Investigation of the Hydrogenation of 5-Methylfurfural by Noble Metal Nanoparticles in a Microcapillary Reactor

H2-D2 Exchange Activity and Electronic Structure of Ag x Pd1-x Alloy Catalysts Spanning Composition Space

Many computational studies of catalytic surface reaction kinetics have demonstrated the existence of linear scaling relationships between physical descriptors of catalysts and reaction barriers on their surfaces. In this work, the relationship between catalyst activity, electronic structure, and alloy composition was investigated experimentally using a Ag x Pd1-x Composition Spread Alloy Film (CSAF) and a multichannel reactor array that allows measurement of steady-state reaction kinetics at 100 alloy compositions simultaneously. Steady-state H2-D2 exchange kinetics were measured at atmospheric pressure on Ag x Pd1-x catalysts over a temperature range of 333-593 K and a range of inlet H2 and D2 partial pressures. X-ray photoelectron spectroscopy (XPS) was used to characterize the CSAF by determining the local surface compositions and the valence band electronic structure at each composition. The valence band photoemission spectra showed that the average energy of the valence band, ε̅v, shifts linearly with composition from -6.2 eV for pure Ag to -3.4 eV for pure Pd. At all reaction conditions, the H2-D2 exchange activity was found to be highest on pure Pd and gradually decreased as the alloy was diluted with Ag until no activity was observed for compositions with x Pd < 0.58. Measured H2-D2 exchange rates across the CSAF were fit using the Dual Subsurface Hydrogen (2H') mechanism to extract estimates for the activation energy barriers to dissociative adsorption, ΔE ads ‡, associative desorption, ΔE des ‡, and the surface-to-subsurface diffusion energy, ΔE ss, as a function of alloy composition, x Pd. The 2H' mechanism predicts ΔE ads ‡ = 0-10 kJ/mol, ΔE des ‡ = 30-65 kJ/mol, and ΔE ss = 20-30 kJ/mol for all alloy compositions with x Pd ≥ 0.64, including for the pure Pd catalyst (i.e., x Pd = 1). For these Pd-rich catalysts, ΔE des ‡ and ΔE ss appeared to increase by ∼5 kJ/mol with decreasing x Pd. However, due to the coupling of kinetic parameters in the 2H' mechanism, we are unable to exclude the possibility that the kinetic parameters predicted when x Pd ≥ 0.64 are identical to those predicted for pure Pd. This suggests that H2-D2 exchange occurs only on bulk-like Pd domains, presumably due to the strong interactions between H2 and Pd. In this case, the decrease in catalytic activity with decreasing x Pd can be explained by a reduction in the availability of surface Pd at high Ag compositions.

Towards Improved Biorefinery Technologies: 5-Methylfurfural as a Versatile C6 Platform for Biofuels Development

Low chemical stability and high oxygen content limit utilization of the bio-based platform chemical 5-(hydroxymethyl)furfural (HMF) in biofuels development. In this work, Lewis-acid-catalyzed conversion of renewable 6-deoxy sugars leading to formation of more stable 5-methylfurfural (MF) is carried out with high selectivity. Besides its higher stability, MF is a deoxygenated analogue of HMF with increased C/O ratio. A highly selective synthesis of the innovative liquid biofuel 2,5-dimethylfuran starting from MF under mild conditions is described. The superior synthetic utility of MF against HMF in benzoin and aldol condensation reactions leading to long-chain alkane precursors is demonstrated.