Evaluation of the effect of four self-etching adhesives on dentin permeability

Impact of Immediate Dentin Sealing Using Universal Adhesive under Simulated Pulp Pressure on Microtensile Bond Strength of Indirect Resin Composite Restorations and Dentin Permeability

Objective  The aim of this study was to investigate the effect of immediate dentin sealing (IDS) technique using universal adhesive under simulated pulp pressure on microtensile bond strength (μTBS) of indirect resin composite restorations and dentin permeability.

Materials and Methods  Fifty extracted caries-free human third molars were used for specimens' preparation. Each molar's occlusal table was abraded flat and their roots were separated under continuous water cooling. Forty specimens were used for microtensile bond strength test (μTBST) evaluation. The μTBST specimens were randomly assigned to two groups according to the dentin sealing time; Immediate dentin sealing (IDS) and delayed dentin sealing (DDS). Each group was further subdivided into two subgroups according to the adhesive system used for dentin sealing: iBOND self-etch adhesive and GLUMA Bond Universal. All specimens were exposed to simulated pulp pressure for 1 week then restored using computer-aided design/computer-aided manufacturing (CAD/CAM) resin composite blocks. The μTBS was evaluated for all tested subgroups after 24 hours and 6 months of water storage. The remaining 10 teeth were used for the preparation of dentin discs for dentin permeability evaluation. They were divided into two groups according to type of self-etch adhesive used. Fluid filtration rate was evaluated after etching, with smear layer and after adhesive application. Results obtained were statistically analyzed using Shapiro–Wilk test and Weibull analysis.

Results  Statistically significant difference was recorded between µTBS mean values of both IDS and DDS techniques at 24 hours and after 6 months of water storage. GLUMA Bond Universal adhesive had significantly higher bond strength compared with iBond at both IDS and DDS techniques, but both adhesives showed a significant reduction in the Weibull characteristic strength after 6 months of water storage. Significant reduction in dentin permeability was recorded by both adhesives without any significant difference between them.

Conclusions  The IDS technique using universal adhesive in self-etch mode is an effective strategy for improving the final bond strength of CAD/CAM resin composite restorations and reducing dentin permeability.

Effects of Poly(Amidoamine) Dendrimer-Coated Mesoporous Bioactive Glass Nanoparticles on Dentin Remineralization

Dentin hypersensitivity (DH) is one of the most common clinical conditions usually associated with exposed dentinal surfaces. In this study, we identified the effectiveness of poly(amidoamine) (PAMAM) dendrimer-coated mesoporous bioactive glass nanoparticles (MBN) (PAMAM@MBN) on DH treatment, examining the ion-releasing effect, dentin remineralization, and the occluding effect of dentinal tubules. We synthesized MBN and PAMAM@MBN. After soaking each sample in simulated body fluid (SBF), we observed ion-releasing effects and dentin remineralization effects for 30 days. Also, we prepared 30 premolars to find the ratio of occluded dentinal tubules after applying MBN and PAMAM@MBN, respectively. The results showed that PAMAM did not disrupt the calcium ion-releasing ability or the dentin remineralization of MBN. The PAMAM@MBN showed a better occluding effect for dentinal tubules than that of MBN (p < 0.05). In terms of dentinal tubule occlusion, the gap between MBN was well occluded due to PAMAM. This implies that PAMAM@MBN could be effectively used in dentinal tubule sealing and remineralization.

Evaluation of Five Different Desensitizers: A Comparative Dentin Permeability and SEM Investigation In Vitro

BACKGROUND/OBJECTIVE

The purpose of this study was to evaluate the efficacy and durability of five different dentin desensitizers (Gluma Desensitizer Powergel, Bifluorid 12, Gluma Self Etch Bond, D/Sense Crystal, Nupro Sensodyne Prophylaxis Paste with Novamin) on tubule occlusion and dentin permeability reduction in vitro.

METHOD

The quantitative changes in permeability of 100 dentin discs were measured after desensitizer treatments and following post-treatments of 6% citric acid challenge for 1 min or immersion in artificial saliva for 24 hours under hydrostatic pressure generated by a computerised fluid filtration meter. Qualitative SEM analyses were also carried out.

RESULTS

Dentin permeability decreased after desensitizer application in all groups. Nevertheless, only the difference between 'Gluma Self Etch Bond' and 'Nupro Sensodyne Prophylaxis Paste with Novamin' groups was significantly different (p<0.05). Dentin permeability increased significantly after post-treatments (p<0.05). There was no statistically difference among the citric acid-subgroups (p>0.05). Of all the artificial saliva-subgroups, only the difference between 'D/Sense Crystal' and 'Bifluorid 12' was significantly different (p<0.05). In SEM analysis, morphological changes were detected on the dentin surface and within the tubules following desensitizer treatments and post-treatments.

CONCLUSION

All the desensitizers significantly reduced dentin permeability by changing the morphology of the dentin surface and/or dentinal tubules. Following post-treatments, there was some reduction in the efficacy of the desensitizers which was represented by the reduction in permeability values. SEM analysis revealed some physical changes in the dentin structure which can partly give an explanation to the reduced efficacy of tested desensitizers.

Marginal sealing durability of two contemporary self-etch adhesives

Introduction. Sealing abilities of two self-etch adhesives were evaluated after two aging processes: storage in water and thermocycling. Materials and Methods. Cl V cavities were prepared on the buccal and lingual aspects of 48 human premolars, with cervical margins 1 mm below the CEJ. Clearfil Protect Bond (CPB) and BeautiBond (BB) (two-step and one-step self-etch adhesives, resp.) were applied, each to half of the cavities and restored with composite resin. Each group was randomly subdivided into 4 subgroups (n = 12) and evaluated for dye penetration after 24 hours, after 3000 thermocycling rounds, after a 6-month water storage, and after 3000 thermocycling rounds plus 6-month water storage, respectively. Data was analyzed using SPSS 11.5 and Kruskal-Wallis and Mann-Whitney U tests (α = 0.05). Results. There were no significant differences in enamel and dentin microleakage between the adhesives (P = 0.683; P = 0.154). Furthermore, no significant differences were observed in enamel microleakage of each one of CPB and BB (P = 0.061 and P = 0.318, resp.). However, significant decrease was observed in subgroups 3 and 4 (P = 0.001) for CPB dentinal margins. Conclusion. In this study, limited aging procedures had no influence on marginal integrity of composite resin restorations bonded with self-etch adhesives of CPB and BB. Furthermore, CPB dentinal sealing improved after aging.

Effect of a new desensitizing material on human dentin permeability

OBJECTIVES

Resin-modified glass ionomers (RMGI) have demonstrated clinical success providing immediate and long-term relief from root sensitivity. RMGIs have been recently introduced as paste-liquid systems for convenience of clinical usage. The objective of this study was to measure the ability of a new paste-liquid RMGI to reduce fluid flow through human dentin, compared to an established single-bottle nanofilled total etch resin adhesive indicated for root desensitization.

METHODS

Dentin permeability was measured on human crown sections on etched dentin, presenting a model for the exposed tubules typical of root sensitivity, and permitting measurement of the maximum permeability. In the first two groups, the etched dentin was coated with either the RMGI or adhesive, and permeability measured on the coated dentin. In a third group, a smear layer was created on the dentin with sandpaper, then the specimens were coated with the RMGI; permeability was measured on the smeared and coated dentin. Specimens from each group were sectioned and examined via scanning electron microscopy (SEM).

RESULTS

Both the resin adhesive and the new paste-liquid RMGI protective material significantly reduced fluid flow through dentin, and exhibited excellent seal on dentin with either open tubules or smear-layer occluded tubules. The RMGI infiltrated the smear layer with resin during placement, penetrated dentin tubules, and formed resin tags.

SIGNIFICANCE

The RMGI was equivalent to the adhesive in its ability to reduce fluid flow and seal dentin. It is therefore concluded that the new RMGI and the adhesive show the potential to offer excellent sensitivity relief on exposed root dentin.

Effect of a new liner/base on human dentin permeability

OBJECTIVES

Resin-modified glass ionomers (RMGI) have demonstrated clinical success in their ability to minimize post-operative sensitivity of restorations. RMGIs have been recently introduced as paste-liquid systems for convenience of clinical usage. The objective of this study was to measure the ability of a new paste-liquid RMGI liner/base to reduce fluid flow through human dentin.

METHODS

Dentin permeability was measured on human crown sections on etched dentin, using etched dentin as a model for the exposed tubules typical of root sensitivity, and permitting measurement of the maximum permeability. In the one group, the etched dentin was coated with the RMGI, and pre- and post-treatment permeability was measured on the coated dentin. In the second group, a smear layer was created on the dentin with sandpaper, then the samples were coated with the RMGI; permeability was measured on the smeared and coated dentin. Samples from each group were sectioned and examined via scanning electron microscopy (SEM).

RESULTS

The new paste-liquid RMGI liner/base significantly reduced fluid flow through dentin, and exhibited excellent seal on dentin with either a smear layer or open tubules. SEM images show evidence that the RMGI infiltrated the smear layer with resin during placement, penetrated dentin tubules, and formed resin tags in acid-etched dentin.

CONCLUSIONS

Based on these results, combined with previous research on adhesion and microleakage, it is concluded that the new RMGI liner/base should minimize post-operative sensitivity in restorations.