Key issues involved with the use of miniature specimens in the characterization of the mechanical behavior of polymeric biomaterials--a review

Influence of the activator in an acrylic bone cement on an array of cement properties

In all but one of the acrylic bone cement brands used in cemented arthroplasties, N,N-dimethyl-4-toluidine (DMPT) serves as the activator of the polymerization reaction. However, many concerns have been raised about this activator, all related to its toxicity. Thus, various workers have assessed a number of alternative activators, with two examples being N,N-dimethylamino-4-benzyl laurate (DMAL) and N,N-dimethylamino-4-benzyl oleate (DMAO). The results of limited characterization of cements that contain DMAL or DMAO have been reported in the literature. The present work is a comprehensive comparison of cements that contain one of these three activators, in which the values of a large array of their properties were determined. These properties range from the setting time and maximum exotherm temperature of the curing cement to the variation of the loss elastic modulus of the cured cement with frequency of the applied indenting force in dynamic nanoindentation tests. The present results, taken in conjunction with those presented in previous reports by the present authors and co-workers on other properties of these cements, indicate that both DMAL and DMPT are suitable alternatives to DMPT.

The mechanical properties of recovered PMMA bone cement: a preliminary study

Samples of polymethylmethacrylate (PMMA) bone cement, used in the fixation of hip prostheses, have been recovered from 11 patients after in service life spans of between 15 and 24 years. Eighteen samples in total have been recovered from the acetabular and/or femoral cement. Samples were subjected to three point bending tests, their density, porosity and microhardness determined and all specimens were examined using EDX and X-ray techniques. Since the porosity of many of the samples is very high, the continuous matrix properties are inferred from the performance of individual specimens. No evidence has been found to suggest that the PMMA has deteriorated whilst in-vivo and the mechanical properties of the cement matrices appear to be comparable to freshly made PMMA.

3D fiber-deposited scaffolds for tissue engineering: influence of pores geometry and architecture on dynamic mechanical properties

One of the main issues in tissue engineering is the fabrication of scaffolds that closely mimic the biomechanical properties of the tissues to be regenerated. Conventional fabrication techniques are not sufficiently suitable to control scaffold structure to modulate mechanical properties. Within novel scaffold fabrication processes 3D fiber deposition (3DF) showed great potential for tissue engineering applications because of the precision in making reproducible 3D scaffolds, characterized by 100% interconnected pores with different shapes and sizes. Evidently, these features also affect mechanical properties. Therefore, in this study we considered the influence of different structures on dynamic mechanical properties of 3DF scaffolds. Pores were varied in size and shape, by changing fibre diameter, spacing and orientation, and layer thickness. With increasing porosity, dynamic mechanical analysis (DMA) revealed a decrease in elastic properties such as dynamic stiffness and equilibrium modulus, and an increase of the viscous parameters like damping factor and creep unrecovered strain. Furthermore, the Poisson's ratio was measured, and the shear modulus computed from it. Scaffolds showed an adaptable degree of compressibility between sponges and incompressible materials. As comparison, bovine cartilage was tested and its properties fell in the fabricated scaffolds range. This investigation showed that viscoelastic properties of 3DF scaffolds could be modulated to accomplish mechanical requirements for tailored tissue engineered applications.

Three-dimensional fiber-deposited PEOT/PBT copolymer scaffolds for tissue engineering: Influence of porosity, molecular network mesh size, and swelling in aqueous media on dynamic mechanical properties

Among novel scaffold fabrication techniques, 3D fiber deposition (3DF) has recently emerged as a means to fabricate well-defined and custom-made scaffolds for tissue regeneration, with 100% interconnected pores. The mechanical behavior of these constructs is dependent not only on different three-dimensional architectural and geometric features, but also on the intrinsic chemical properties of the material used. These affect the mechanics of the solid material and eventually of 3D porous constructs derived from them. For instance, poly(ethylene oxide terephthalate)-poly(butylene terephthalate) (PEOT/PBT) block copolymers are known to have mechanical properties, depending on the PEOT/PBT weight ratio in block form and on the molecular weight of the initial poly(ethylene glycol) (PEG) blocks. These differences are enhanced even more by their different swelling properties in aqueous media. Therefore, this article examines the influence of copolymer compositions in terms of their swelling on dynamic mechanical properties of solid material and porous 3DF scaffolds. The molecular weight of the starting PEG blocks used in the copolymer synthesis varied from 300 to 1000 g/mol. The PEOT/PBT weight ratio in the blocks used varied from 55/45 to 80/20. This corresponded to an increase of the swelling ratio Q from 1.06 to 2.46, and of the mesh size xi from approximately 9 Angstrom to approximately 47 Angstrom. With increased swelling, dynamic mechanical analysis (DMA) revealed a decrease in elastic response and an increase of viscoelasticity. Thus, by coupling structural and chemical characteristics, the viscoelastic properties of PEOT/PBT 3DF scaffolds may be fine tuned to achieve mechanical requirements for a variety of engineered tissues. Ultimately, the combination of 3DF and DMA may be useful to validate the hypothesis that mimicking the biomechanical behavior of a specific tissue for its optimal replacement is an important issue for at least some tissue-engineering applications.

Quasi-static and dynamic nanoindentation studies on highly crosslinked ultra-high-molecular-weight polyethylene

In four separate studies, the effect of three methods used to highly crosslink ultra-high-molecular-weight polyethylene (UHMWPE) (gamma irradiation, electron beam irradiation, and peroxide treatment) on the polymer's stiffness was investigated using quasi-static and dynamic nanoindentation. From the quasi-static studies, it was found that (a) the highest value of the elastic modulus, E (2240 +/- 157 MPa) was obtained from specimens prepared from direct compression molded UHMWPE crosslinked using gamma irradiation, with a dosage of 7.5 Mrad; (b) the value of E for specimens formed from direct compression molded UHMWPE was higher (1950 +/- 255 MPa) compared to results obtained from specimens formed from ram extruded UHMWPE (1583 +/- 140 MPa); and (c) the magnitude of the decrease in the value of E as a result of subjecting a highly crosslinked UHMWPE specimen to uniaxial tensile forces depends on the method used for the crosslinking. From the dynamic study, (d) it was found that the extent of the change in both the storage modulus and the loss modulus, as a result of subjecting a highly crosslinked UHMWPE specimen to uniaxial tension forces, depends on the method used for the crosslinking.