Self-setting properties andin vitrobioactivity of Ca2SiO4/CaSO4·1/2H2O composite bone cement

Enhancing bioactivity and mechanical performances of hydroxyapatite-calcium sulfate bone cements for bone repair: in vivo histological evaluation in rabbit femurs

This study deals with synthesizing hydroxyapatite-calcium sulfate bone cements or HAP-xCaS for bone repair. The effect of CaS on the setting time, injectability, washout resistance, phase evolution, water absorption, and physical, microstructural, and mechanical properties, as well as in vitro apatite-forming ability test and pH behavior of the HAP were investigated. Implantation of bone cement in rabbit femur and in vivo histological analysis were also analyzed. Initial and final setting times decrease with increasing CaS, which would be helpful for clinical procedures. All compositions have mixed phases of HAP, CaS, brushite, and gypsum. The prepared bone cement exhibited a dense structure and increased linear shrinkage with increasing CaS content. Adding more CaS inhibited grain growth and improved the mechanical properties, including compressive strength (σ c), bending strength (σ f), and Young's modulus (E). SEM micrographs displayed that the x = 0.7 or HAP-0.7CaS bone cement produced the highest ability to induce in vitro apatite formation, indicating its biocompatibility. In vivo histological analysis for the HAP-0.7CaS bone cement demonstrated that more new bone formed around defects and bone cement particles. Osteoblasts were found peripherally at the bone trabeculae, and occasional osteoblast-like cells were observed at the granules after 4-8 weeks of implantation. The obtained results indicated that the HAP-0.7CaS bone cement has the potential to exhibit good bioactivity, injectability, and good mechanical properties for bone repair applications.

The Ability of Biodegradable Thermosensitive Hydrogel Composite Calcium-Silicon-Based Bioactive Bone Cement in Promoting Osteogenesis and Repairing Rabbit Distal Femoral Defects

Osteoporotic vertebral compression fractures are a global issue affecting the elderly population. To explore a new calcium silicate bone cement, polylactic acid (PLGA)–polyethylene glycol (PEG)–PLGA hydrogel was compounded with tricalcium silicate (C₃S)/dicalcium silicate (C₂S)/plaster of Paris (POP) to observe the hydration products and test physical and chemical properties. The cell compatibility and osteogenic capability were tested in vitro. The rabbit femoral condylar bone defect model was used to test its safety and effectiveness in vivo. The addition of hydrogel did not result in the formation of a new hydration product and significantly improved the injectability, anti-washout properties, and in vitro degradability of the bone cement. The cholecystokinin octapeptide-8 method showed significant proliferation of osteoblasts in bone cement. The Alizarin red staining and alkaline phosphatase activity test showed that the bone cement had a superior osteogenic property in vitro. The computed tomography scan and gross anatomy at 12 weeks after surgery in the rabbit revealed that PLGA-PEG-PLGA/C3S/C2S/POP was mostly degraded, with the formation of new bone trabeculae and calli at the external orifice of the defect. Thus, PLGA-PEG-PLGA/C₃S/C₂S/POP composite bone cement has a positive effect on bone repair and provides a new strategy for the clinical application of bone tissue engineering materials.

Ball Milling Medium May Tune the Self-Curing Property and Root Canal Microleakage of β-Dicalcium Silicate-Based Cement

It is still a challenge to overcome the extended setting process of pure Ca-silicate as root canal fillers. We investigated the effects of attapulgite (a basic hydrous silicate of magnesium and aluminum) and ball-milling liquid medium on the self-curing properties of conventional β-dicalcium silicate (C2Si)-based cements. It was shown that a minor amount of attapulgite nanofibers (1–4%) had only a slight influence on setting time but caused a large increase in compressive resistance and structural stability. In particular, the ball milling media with different acetone/water ratios (3:0, 2:1, 1:2, 0:3) could directly influence the particle size distribution of C2Si powders, and the co-existence of liquid media (2:1 or 1:2) may be beneficial for shortening the setting time, enhancing early-stage compressive strength, and significantly improving the anti-microleakage ability of cement. Moreover, the composite cements also exhibited appreciable antibacterial efficacy in vitro. These findings demonstrated that the physicochemical properties of the Ca-silicate powders could be tuned by adding a minor amount of inorganic silicate nanofibers and a simple ball milling condition, and such a facile strategy is favorable for developing novel (pre-mixed) Ca silicate-based cements as root canal sealers.

Assessment of calcium sulfate hemihydrate-Tricalcium silicate composite for bone healing in a rabbit femoral condyle model

Calcium sulfate or plaster of Paris (POP) is considered as a bone cement with a fast degradation rate, which frequently makes it resorb before the bone defect area is completely filled by new bone. The incorporation of tricalcium silicate (C3S) into POP cement has been proven as a feasible approach to reduce the in vitro degradation rate and improve the in vitro bioactivity of the material. However, the in vivo performance of the POP/C3S composite cement is still unclear. Therefore, the aim of the present study is to assess the biodegradability and osteogenesis of POP/C3S composite cement in comparison with those of POP bone cement. To carry out the in vivo evaluation, POP and POP/C3S cements were implanted into a femoral condyle defect model in rabbits (5 mm diameter × 10 mm length) for 4, 8, and 12 weeks duration. The area of the remaining cement and new bone regeneration in bone defect were investigated and quantitatively measured using radiography, micro-computed tomography, and histological staining. For both cements, no sign of inflammation was observed. POP cement was completely degraded at the 8th week of post-implantation. By contrast, only approximately 50% by volume of POP/C3S composite cement degraded at the 12th week, which allowed a long-term framework for new bone formation. The osteogenic ability of POP/C3S composite cement was significantly superior to that of POP as indicated by the higher mineralization rate and maturity of the newly formed bone around the composite cement. In summary, our findings demonstrated that the in vivo degradation behaviors and osteogenic ability of POP cement could be improved by incorporating C3S in vivo, suggesting that POP/C3S composite cement has potential as a biodegradable cement for bone repair.

Systematic investigation of β-dicalcium silicate-based bone cements in vitro and in vivo in comparison with clinically applied calcium phosphate cement and Bio-Oss®

Herein we systematically investigated the biological performance of a β-dicalcium silicate (β-C₂S)-based bone cement in comparison with the clinically used calcium phosphate cement (CPC) and Bio-Oss®.

Apical Sealing Ability of a Novel Material: Analysis by Fluid Filtration Technique

AIM

The aim of this study is to evaluate the sealing ability of Biodentine(TM), which is new calcium-silicate based dental cement and has endodontic indications similar to those of MTA.

METHODS

The study sample consists of 21extracted human mandibular anterior teeth. The teeth were submitted to root-end preparation and instrumented up to file #40 by step back technique and randomly divided into 3 study groups (n=7): White MTA Angelus(TM) (Angelus, Angelus Odontológica, Londrina, PR, Brazil), Biodentine(TM) (Septodont, SeptodontSpecialités, Saint-MaurdesFosses, France) and the controls. The length of dye penetration between the filling material and tooth structure was measured in millimetres, using a calibrated stereo microscope (Leica MZ75, Germany) at 20× magnification under the same conditions. One-way Analysis of Variance (ANOVA) was used to indicate differences between the experimental groups and the controls. In addition, Tukey Multiple Comparisons Test was used to indicate differences within each group.

RESULTS

The results showed that none of the groups were completely sealed. The mean and standard deviation for dye penetration in Biodentine(TM) group was 0.63±0.20 and in MTA Angelus(TM) group, it was 0.26±0.25. Regarding the comparisons between each group, significant differences were not observed (P=0.0193). The comparison between materials only found a significant difference only between MTA Angelus(TM) and Biodentine(TM) (P<0.05).

CONCLUSIONS

This study evaluated the possibility of Biodentine(TM)'s sealing ability and marginal adaptation, since no studies are available on Biodentine. However, further in vitro and in vivo investigations should be conducted to determine the suitability of Biodentine(TM) for clinical application.

Rational design and fabrication of a β-dicalcium silicate-based multifunctional cement with potential for root canal filling treatment

Gypsum-introduced, CaO-rich dicalcium silicate-based cements exhibit multifunctional physicochemical and biological properties and meet some challenging criteria in root canal therapy.

β-Dicalcium silicate-based cement: synthesis, characterization and in vitro bioactivity and biocompatibility studies

β-dicalcium silicate (β-Ca₂ SiO₄, β-C₂ S) is one of the main constituents in Portland cement clinker and many refractory materials, itself is a hydraulic cement that reacts with water or aqueous solution at room/body temperature to form a hydrated phase (C-S-H), which provides mechanical strength to the end product. In the present investigation, β-C₂ S was synthesized by sol-gel process and it was used as powder to cement preparation, named CSiC. In vitro bioactivity and biocompatibility studies were assessed by soaking the cement samples in simulated body fluid solutions and human osteoblast cell cultures for various time periods, respectively. The results showed that the sol-gel process is an available synthesis method in order to obtain a pure powder of β-C₂ S at relatively low temperatures without chemical stabilizers. A bone-like apatite layer covered the material surface after soaking in SBF and its compressive strength (CSiC cement) was comparable with that of the human trabecular bone. The extracts of this cement were not cytotoxic and the cell growth and relative cell viability were comparable to negative control.

Effect of tricalcium silicate (Ca(3)SiO(5)) bioactive material on reducing enamel demineralization: an in vitro pH-cycling study

OBJECTIVES

The aim of this study was to investigate the effect of Ca(3)SiO(5) on reducing enamel demineralization under pH-cycling conditions.

METHODS

Forty bovine enamel samples were treated under four conditions: group 1, double distilled water (negative control); group 2, 1000 ppm F (as NaF, positive control); group 3, Ca(3)SiO(5) slurry; and group 4, Ca(3)SiO(5)-F slurry (Ca(3)SiO(5) with 1000 ppm F aq.). All the specimens were treated with treatment materials 4 times each day. Samples in groups 1 and 2 were soaked in test solutions for 2 min and samples in groups 3 and 4 were painted in treatment slurry for 2 min. At times between treatments, they were immersed in citric acid solution 3 times a day and 15 s each time. All the procedures were repeated for 7 days. Knoop microhardness, scanning electron microscopy (SEM), X-ray diffraction (XRD) and atom force microscopy (AFM) were used to examine samples.

RESULTS

After treatment for 7 days, enamels in all the groups were significantly softened. The extents of microhardness reduction were 52.3%, 28.5%, 28.5% and 20.2% for groups 1, 2, 3 and 4, respectively. Samples in the negative control group showed a typical acid etched pattern while enamels in other groups were relatively compact. There was no significant difference between samples treated with Ca(3)SiO(5) and F. The combination of Ca(3)SiO(5) with F showed the best effect on reducing enamel demineralization.

CONCLUSIONS

Ca(3)SiO(5) is an effective material against enamel demineralization alone but in combination with F a better anti-demineralization effect may be obtained.

Quantitative evaluation by glucose diffusion of microleakage in aged calcium silicate-based open-sandwich restorations

This study compared the in vitro marginal integrity of open-sandwich restorations based on aged calcium silicate cement versus resin-modified glass ionomer cement. Class II cavities were prepared on 30 extracted human third molars. These teeth were randomly assigned to two groups (n = 10) to compare a new hydraulic calcium silicate cement designed for restorative dentistry (Biodentine, Septodont, Saint Maur des Fossés, France) with a resin-modified glass ionomer cement (Ionolux, Voco, Cuxhaven, Germany) in open-sandwich restorations covered with a light-cured composite. Positive (n = 5) and negative (n = 5) controls were included. The teeth simultaneously underwent thermocycling and mechanocycling using a fatigue cycling machine (1,440 cycles, 5-55°C; 86,400 cycles, 50 N/cm(2)). The specimens were then stored in phosphate-buffered saline to simulate aging. After 1 year, the teeth were submitted to glucose diffusion, and the resulting data were analyzed with a nonparametric Mann-Whitney test. The Biodentine group and the Ionolux group presented glucose concentrations of 0.074 ± 0.035 g/L and 0.080 ± 0.032 g/L, respectively. No statistically significant differences were detected between the two groups. Therefore, the calcium silicate-based material performs as well as the resin-modified glass ionomer cement in open-sandwich restorations.