Decorated PtRu Electrocatalyst for Concentrated Direct Methanol Fuel Cells

PdPtRu nanocages with tunable compositions for boosting the methanol oxidation reaction

PtRu/C is a well-known commercial electrocatalyst with promising performance for the methanol oxidation reaction (MOR). Further improving the MOR properties of PtRu-based electrocatalysts is highly desirable, especially through structure design. Here we report a facile approach for the synthesis of PdPtRu nanocages with different components through a seed-mediated approach followed by chemical etching. The Pd@PtRu nanocubes were first generated using Pd nanocubes as the seeds and some Pd atoms were subsequently etched away, leading to the nanocages. When evaluated as electrocatalysts for the MOR in acidic media, the PdPtRu nanocages exhibited substantially enhanced catalytic activity and stability relative to commercial Pt/C and PtRu/C. Specifically, PdPt_2.5Ru_2.4 achieved the highest specific (8.2 mA cm^-2) and mass (0.75 mA mg_Pt ^-1) activities for the MOR, which are 2.2 and 4.2 times higher than those of commercial Pt/C. Such an enhancement can be attributed to the highly open structure of the nanocages, and the possible synergistic effect between the three components.

One-Pot Microwave-Assisted Synthesis of Graphene-Supported PtCoM (M = Mn, Ru, Mo) Catalysts for Low-Temperature Fuel Cells

In this study, one-pot microwave-assisted synthesis was used to fabricate the graphene (GR)-supported PtCoM catalysts where M = Mn, Ru, and Mo. The catalysts with the molar ratios of metals Pt:Co:Mn, Pt:Co:Ru, and Pt:Co:Mo equal to 1:3:1, 1:2:2, and 7:2:1, respectively, were prepared. Catalysts were characterized using Transmission Electron Microscopy (TEM). The electrocatalytic activity of the GR-supported PtCoMn, PtCoRu, and PtCoMo catalysts was evaluated toward methanol oxidation in an alkaline medium employing cyclic voltammetry and chrono-techniques. The most efficient electrochemical characteristics demonstrated the PtCoMn/GR catalyst with a current density value of 144.5 mA cm−2, which was up to 4.8 times higher than that at the PtCoRu(1:2:2)/GR, PtCoMo(7:2:1)/GR, and bare Pt/GR catalysts.

Effect of Sb-Doped SnO2 Nanostructures on Electrocatalytic Performance of a Pt Catalyst for Methanol Oxidation Reaction

In this study, antimony-doped tin oxide (ATO) support materials for a Pt anode catalyst in direct methanol fuel cells were prepared and electrochemically evaluated. When the heating temperature was increased from 300 to 400 °C, the ATO samples exhibited a slightly decreased specific surface area and increased electrical conductivity. In particular, the ATO sample heated at 350 °C in an air atmosphere showed improved electrical conductivity (1.3 S cm−1) with an optimum specific surface area of ~34 m2 g−1. The supported Pt catalysts were synthesized using a polyol process with as-prepared and heated ATO samples and Vulcan XC-72R as supports (denoted as Pt/ATO, Pt/ATO-350, and Pt/C, respectively). In the methanol oxidation reaction (MOR), compared to Pt/C and Pt/ATO, Pt/ATO-350 exhibited the best electrocatalytic activity and stability for MOR, which could be attributed to Pt nanoparticles on the relatively stable oxide support with high electrical conductivity and interaction between the Pt catalyst and the heated ATO support.

Core-shell structured PtRu nanoparticles@FeP promoter with an efficient nanointerface for alcohol fuel electrooxidation

In this study, a bottleneck was overcome for direct alcohol fuel cells using state-of-the-art PtRu catalysts for alcohol fuel oxidation. Herein, a core-shell structured PtRu catalyst system based on the emerging promoter FeP was developed that showed excellent catalytic performance for the oxidation of alcohol fuels. The surface spectrometric analysis and morphology observation confirmed the formation of a nanointerface of the PtRu shell and FeP core hybrid catalyst (PtRu@FeP), and efficient ligand effects and electronic effects were found to result from the noble metal active sites and adjacent promoter in the core-shell structure. The facile formation of oxygen-containing species and the strong electronic effects could activate the Pt active sites, leading to high catalytic performance. High anti-CO poisoning ability was found for this catalyst system when compared with the case of the benchmark commercial PtRu/C catalyst (110 mV less and 60 mV less as evaluated by the peak and onset potentials for CO oxidation, respectively). The PtRu@FeP catalysts also exhibited much higher catalytic activity and stability when compared with commercial and home-made PtRu/C catalysts; specifically, the peak current density of the PtRu@FeP 1 : 1 catalyst was about 2 and 3 times higher than those of the commercial PtRu/C catalyst and home-made PtRu/C for the oxidation of the alcohol fuels methanol and ethanol; moreover, high catalytic efficiency, improved by 2 times, was found, as expressed by the specific activity. Excellent catalytic stability as evaluated by 1000 cycles of cyclic voltammetry measurements was also demonstrated for the PtRu@FeP catalysts. The high catalytic performance could be attributed to the intimate nanointerface contact of the core-shell structured PtRu shell over the FeP core via a bi-functional catalytic mechanism and electronic effects based on the ligand effect in this catalyst system. The current study is a significant step to increase the PtRu catalytic performance via nanointerface construction by a core-shell structure on a novel promoter for direct alcohol fuel cells.