Microbiological or chemical models of enamel secondary caries compared by polarized-light microscopy and energy dispersive X-ray spectroscopy

Recurrent caries models to assess dental restorations: A scoping review

OBJECTIVES

To review the literature on recurrent caries models used to evaluate restorative materials, compare reported methodology and parameters, and devise specific recommendations to be considered in future investigations.

DATA

The following were extracted: study design, sample characteristics, source of teeth, name of restorations compared including controls, recurrent caries model type, type of demineralizing and remineralizing solutions, type of biofilm used, methods to detect recurrent caries.

SOURCES

Literature searches were performed in OVID Medline, EMBASE, SCOPUS, and Cochrane Library.

STUDY SELECTION

For a study to be included, it had to examine dental materials for tooth restoration purposes only with a valid control group and evaluate restorative dental materials regardless of the form of the teeth caries model used or nature of the tooth structure used. A total of 91 studies were included. Most of the studies presented were in vitro. Human teeth were the main source of specimens utilized. Around 88% of the studies used specimens without an artificial gap, and 44% used a chemical model. S. mutans was the main bacterial species used in microbial caries models.

CONCLUSION

The findings of this review provided an insight into the performance of available dental materials assessed using different recurrent caries models, yet this review cannot be used as a guideline for material selection. Selecting the appropriate restorative material relies on several patient-related factors such as microbiota, occlusion, and diet that are not comprehensively taken into consideration in recurrent caries models and thus hinder reliable comparison.

CLINICAL SIGNIFICANCE

Due to the heterogenicity of variables among studies on the performance of dental restorative materials, this scoping review aimed to provide insights for dental researchers concerning the available recurrent caries models, testing methods used, and aspects of comparison between these materials including their characteristics and limitations.

Glass ionomer cement inhibits secondary caries in an in vitro biofilm model

OBJECTIVES

The objective of this study was to investigate the effect of different glass ionomer cements on secondary caries inhibition in a fully automated in vitro biofilm model.

MATERIALS AND METHODS

One hundred and twenty-four extracted third molars received class V cavities and were filled with one conventional (Ketac Molar/KM), and two resin-modified glass ionomer cements (Photac Fil/PF, Ketac N100/KN, 3M Espe). A bonded resin composite (Single Bond Plus/Filtek Supreme XTE) served as control. After 14 days water storage at 37 °C, specimens were thermocycled (10,000 × 5/55 °C). Over a period of 10 days, specimens were subjected to cariogenic challenge for 3/4/6 h/day. Demineralization was caused by Streptococcus mutans (DSM 20523) alternatingly being rinsed over specimens using artificial saliva. After biological loading, teeth were cut longitudinally and demineralization depths were evaluated at the margins and at a distance of 0.5 mm from the margins using fluorescence microscopy. Marginal quality was investigated under a SEM at ×200 magnification.

RESULTS

Four-hour demineralization depths were for enamel margins (EM), enamel (E), dentin margin (DM), and dentin (D) (μm ± SD): KM: EM 12 ± 8, E 33 ± 7, DM 56 ± 11, D 79 ± 6; PF: EM 19 ± 13, E 34 ± 13, DM 53 ± 10, D 77 ± 12; and KN: EM 26 ± 5, E 38 ± 6, DM 57 ± 11, D 71 ± 7. For all glass ionomer cements (GICs), demineralization depth at the margins was less compared to 0.5 mm distance, with demineralization depth having been correlated to duration of cariogenic challenge (ANOVA [mod. LSD, p < 0.05]). Compared to the bonded resin composite, all GICs exhibited caries inhibition at restoration margins in enamel and dentin.

CONCLUSIONS

Fluoride-releasing GIC materials exhibit a secondary caries inhibiting effect in vitro.

CLINICAL RELEVANCE

Glass ionomer cements have a higher secondary caries inhibiting effect than resin composites.

Effect of microparticulate silver addition in dental adhesives on secondary caries in vitro

OBJECTIVES

The aim of the present study was evaluate the effect of microparticulate silver additions in adhesives on secondary caries formation using an artificial mouth model.

MATERIALS AND METHODS

One hundred eight intact human third molars received standardized Class-V resin composite restorations (Filtek Supreme XTE bonded with Syntac, Scotchbond 1 XT, Futurabond M). Adhesives were charged with different amounts of microparticulate silver (0 %/0.1 %/0.5 %). After storage for 4 weeks at 37 °C, teeth were subjected to 10,000 thermocycles (+5 °C and +55 °C), and impressions were taken. Streptococcus mutans 10449 was used in a nutrition medium for secondary caries simulation in a fully automated artificial mouth. After completion of thermocycling and biological load cycling, impressions were taken and replicas were investigated under a light microscope for gap widths at enamel and dentin margins. Evaluation of fluorescence was carried out using a special FITC filter. The demineralization depths at the cavity margin were evaluated using Xpert for Windows working at a pixel distance of 5 μm.

RESULTS

After thermocycling, no difference in gap widths and demineralization depths was found (p > 0.05). After incubation, gap widths and demineralization depths were significantly reduced with higher amounts of silver loading in most of the adhesives (p < 0.05). The 0.5 % silver addition resulted in a slight decrease of secondary caries at resin-dentin margins (p < 0.05).

CONCLUSIONS

Addition of microparticulate silver in commercially available dental adhesives has the potential of reducing secondary caries.

CLINICAL RELEVANCE

The chosen setup was able to produce secondary caries with a distinct in vivo appearance. Microparticulate silver additions in dental adhesives may have an impact on inhibition of secondary caries.

Efeito da aplicação tópica de um verniz de TiF4 quimicamente estável na desmineralização do esmalte dentário bovino: estudo in vitro

OBJETIVO: Avaliar, in vitro, o efeito preventivo da aplicação tópica de um verniz à base de tetrafluoreto de titânio quimicamente estável e de um verniz à base de fluoreto de sódio sobre o esmalte bovino, mediante ciclagem de pH. METODOLOGIA: A amostra foi constituída por 75 blocos de esmalte bovino 3×3 mm, sendo 15 aleatoriamente alocados em cada um dos cinco grupos: G1: Dentifrício Fluoretado + Verniz sem princípio ativo; G2: Dentifrício Fluoretado + Verniz à base de TiF4 (4 minutos); G3: Dentifrício Fluoretado + Verniz à base de TiF4 (24 horas); G4: Dentifrício Fluoretado + Verniz à base de NaF (24 horas); G5: Dentifrício Fluoretado. A ciclagem de pH foi realizada por um período de 14 dias, constando de oito ciclos, a 37 °C. Os blocos tratados foram mantidos em solução desmineralizante por oito horas e, por 16 horas, em solução remineralizante, sendo submetidos à análise da superfície em microscopia eletrônica de varredura e espectroscopia de energia dispersiva. RESULTADO: O verniz à base de TiF4 promoveu uma maior proteção ao esmalte quando comparado com os demais grupos. Mesmo após o período de ciclagem, foram encontrados fósforo, cálcio, sódio, magnésio, titânio, cloro, silício, alumínio, enxofre, potássio, oxigênio e flúor na superfície do esmalte. CONCLUSÃO: O aspecto da estrutura adamantina submetida à ação do tetrafluoreto de titânio revelou a presença de uma película protetora. O cálcio e o fósforo foram os principais compostos inorgânicos encontrados no esmalte, sendo observadas alterações na constituição química da camada superficial adamantina em função do tratamento com fluoreto instituído.

Degree of conversion and hardness of two different systems of the Vitrebond™ glass ionomer cement light cured with blue LED

This study investigated the physicochemical properties of the new formulation of the glass ionomer cements through hardness test and degree of conversion by infrared spectroscopy (FTIR). Forty specimens (n = 40) were made in a metallic mold (4 mm diameter x 2 mm thickness) with two resin-modified glass ionomer cements, Vitrebond™ and Vitrebond™ Plus (3M/ ESPE). Each specimen was light cured with blue LED with power density of 500 mW/cm(2) during 30 s. Immediately after light curing, 24h, 48h and 7 days the hardness and degree of conversion was determined. The Vickers hardness was performed by the MMT-3 microhardness tester using load of 50 gm force for 30 seconds. For degree of conversion, the specimens were pulverized, pressed with KBr and analyzed with FT-IR (Nexus 470). The statistical analysis of the data by ANOVA showed that the Vitrebond™ and Vitrebond™ Plus were no difference significant between the same storage times (p > 0.05). For degree of conversion, the Vitrebond™ and Vitrebond™ Plus were statistically different in all storage times after light curing. The Vitrebond™ showed higher values than Vitrebond™ Plus (p < 0.05). The performance of Vitrebond™ had greater results for degree of conversion than Vitrebond™ Plus. The correlation between hardness and degree of conversion was no evidence in this study.

Chemical and crystallographic study of remineralized surface on initial carious enamel treated with Galla chinensis

To investigate the morphologic, chemical and crystallographic characters of remineralized surface on initial carious enamel treated with Galla chinensis, scanning electron microscopy equipped with energy dispersive analysis spectroscopy were used, and X-ray microdiffraction (microzone XRD) was used for the first time to analyze in situ the microzone crystallite of remineralized surface on carious enamel. Bovine sound enamel slabs were demineralized to produce initial carious lesion in vitro. Then, the lesions were exposed to a pH-cycling regime for 12 days of remineralization. Each daily cycle included 4x1 min applications with one of the three treatments: distilled and deionized water (DDW); 1 g/L NaF; 4 g/L G. chinensis extract (GCE). After the treatments, some rod-like deposits and many irregular prominences were found on GCE-treated enamel surface, and the intensities of Ca and P signals showed a tendency to increase; Ca:P ratio was significantly higher than that of DDW-treated enamel. X-ray microdiffraction showed hydroxyapatite was still the main component of GCE-treated enamel, and the crystallinity was increased, the crystal lattice changed gently with decreased lattice parameter a. These results indicated the potential of GCE in promoting the remineralization of initial enamel carious lesions, and supported the previous hypothesis about GCE mechanism. Combined with the anti-bacteria and demineralization inhibition properties of GCE, the natural G. chinensis may become one more promising agent for caries prevention.