In vitro biocompatibility evaluation of poly(3-hydroxybutyrate-co-4-hydroxybutyrate) copolymer in fibroblast cells

P(3HB-co-4HB) as high value polyhydroxyalkanoate: its development over recent decades and current advances

Polyhydroxyalkanoate (PHA) is a biogenic polymer that has the potential to substitute synthetic plastic in numerous applications. This is due to its unique attribute of being a biodegradable and biocompatible thermoplastic, achievable through microbial fermentation from a broad utilizable range of renewable resources. Among all the PHAs discovered, poly(3-hydroxybutyrate-co-4-hydroxybutyrate) [P(3HB-co-4HB)] stands out as a next generation healthcare biomaterial for having high biopharmaceutical and medical value since it is highly compatible to mammalian tissue. This review provides a critical assessment and complete overview of the development and trend of P(3HB-co-4HB) research over the last few decades, highlighting aspects from the microbial strain discovery to metabolic engineering and bioprocess cultivation strategies. The article also outlines the relevance of P(3HB-co-4HB) as a material for high value-added products in numerous healthcare-related applications.

Zein/Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) electrospun blend fiber scaffolds: Preparation, characterization and cytocompatibility

In the present work, a series of Zein/Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blend fiber scaffolds have been prepared by electrospinning method. The electrospun fibers showed a circular and uniform morphology with random distribution. The blend fiber scaffolds possessed well interconnected porous fibrous network structure with high porosity and large aspect surface areas. The FTIR and XPS spectra of Zein/P(3HB-co-4HB) blend fibers demonstrated the same characteristics to that of pure Zein and P(3HB-co-4HB) electrospun fibers. However, Zein might hinder the crystallization of P(3HB-co-4HB) owing to the formation of weak intermolecular interactions, which can affect the preferential orientation of P(3HB-co-4HB) molecules. Only one glass transition temperature (Tg) can be detected for electrospun Zein/P(3HB-co-4HB) blend fiber scaffolds implying the miscibility of Zein and P(3HB-co-4HB) in the blend fibers. The Zein/P(3HB-co-4HB) blend fiber scaffolds showed about 50% of improvement in tensile strength and 400% of increase in elongation at break by increasing P(3HB-co-4HB) content from 20% to 80%. The cytocompatibility of the Zein/P(3HB-co-4HB) blend fiber scaffolds was preliminarily evaluated by cell culture in vitro. The as-prepared electrospun Zein/P(3HB-co-4HB) blend fiber scaffolds with the characteristics of good biocompatibility, excellent pore characteristic as well as sufficient mechanical properties should be more promising for applications as tissue engineering scaffold.

The Oil-Absorbing Property of Polyhydroxyalkanoate Films and its Practical Application: A Refreshing New Outlook for an Old Degrading Material

Polyhydroxyalkanoates (PHAs) have attracted the attention of academia and industry because of their plastic-like properties and biodegradability. However, practical applications as a commodity material have not materialized because of their high production cost and unsatisfactory mechanical properties. PHAs are also believed to have high-value applications as an absorbable biomaterial for tissue engineering and drug-delivery devices because of their biocompatibility. However, research in these areas is still in its very early stages. The main problem faced by proponents of PHAs is the lack of a niche area where PHAs will be the most desired material in terms of its function during use rather than because of its eco-friendly virtues after use. Here, we report on the oil-absorbing property of PHA films and its potential applications. By comparing with some of the existing commercial products, the potential application of PHAs as cosmetic oil-blotting films is revealed for the first time. Besides having the ability to rapidly absorb and retain oil, PHA films also have a natural oil-indicator property, showing obvious changes in opacity following oil absorption. Surface analysis revealed that the surface structures such as porosity and smoothness exert great influence on the rapid oil-absorption properties of the PHA films. These newly discovered properties could be exploited to create a niche area for the practical applications of PHAs.