The color stability and wear resistance of provisional implant restorations: A prospective clinical study

Fracture strength test of digitally produced ceramic-filled and unfilled dental resin restorations via 3d printing: An in vitro study

Background

Purpose of this study was to investigate the mechanical efficiency of 3D-printed permanent and provisional implant cemented fixed bridges produced via CAD/CAM technology using an interim and a permanent ceramic filled hybrid material.

Material and Methods

Two groups with twenty specimens each were designed and 3D-printed via digital light processing technology (DLP). A fracture strength test was performed. Statistical analysis was performed (p>0.05) for impression distance and force.

Results

For the fracture resistance and impression distance no significant difference (p = 0.643) were detected. The specimens of interim resin showed a mean value of 365.90 ± 86.67 N. Whereas specimens of permanent ceramic filled hybrid material showed a mean value of 363.45 ± 87.57 N.

Conclusions

In this in vitro study 3D-printed ceramic filled hybrid material and interim resin based on methacrylic acid esters showed an acceptable resistance to bite forces with no differences in fracture mechanism. Key words:CAD-CAM, dental resin, 3D printing.

Wear of 3D printed and CAD/CAM milled interim resin materials after chewing simulation

PURPOSE

The purpose of this in vitro study was to investigate the wear resistance and surface roughness of three interim resin materials, which were subjected to chewing simulation.

MATERIALS AND METHODS

Three interim resin materials were evaluated: (1) three-dimensional (3D) printed (digital light processing type), (2) computer-aided design and computer-aided manufacturing (CAD/CAM) milled, and (3) conventional polymethyl methacrylate interim resin materials. A total of 48 substrate specimens were prepared. The specimens were divided into two subgroups and subjected to 30,000 or 60,000 cycles of chewing simulation (n = 8). The wear volume loss and surface roughness of the materials were compared. Statistical analysis was performed using one-way analysis of variance and Tukey's post-hoc test (α=.05).

RESULTS

The mean ± standard deviation values of wear volume loss (in mm³) against the metal abrader after 60,000 cycles were 0.10 ± 0.01 for the 3D printed resin, 0.21 ± 0.02 for the milled resin, and 0.44 ± 0.01 for the conventional resin. Statistically significant differences among volume losses were found in the order of 3D printed, milled, and conventional interim materials (P<.001). After 60,000 cycles of simulated chewing, the mean surface roughness (Ra; μm) values for 3D printed, milled, and conventional materials were 0.59 ± 0.06, 1.27 ± 0.49, and 1.64 ± 0.44, respectively. A significant difference was found in the Ra value between 3D printed and conventional materials (P=.01).

CONCLUSION

The interim restorative materials for additive and subtractive manufacturing digital technologies exhibited less wear volume loss than the conventional interim resin. The 3D printed interim restorative material showed a smoother surface than the conventional interim material after simulated chewing.

The color stability and wear resistance of provisional implant restorations: A prospective clinical study

Objectives

The aim of the present clinical study was to determine the stability of color and resistance against abrasion and attrition of provisional single implant restorations.

Material and Methods

A group of 16 patients were treated with provisional crowns made of Telio CAD. Shortly before the insertion the crowns were photographed and scanned using a 3D‐laser scanner. After 8 weeks of clinical usage, the crowns were photographed and scanned again. The vertical occlusal wear and color changes between the restorations were measured.

Results

The occlusal plane of the original crown showed a statistically significant reduction of 0.052 mm ± 0.037 mm 8 weeks after placement (p < .05). For the stability of color, a change in red, green and blue was described. All three scopes (red, green and blue) showed a statistically significant reduction (p < .05).

Conclusions

This prospective clinical study showed that Telio CAD experienced a significant occlusal reduction and color change after an intraoral placement of 8 weeks.