A versatile strategy for the synthesis and mechanical property manipulation of networked biodegradable polymeric materials composed of well-defined alternating hard and soft domains

Networked materials composed of well-defined alternating domains of two types of biodegradable polymers, hard poly(l-lactide) and soft poly(ε-caprolactone), were successfully synthesized.

Strong, Resilient, and Sustainable Aliphatic Polyester Thermoplastic Elastomers

Thermoplastic elastomers (TPEs) composed of ABA block polymers exhibit a wide variety of properties and are easily processable as they contain physical, rather than chemical, cross-links. Poly(γ-methyl-ε-caprolactone) (PγMCL) is an amorphous polymer with a low entanglement molar mass (M_e = 2.9 kg mol^-1), making it a suitable choice for tough elastomers. Incorporating PγMCL as the midblock with polylactide (PLA) end blocks (f_LA = 0.17) results in TPEs with high stresses and elongations at break (σ_B = 24 ± 2 MPa and ε_B = 1029 ± 20%, respectively) and low levels of hysteresis. The use of isotactic PLA as the end blocks (f_LLA = 0.17) increases the strength and toughness of the material (σ_B = 30 ± 4 MPa, ε_B = 988 ± 30%) due to its semicrystalline nature. This study aims to demonstrate how the outstanding properties in these sustainable materials are a result of the entanglements, glass transition temperature, segment-segment interaction parameter, and crystallinity, resulting in comparable properties to the commercially relevant styrene-based TPEs.