Electrochemically Directed Synthesis of Co 2+ and Ni 2+ Complexes with TCNQF 4 2– (TCNQF 4 = 2,3,5,6‐Tetrafluoro‐7,7,8,8‐tetracyanoquinodimethane)

Electrochemically Directed Synthesis of Cobalt(II) and Nickel(II) TCNQF21–/2– Coordination Polymers: Solubility and Substituent Effects in the TCNQFn (n=0, 1, 2, 4) Series of Complexes

The reversible diffusion controlled cyclic voltammetry for the reduction of TCNQF­n0/1–/2– (where n=0, 1, 2, 4) changes significantly on addition of Co2+ and Ni2+ transition metal ions (M2+) because the kinetics associated with electrocrystallisation of the resulting coordination polymers [M(TCNQF2)2(H2O)2] and [M(TCNQF2)] are rapid on the voltammetric time scale. The voltammetry of solutions containing M2+ and TCNQF­2 was undertaken in acetonitrile (0.1M Bu4NPF6) at both GC and ITO electrodes. New one electron reduced TCNQF2 materials prepared via electrochemically directed synthesis were shown to have the formula [M(TCNQF2)2(H2O)2], assessed by vibrational (IR and Raman) spectroscopy, elemental analysis and thermogravimetric analysis. The solubility of [Ni(TCNQF2)2(H2O)2] (Ksp=8.29×10−11 M3) was significantly higher than the [Co(TCNQF2)2(H2O)2] (Ksp=1.43×10−11M3). Cyclic voltammetric data suggest the electrocrystallisation of two phases of [Ni(TCNQF2)2(H2O)2] occurs, which is not evident for [Co(TCNQF2)2(H2O)2]. Electrocrystallisation of the highly insoluble [M(TCNQF2)] was achieved at low M2+ and TCNQF2 concentrations. A comparison with published data on the voltammetry of TCNQF­n (n=0, 1, 2 and 4) for the series of TCNQF­n (n=0, 1, 2 and 4) containing M2+ is provided. An assessment of the electronic impact of the fluorine substituent of the underlying redox reactions also is established. Predictions are made for the voltammetric behaviour expected for the other transition metal cations with reduced TCNQFn derivatives.

Controlling nickel nanoparticle size in an organic/metal-organic matrix through the use of different solvents

Nickel nanoparticles have been created in an organic-based matrix by the reaction of Ni(COD)2 (COD = 1,5-bis-cyclooctadiene) and 2,3,5,6-tetrafluoro-7,7,8,8-tetracyanoquinodimethane (TCNQF4). The size of the nickel nanoparticles can be controlled by the use of different solvents and inclusion of tetrahydrofuran (THF) within the reaction to stabilise the Ni(0) atoms from the Ni(COD)2. Materials are characterised with a combination of X-ray diffraction, electron microscopy and magnetometry and it is found that samples made using a halocarbon solvent resulted in clustered bulk Ni particles (size ≤ 10 nm) with anomalously high superparamagnetic blocking temperatures. Using an isocyanide solvent produces smaller (size ∼ 1 nm), well dispersed particles that show little evidence of superparamagnetic blocking in the range of temperatures investigated (>2 K). In all samples there is another component which dominates the magnetic response at low temperatures and shows an interesting temperature dependent scaling behaviour when plotted as M vs. B/T which we believe is related to the organo-metallic matrix that the particles are trapped within. We propose that the enhanced blocking temperature of particles synthesised using halocarbon solvents can be attributed to inter-particle dipolar interactions and nanoparticle-matrix exchange interactions.