A stable and highly luminescent 3D Eu(III)-organic framework for the detection of colchicine in aqueous environment

The metal-organic framework materials have an important application as sensors. In this work, a microporous three-dimensional (3D) Eu(III)-organic framework (Eu-MOF), [Eu₂(3,5-bct)(phen)₂(ox)₂(H₂O)]·H₂O, was constructed from 3,5-bis(3'-carboxyphenyl)-1,2,4-triazole (3,5-H₂bct), oxalate (ox) and 1,10-phenanthroline (phen) as a luminescent sensor. The free volume was found to be 15.7% per unit volume ignoring the free water molecules. The Eu-MOF showed bright red light due to the emission at 622 nm (⁵D₀ → ⁷F₂ transition) of the Eu(III) with high quantum yield (QY, 52.51%). The Eu-MOF exerted high luminescence stability in common organic solvents as well as aqueous solutions within a wide pH range from 4 to 11. Based on the luminescent Eu-MOF, the sensing behavior for colchicine in the aqueous environment was studied. Highly selective and sensitive detection (LOD = 2.43 × 10^-5 mol L^-1) of colchicine was observed by the Eu-MOF even in the presence of potential interfering components. The sensing mechanism for colchicine was investigated by experimental and theoretical results. It is worth noting that a film (Film@Eu-MOF) prepared by loading Eu-MOF showed intense characteristic red light emission under UV light. The luminescence color changed immediately from red to colorless when the Film@Eu-MOF came in contact with colchicine. Highly sensitive and rapid detection of colchicine in wastewater was achieved using this Film@Eu-MOF, which could be identified by the naked eye. The experimental results suggest that the synthesized Eu-MOF has potential application as a luminescent sensing material for pollutants in the environmental system.

A Comprehensive Study on the Dye Adsorption Behavior of Polyoxometalate-Complex Nano-Hybrids Containing Classic β-Octamolybdate and Biimidazole Units

Six new hybrids based on β-[Mo₈O26]4- polyoxometalates, [Ni(H₂biim)₃]₂[β-Mo₈O26]•8DMF(1); (DMA)₂[M(H₂biim)₂(H₂O)₂][β-Mo₈O26]•4DMF (M = Ni (2), Co (3)), DMA = dimethyl-ammonium, H₂biim=2,2'-biimidazole); [M(H₂biim)(DMF)₃]₂[β-Mo₈O26]•2DMF (M = Zn (4), Cu (5)); [(DMA)₂[Cu(DMF)₄][β-Mo₈O26]•2DMF]n (6), have been successfully synthesized and characterized. Compounds 2⁻5 show favorable capacity to adsorb methylene blue (MB) at room temperature, and they can selectively capture MB molecules from binary-mixture solutions of MB/MO (MO = Methyl Orange), or MB/RhB (RhB = Rhodamine B). Compound 3 can uptake up to 521.7 mg g-1 MB cationic dyes rapidly, which perform the maximum adsorption in an hour among the reported materials as far as we know. The compounds are stable and still work very efficiently after three cycles. For compound 3, the preliminary adsorption mechanism studies indicated that the adsorption is an ion exchange process and the adsorption behavior of polyoxometalate-complex can be benefited from additional exchangeable protons in the complex cations.

The synthesis, structure and catalytic properties of the [Mo7O24(μ-Mo8O26)Mo7O24]16− anion formed via two intermediate heptamolybdates [Co(en)3]2[NaMo7O24]Cl·nH2O and (H3O)[Co(en)3]2[Mo7O24]Cl·9H2O

Ageing a mixture of sodium molybdate, malonic acid, and tris(ethylenediamine)cobalt(iii) chloride yielded POMs.

Various polyoxomolybdate-based hybrids induced by pH and solvents: structures, adsorption activities for dyes and bifunctional electrocatalytic properties

By changing the pH values and solvents, four different polyoxomolybdate hybrids were synthesized, which display good adsorption activities for different organic dyes and bifunctional electrocatalytic properties.