Effect of Rh valence state and doping concentration on the structure and photocatalytic H2 evolution in (Nb,Rh) codoped TiO2 nanorods

The simultaneous realization of visible light response and high photocatalytic activity remains a challenging task for TiO2 despite extensive research. Herein, (Nb,Rh) codoping is adopted to extend the absorption band of anatase TiO2 into the visible-light region. Meanwhile, the dependence of the electronic structure, visible-light absorption, and photocatalytic performance on the dopant ratio as well as doping concentration is studied. Open shell t2g5 Rh(iv) and closed shell t2g6 Rh(iii) coexist in Rh-doped TiO2, and the codoped Nb promotes a change in valence state from Rh(iv) to Rh(iii). Rh(iii) is the main active species in charge of the excellent photocatalytic performance, while Rh(iv) doping introduces electron/hole recombination centres. However, surprisingly, a trace of Rh(iv)-doping contributes to a decrease in electron transfer resistance and an increase in donor density, which help to improve photocatalytic performance. By virtue of the controlled content of Rh(iii) and Rh(iv), Ti1-2xNbxRhxO2 exhibits a high hydrogen evolution rate of ∼9000 μmol g-1 h-1 in methanol solution, along with a remarkable photocurrent density of ∼9 μA cm-2 under visible-light irradiation, which are about 170 and 30 times higher than those of pristine TiO2 nanorods, respectively.

Constructing Rh–Rh3+ modified Ta2O5@TaON@Ta3N5 with special double n–n mutant heterojunctions for enhanced photocatalytic H2-evolution

A multiple core–shell heterostructure Rh–Rh³⁺ modified Ta₂O₅@TaON@Ta₃N₅ nanophotocatalyst was successfully constructed through nitriding Rh³⁺-doped Ta₂O₅ nanoparticles, which exhibited a much higher carrier separation efficiency about one order of magnitude higher than the Ta₂O₅@Ta₃N₅ precursor, and thus an excellent visible light photocatalytic H₂-evolution activity (83.64 μmol g⁻¹ h⁻¹), much superior to that of Rh anchored Ta₂O₅@TaON (39.41 μmol g⁻¹ h⁻¹), and improved stability due to the residual Rh–O/N in the Ta₃N₅ shell layer. Rh-modifying significantly extended light absorption to the overall visible region. Localized built-in electric fields with hierarchical potential gradients at the multiple interfaces including a Rh/Ta₃N₅ Schottky junction and double n–n Ta₃N₅/TaON/Ta₂O₅ mutant heterojunctions, drove charge carriers to directionally transfer from inside to outside, and efficiently separate. Enhanced photoactivity was ascribed to a synergetic effect of improved light absorption ability, increased carrier separation efficiency, and accelerated surface reaction. A promising strategy of developing excellent Ta₃N₅-based photocatalysts for solar energy conversion is provided by constructing double n–n mutant heterojunctions.

Localized built-in electric fields at multiple hierarchical interfaces facilitate the efficient separation and fast inside-out directional transfer of photogenerated carriers.