Engineering copolymeric artificial cornea with salt porogen

Genipin-crosslinked polyvinyl alcohol/silk fibroin/nano-hydroxyapatite hydrogel for fabrication of artificial cornea scaffolds-a novel approach to corneal tissue engineering

Design of artificial corneal scaffolds substitute is crucial for replacement of impaired cornea. In this paper, porous polyvinyl alcohol/silk fibroin/nano-hydroxyapatite (PVA/SF/n-HA) composite hydrogel was prepared via the genipin (GP) cross-linking, the pore diameter of the hydrogel ranged from 8.138 nm and 90.269 nm, and the physical and physiological function of hydrogel were investigated. The resulting hydrogel exhibited favourable physical properties. With the GP content increasing, the structural regularity of PVA/SF/n-HA composite hydrogel was enhanced and the thermal stability was improved. The moisture content was slightly decreased and generally maintained at approximately 70%. The tensile strength was heightened up to 0.64 MPa, while the breaking elongation was decreased slightly. Moreover, the biofunction was investigated. The in vitro degradation test demonstrated that with the addition of GP, the stability of the composite hydrogels in protease XIV solution was promoted and the three-dimensional porosity structure of composite hydrogels was maintained as ever. And the human corneal fibroblasts (HCFs) were employed to examine the cells cytotoxicity of the PVA/SF/n-HA composite hydrogels with different GP content by CCK-8 assay. Based on confocal laser scanning microscope (CLSM) and scanning electron microscope (SEM), HCFs had individually commendable adhesion and proliferation on PVA/n-HA/SF composite hydrogel. HCFs proliferated and grew into the pores of composite hydrogel. The results of biocompatibility experiments of composite hydrogel suggested that it was no acute toxicity, in vitro cytotoxicity was 0 or 1 grade. Overall, results from this paper, PVA/n-HA/SF composite hydrogel was a qualified medical material which conformed to the national standard, could be a promising alternative for artificial cornea scaffold material-a novel approach to corneal tissue engineering.

New strategy for design and fabrication of polymer hydrogel with tunable porosity as artificial corneal skirt

In order to obtain an ideal material using for artificial corneal skirt, a porous polymer hydrogel containing 2-hydroxyethyl methacrylate (HEMA), trimethylolpropane triacrylate (TMPTA) and butyl acrylate was prepared through one-step radical polymerization method and the usage of CaCO₃ whisker as porogen. The physical-chemical properties of the fabricated polymer hydrogel can be adjusted by CaCO₃ whisker content, such as pore size, porosity, water content of materials and surface topography. Then a series of cell biology experiments of human corneal fibroblasts (HCFs) were carried out to evaluate its properties as an artificial corneal skirt, such as the adhesion of cells on the materials with different pore size and porosity, the apoptosis on materials with different characteristics, the distribution of the cells on the material surface. The results revealed that high porosity not only could improve water content of hydrogel, but also strengthen the adhesion of HCFs on hydrogel. In addition, high porosity hydrogel with the whisker shape of pores showed much elongate spindle-like morphology than those low porosity hydrogels. MTT assay certified that the resulted polymer hydrogel material possessed excellent biocompatibility and was suitable for HCFs growing, making it promising for being developed as artificial corneal skirt.