Effects of bioactive glass particles and their ionic products on intracellular concentrations

A review of the biological response to ionic dissolution products from bioactive glasses and glass-ceramics

Several inorganic materials such as special compositions of silicate glasses, glass-ceramics and calcium phosphates have been shown to be bioactive and resorbable and to exhibit appropriate mechanical properties which make them suitable for bone tissue engineering applications. However, the exact mechanism of interaction between the ionic dissolution products of such inorganic materials and human cells are not fully understood, which has prompted considerable research work in the biomaterials community during the last decade. This review comprehensively covers literature reports which have investigated specifically the effect of dissolution products of silicate bioactive glasses and glass-ceramics in relation to osteogenesis and angiogenesis. Particularly, recent advances made in fabricating dense biomaterials and scaffolds doped with trace elements (e.g. Zn, Sr, Mg, and Cu) and investigations on the effect of these elements on the scaffold biological performance are summarized and discussed in detail. Clearly, the biological response to artificial materials depends on many parameters such as chemical composition, topography, porosity and grain size. This review, however, focuses only on the ion release kinetics of the materials and the specific effect of the released ionic dissolution products on human cell behaviour, providing also a scope for future investigations and identifying specific research needs to advance the field. The biological performance of pure and doped silicate glasses, phosphate based glasses with novel specific compositions as well as several other silicate based compounds are discussed in detail. Cells investigated in the reviewed articles include human osteoblastic and osteoclastic cells as well as endothelial cells and stem cells.

Imaging physicochemical reactions occurring at the pore surface in binary bioactive glass foams by micro ion beam analysis

In this work, the physicochemical reactions occurring at the surface of bioactive sol-gel derived 3D glass scaffolds via a complete PIXE characterization were studied. 3D glass foams in the SiO(2)-CaO system were prepared by sol-gel route. Samples of glass scaffolds were soaked in biological fluids for periods up to 2 days. The surface changes were characterized using particle induced X-ray emission (PIXE) associated to Rutherford backscattering spectroscopy (RBS), which are efficient methods to perform quantitative chemical maps. Elemental maps of major and trace elements at the glass/biological fluids interface were obtained at the micrometer scale for every interaction time. Results revealed interconnected macropores and physicochemical reactions occurring at the surface of pores. The micro-PIXE-RBS characterization of the pores/biological fluids interface shows the glass dissolution and the rapid formation of a Ca rich layer with the presence of phosphorus that came from biological fluids. After 2 days, a calcium phosphate-rich layer containing magnesium is formed at the surface of the glass scaffolds. We demonstrate that quantities of phosphorus provided only by the biological medium have a significant impact on the development and the formation of the phosphocalcic layer.

Cryo-X-ray analysis-A novel tool to better understand the physicochemical reactions at the bioglass/biological fluid interface

The present study deals with the short-term physicochemical reactions at the interface between bioactive glass particles [55SiO(2)-20CaO-9P(2)O(5)-12Na(2)O-4MgO. mol%] and biological fluid (Dulbecco Modified Eagle's Medium (DMEM)). The physicochemical reactions within the interface are characterized by scanning transmission electron microscopy (TEM) (STEM) associated with Energy-dispersive X-ray spectroscopy (EDXS). Microanalysis of diffusible ions such as sodium, potassium, or oxygen requires a special care. In the present investigation the cryo-technique was adopted as a suitable tool for the specimen preparation and characterization. Cryosectioning is essential for preserving the native distribution of ions so that meaningful information about the local concentrations can be obtained by elemental microanalysis. The bioglass particles immersed in biological fluid for 24 h revealed five reaction stages: (i) dealkalization of the surface by cationic exchange (Na(+), Ca(2+) with H(+) or H(3)O(+)); (ii) loss of soluble silica in the form of Si(OH)(4) to the solution resulting from the breakdown of Si--O--Si bonds (iii); repolymerization of Si(OH)(4) leading to condensation of SiO(2)); (iv) migration of Ca(2+) and PO(4) (3-) to the surface through the SiO(2)-rich layer to form CaO-P(2)O(5) film; (v) crystallization of the amorphous CaO-P(2)O(5) by incorporating OH-- or CO(3) (2-) anions with the formation of three different surface layers on the bioactive glass periphery. The thickness of each layer is approximately 300 nm and from the inner part to the periphery they consist of Si--OH, which permits the diffusion of Ca(2+) and PO(4) (3-) ions and the formation of the middle Ca--P layer, and finally the outer layer composed of Na--O, which acts as an ion exchange layer between Na(+) ions and H(+) or H(3)O(+) from the solution.

Potential of biomimetic surfaces to promote in vitro osteoblast-like cell differentiation

Bioactive glasses, osteoproductive materials, have received considerable attention as bone graft substitutes in the treatment of bony defects. More recent strategies for achieving a predictable periodontal regeneration include the use of enamel matrix proteins, due to their role in the formation of bone tissue. The aim of our study is to examine the effects of these materials on the proliferation and differentiation of the mouse preosteoblastic cell line MC3T3-E1. Cells were cultured up to 28 days in contact with three types of granules: Bioglass 45S5 granules (BG), 45S5 granules coated with enamel matrix proteins (Emdogain) (BG/EMD), and a less reactive glass used as a control (60S). Phase contrast microscopic observations have shown that all substrates supported the growth of osteoblastic cells. Zones of differentiation were observed at an earlier stage in cultures of BG and BG/EMD. TEM observations revealed ultrastructural features very close to what is observed in vivo during intramembranous ossification with a direct bone apposition on the bioactive glasses. Total protein production was higher in the cultures with BG and BG/EMD. Northern Blot analysis revealed a stimulation of the transcription factor Cbfa1/Runx2 at day 13 in cultures of BG when compared to the two other cultures. Bone sialoprotein (early marker of differentiation) and osteocalcin (marker of late-stage differentiation) expression was increased in cultures with BG and BG/EMD when compared to 60S. Taken together, our findings indicate that Bioglass alone or combined with Emdogain, have the ability to support the growth of osteoblast-like cells in vitro and to promote osteoblast differentiation by stimulating the expression of major phenotypic markers. In addition, we noticed that the bioactive granules coated with Emdogain revealed significantly higher protein production than the bioactive granules alone at day 20.

Cytotoxicity of three-dimensionally ordered macroporous sol-gel bioactive glass (3DOM-BG)

In this study, 80% SiO(2)-20% CaO (mole fraction) three-dimensionally ordered macroporous sol-gel bioactive glass (3DOM-BG, average pore size: 345 nm) particles were prepared and characterized. Since the 3DOM-BGs have a novel microstructure and ion-releasing profile, the cytotoxicity of 3DOM-BG particles was tested. The cytotoxicity tests were performed using MC3T3-E1 osteoblast-like cells: (1) Wst-1 assay for cell viability after culture in extracts from 3DOM-BG particles; (2) phase contrast microscopy for cell morphology after culture with 3DOM-BG particles; and (3) fluorescence microscopy for imaging cells cultured directly on 3DOM-BG particles. The results showed that 3DOM-BG particles were not cytotoxic, and that cells attached, spread and proliferated on and around 3DOM-BG particles.