsorption-desorption isotherms and high-resolution transmission electron microscopy confirm the mesopore structure of the materials. Acidity analysis using pyridine temperature-programmed desorption and isopropanol dehydration corroborates that ZrOSO₄@C has weak and intermediate acidic sites making ZrOSO₄@C an effective catalyst for methanol dehydration to DME. The materials offered full conversion (100%) with excellent selectivity (100%) at a relatively low temperature (250 °C). The catalyst exhibited a long-term stability for 120 h. Based on these results, DME is produced efficiently in terms of conversion, selectivity, and long-term stability.