Structural stability and optical properties of 1D photonic crystals based on porous anodic alumina after annealing at different temperatures

Porous anodic alumina (PAA) photonic crystals with a photonic stop-band (PSB) placed in the mid-infrared (MIR) spectral region represent a promising approach for increasing of gas sensors sensitivity. An onion-like layered distribution of anionic impurities is a hallmark of PAA, and its presence is generally considered to demarcate the boundary between transparent and opaque ranges in the infrared spectral region. Here, we study the effect of annealing in the temperature range of 450 °C-1 100 °C on the structural stability and optical properties in photonic crystals based on PAA fabricated by pulse anodization in oxalic acid. Pulse sequences were selected in a way to obtain photonic crystals of different periodic structures with a PSB located in visible and MIR spectral regions. The first photonic crystal was composed of layers with gradually changing porosity, whereas the second photonic crystal consisted of a sequentially repeated double-layer unit with an abrupt change in porosity. We investigated the response of alumina with rationally designed porosities and different arrangements of porous layers for high-temperature treatment. The microstructure (scanning electron microscopy), phase composition (x-ray diffraction), and optical properties (optical spectroscopy) were analysed to track possible changes after annealing. Both photonic crystals demonstrated an excellent structural stability after 24 h annealing up to 950 °C. At the same time, the evaporation of the anionic impurities from PAA walls caused a shift of the PSB towards the shorter wavelengths. Furthermore, the annealing at 1 100 °C induced a high transparency (up to 90%) of alumina in MIR spectral region. It was shown thus that properly selected electrochemical and annealing conditions enable the fabrication of porous photonic crystals with the high transparency spanning the spectral range up to around 10μm.

Liquid permeation and chemical stability of anodic alumina membranes

A study on the chemical stability of anodic alumina membranes and their performance in long-term water and organic solvent permeation experiments is reported. Anodic alumina possesses high stability for both protonic and aprotonic organic solvents. However, serious degradation of the membrane occurs in pure water, leading to a drastic decrease of permeance (over 20% of the initial value after the passing of 0.250 m³/m² of pure water). The drying of the membrane induces further permeance drop-off. The rate of membrane degradation strongly depends on the pH of the penetrant solution and increases in basic media. According to ²⁷Al NMR and thermogravimetry results, the degradation of the membranes is associated with the dissolution of water-soluble [Al₁₃O₄(OH)₂₄(H₂O)₁₂]⁷⁺ polyhydroxocomplexes and their further redeposition in the form of [Al(OH)₄]^-, resulting in channels blocking. This process intensifies in basic pH due to the high positive charge of the anodic alumina surface. An approach for improving anodic aluminum oxide stability towards dissolution in water by carbon CVD coating of the membrane walls is suggested.