Hf-based Metal-Organic Frameworks in Heterogeneous Catalysis

Syntheses and High Proton Conductivities of Two 3D Zr(IV)/Hf(IV)-MOFs from Furandicarboxylic Acid

With the gradual progress of research on proton-conducting metal-organic framework (MOFs), it has become a challenging task to find MOF materials that are easy to prepare and have low toxicity, high stability, and splendid proton conductivity. With the abovementioned objectives in mind, we selected the non-toxic organic ligand 2,5-furandicarboxylic acid and the low toxic quadrivalent metals zirconium(IV) or hafnium(IV) as starting materials and successfully obtained 2 three-dimensional porous MOFs, [M6O4(OH)4(FDC)4(OH)4(H2O)4] [M = ZrIV (1) and HfIV (2)], with ultrahigh water stability using a rapid and green synthesis approach. Their proton conductive ability is remarkable, thanks to the large number of Lewis acidic sites contained in their porous frameworks and the abundant H-bonding network, hydroxyl groups, as well as coordination and crystalline water molecules. The positive correlation of their proton conductivity with relative humidity (RH) and the temperature was observed. Notably, their optimized proton conductivities are 2.80 × 10-3 S·cm-1 of 1 and 3.38 × 10-3 S·cm-1 of 2 under 100 °C/98% RH, which are at the forefront of Zr(IV)/Hf(IV) MOFs with prominent proton conductivity. Logically, their framework features, nitrogen/water adsorption/desorption data, and activation energy values are integrated to deduce their proton conductivity and conducting mechanism differences.

Principles of Design and Synthesis of Metal Derivatives from MOFs

Materials derived from metal-organic frameworks (MOFs) have demonstrated exceptional structural variety and complexity and can be synthesized using low-cost scalable methods. Although the inherent instability and low electrical conductivity of MOFs are largely responsible for their low uptake for catalysis and energy storage, a superior alternative is MOF-derived metal-based derivatives (MDs) as these can retain the complex nanostructures of MOFs while exhibiting stability and electrical conductivities of several orders of magnitude higher. The present work comprehensively reviews MDs in terms of synthesis and their nanostructural design, including oxides, sulfides, phosphides, nitrides, carbides, transition metals, and other minor species. The focal point of the approach is the identification and rationalization of the design parameters that lead to the generation of optimal compositions, structures, nanostructures, and resultant performance parameters. The aim of this approach is to provide an inclusive platform for the strategies to design and process these materials for specific applications. This work is complemented by detailed figures that both summarize the design and processing approaches that have been reported and indicate potential trajectories for development. The work is also supported by comprehensive and up-to-date tabular coverage of the reported studies.

High Protonic Conductivity of Three Highly Stable Nanoscale Hafnium(IV) Metal-Organic Frameworks and Their Imidazole-Loaded Products

Attracted by the exceptional structural rigidity and inherent porous structures of the Hf-based metal-organic frameworks (MOFs), we adopted a rapid synthesis approach to preparing three nanoscale MOFs, Hf-UiO-66 (1), Hf-UiO-66-(OH)₂ (2), and Hf-UiO-66-NH₂ (3), and systematically explored the water-assisted proton conductivities of the original ones and the post-modified products. Interestingly, the proton conductivities (σ) of all three MOFs exhibit significant temperature and humidity dependence. At 98% RH and 100 °C, their optimal σ values can reach up to 10^-3 S·cm^-1. Consequently, imidazole units are loaded into 1-3 to obtain related MOFs, Im@1, Im@2, and Im@3, and the σ values of the imidazole-loaded products are boosted to 10^-2 S·cm^-1. Note that these modifications not only do not change the frameworks of the pristine MOFs but also do not affect their high chemical and water stability. The proton-conductive mechanisms of these MOFs before and after modification have been thoroughly discussed based on structural analyses, N₂ and H₂O vapor adsorptions, and activation energy values. The excellent structural stability as well as the durability and stability of their proton conduction ability indicate that these MOFs can be used in the field of fuel cells and so on.

Coordinatively Unsaturated Hf-MOF-808 Prepared via Hydrothermal Synthesis as a Bifunctional Catalyst for the Tandem N-Alkylation of Amines with Benzyl Alcohol

The modulated hydrothermal (MHT) synthesis of an active and selective Hf-MOF-808 material for the N-alkylation reaction of aniline with benzyl alcohol under base-free mild reaction conditions is reported. Through kinetic experiments and isotopically labeled NMR spectroscopy studies, we have demonstrated that the reaction mechanism occurs via borrowing hydrogen (BH) pathway, in which the alcohol dehydrogenation is the limiting step. The high concentration of defective -OH groups generated on the metallic nodes through MHT synthesis enhances the alcohol activation, while the unsaturated Hf⁴⁺, which acts as a Lewis acid site, is able to borrow the hydrogen from the methylene position of benzyl alcohol. This fact makes this material at least 14 times more active for the N-alkylation reaction than the material obtained via solvothermal synthesis. The methodology described in this work could be applied to a wide range of aniline and benzyl alcohol derivates, showing in all cases high selectivity toward the corresponding N-benzylaniline product. Finally, Hf-MOF-808, which acts as a true heterogeneous catalyst, can be reused in at least four consecutive runs without any activity loss.

Heterogeneous nanozymatic activity of Hf oxo-clusters embedded in a metal-organic framework towards peptide bond hydrolysis

Materials with enzyme-like activities and proteolytic potential are emerging as a robust and effective alternative to natural enzymes. Herein, a Hf₆O₈-based NU-1000 metal organic framework (Hf-MOF) is shown to act as a heterogeneous catalyst for the hydrolysis of peptide bonds under mild conditions. In the presence of Hf-MOF, a glycylglycine model dipeptide was hydrolysed with a rate constant of k_obs = 8.33 × 10^-7 s^-1 (half-life (t_1/2) of 231 h) at 60 °C and pD 7.4, which is significantly faster than the uncatalyzed reaction. Other Gly-X peptides (X = Ser, Asp, Ile, Ala, and His) were also smoothly hydrolysed under the same conditions with similar rates, except for the faster reactions observed for Gly-His and Gly-Ser. Moreover, the Hf₆O₈-based NU-1000 MOF also exhibits a high selectivity in the cleavage of a protein substrate, hen egg white lysozyme (HEWL). Our results suggest that embedding Hf₆O₈ oxo-clusters is an efficient strategy to conserve the hydrolytic activity while smoothing the strong substrate adsorption previously observed for a discrete Hf oxo-cluster that hindered further development of its proteolytic potential. Furthermore, comparison with isostructural Zr-NU-1000 shows that although the Hf variant afforded the same cleavage pattern towards HEWL but slightly slower reaction rates, it exhibited a larger stability window and a better recyclability profile. The results suggest that these differences originate from the intrinsic differences between Hf^IV and Zr^IV centers, and from the lower surface area of Hf-NU-1000 in comparison to Zr-NU-1000.

Tailoring Lewis/Brønsted acid properties of MOF nodes via hydrothermal and solvothermal synthesis: simple approach with exceptional catalytic implications

The Lewis/Brønsted catalytic properties of the Metal-Organic Framework (MOF) nodes can be tuned by simply controlling the solvent employed in the synthetic procedure. In this work, we demonstrate that Hf-MOF-808 can be prepared from a material with a higher amount of Brønsted acid sites, via modulated hydrothermal synthesis, to a material with a higher proportion of unsaturated Hf Lewis acid sites, via modulated solvothermal synthesis. The Lewis/Brønsted acid properties of the resultant metallic clusters have been studied by different characterization techniques, including XAS, FTIR and NMR spectroscopies, combined with a DFT study. The different nature of the Hf-MOF-808 materials allows their application as selective catalysts in different target reactions requiring Lewis, Brønsted or Lewis-Brønsted acid pairs.

Hybrids of Pd Nanoparticles and Metal-Organic Frameworks for Enhanced Magnetism

Nonmagnetic Pd exhibits ferromagnetism in the nanosize regime. Various stabilization agents, including surfactants, metal oxide supports, polymers, and porous materials (e.g., metal-organic frameworks (MOFs)), have been employed to prevent the agglomeration of metal nanoparticles. However, magnetic properties are greatly affected by the structural and electronic changes imposed by these stabilizing agents. In particular, metal-MOF hybrids (NPs@MOFs) have reduced magnetic properties, as reported by several authors. Herein, we report the enhancement in magnetic properties resulting from the combination of magnetic Pd NPs with UiO-66(Hf), which exhibits ferromagnetism, and the corresponding modifications in the hybridized structures. These hybridized structures are found to be strongly ferromagnetic, showing high magnetization and coercivity. We observed that the magnetic property is enhanced by 2 to 3 times upon including the Pd NPs on the surface of a UiO-66(Hf) shell support. For a fundamental understanding, the magnetization (M-H data) of the hybridized structure is analyzed with a modified Langevin function.

A hafnium-based metal-organic framework for the entrapment of molybdenum hexacarbonyl and the light-responsive release of the gasotransmitter carbon monoxide

A carbon monoxide-releasing material (CORMA) has been prepared by inclusion of molybdenum hexacarbonyl in a hafnium-based metal-organic framework (MOF) with the UiO-66 architecture. Mo(CO)₆ was adsorbed from solution to give supported materials containing 6.0-6.6 wt% Mo. As confirmed by powder X-ray diffraction (PXRD) and SEM coupled with energy dispersive X-ray spectroscopy, neither the crystallinity nor the morphology of the porous host was affected by the loading process. While the general shape of the N₂ physisorption isotherms (77 K) did not change significantly after encapsulation of Mo(CO)₆, the micropore volume decreased by ca. 20%. Thermogravimetric analysis of the as-prepared materials revealed a weight loss step around 160 °C associated with the decomposition of Mo(CO)₆ to subcarbonyl species. Confirmation for the presence of encapsulated Mo(CO)₆ complexes was provided by FT-IR and ¹³C{¹H} cross-polarization magic-angle spinning NMR spectroscopies. To test the capability of these materials to behave as CORMAs and transfer CO to heme proteins, the standard myoglobin (Mb) assay was used. While stable in the dark, photoactivation with low-power UV light (365 nm) liberated CO from the encapsulated hexacarbonyl molecules in Mo(6.0)/UiO-66(Hf), leading to a maximum amount of 0.26 mmol CO released per gram of material. Under the simulated physiological conditions of the Mb assay (37 °C, pH 7.4 buffer), minimal leaching of molybdenum occurred, PXRD showed only slight amorphization, and FT-IR spectroscopy confirmed the high chemical stability of the MOF host.

The chemistry and applications of hafnium and cerium(iv) metal-organic frameworks

The coordination connection of organic linkers to the metal clusters leads to the formation of metal-organic frameworks (MOFs), where the metal clusters and ligands are spatially entangled in a periodic manner. The immense availability of tuneable ligands of different length and functionalities gives rise to robust molecular porosity ranging from several angstroms to nanometres. Among the large family of MOFs, hafnium (Hf) based MOFs have been demonstrated to be highly promising for practical applications due to their unique and outstanding characteristics such as chemical, thermal, and mechanical stability, and acidic nature. Since the report of UiO-66(Hf) and DUT-51(Hf) in 2012, less than 200 Hf-MOFs (ca. 50 types of structures) have been reported. Besides, tetravalent cerium [Ce(iv)] has been proven to be capable of forming similar topological MOF structures to Zr and Hf since its first discovery in 2015. So far, ca. 40 Ce(iv) MOFs with 60% having UiO-66-type structure have been reported. This review will offer a holistic summary of the chemistry, uniqueness, synthesis, and applications of Hf/Ce(iv)-MOFs with a focus on presenting the development in the Hf/Ce(iv)-clusters, topologies, ligand structures, synthetic strategies, and practical applications of Hf/Ce(iv)-MOFs. In the end, we will present the research outlook for the development of Hf/Ce(iv)-MOFs in the future, including fundamental design of Hf/Ce(iv)-clusters, defect engineering, and various applications including membrane development, diversified types of catalytic reactions, irradiation absorption in nuclear waste treatment, water production and wastewater treatment, etc. We will also present the emerging computational approaches coupled with machine-learning algorithms that can be applied in screening Hf and Ce(iv) based MOF structures and identifying the best-performing MOFs for tailor-made applications in future practice.

Cooperative catalysis at the metal–MOF interface: hydrodeoxygenation of vanillin over Pd nanoparticles covered with a UiO-66(Hf) MOF

Cooperative catalysis has been demonstrated over metal–MOF hybrids for the conversion of vanillin (biomass based platform molecules) into value-added 2-methoxy-4-methylphenol.