HPLC analysis of HEMA released from two different adhesive systems

Incomplete Polymerization of Dual-Cured Resin Cement Due to Attenuated Light through Zirconia Induces Inflammatory Responses

Zirconia restorations are becoming increasingly common. However, zirconia reduces the polymerization of dual-cured resin cement owing to light attenuation, resulting in residual resin monomers. This study investigated the effects of dual-cured resin cement, with incomplete polymerization owing to attenuated light through zirconia, on the inflammatory response in vitro. The dual-cured resin cement (SA Luting Multi, Kuraray) was light-irradiated through zirconia with three thickness diameters (1.0, 1.5, and 2.0 mm). The light transmittance and the degree of conversion (DC) of the resin cement significantly decreased with increasing zirconia thickness. The dual-cured resin cement in 1.5 mm and 2.0 mm zirconia and no-irradiation groups showed significantly higher amounts of hydroxyethylmethacrylate and triethyleneglycol dimethacrylate elution and upregulated gene expression of proinflammatory cytokines IL-1β and IL-6 from human gingival fibroblasts (hGFs) and TNFα from human monocytic cells, compared with that of the 0 mm group. Dual-cured resin cement with lower DC enhanced intracellular reactive oxygen species (ROS) levels and activated mitogen-activated protein (MAP) kinases in hGFs and monocytic cells. This study suggests that dual-cured resin cement with incomplete polymerization induces inflammatory responses in hGFs and monocytic cells by intracellular ROS generation and MAP kinase activation.

Polymeric Tissue Adhesives

Polymeric tissue adhesives provide versatile materials for wound management and are widely used in a variety of medical settings ranging from minor to life-threatening tissue injuries. Compared to the traditional methods of wound closure (i.e., suturing and stapling), they are relatively easy to use, enable rapid application, and introduce minimal tissue damage. Furthermore, they can act as hemostats to control bleeding and provide a tissue-healing environment at the wound site. Despite their numerous current applications, tissue adhesives still face several limitations and unresolved challenges (e.g., weak adhesion strength and poor mechanical properties) that limit their use, leaving ample room for future improvements. Successful development of next-generation adhesives will likely require a holistic understanding of the chemical and physical properties of the tissue-adhesive interface, fundamental mechanisms of tissue adhesion, and requirements for specific clinical applications. In this review, we discuss a set of rational guidelines for design of adhesives, recent progress in the field along with examples of commercially available adhesives and those under development, tissue-specific considerations, and finally potential functions for future adhesives. Advances in tissue adhesives will open new avenues for wound care and potentially provide potent therapeutics for various medical applications.

In Vitro Cytotoxicity of Self-Adhesive Dual-Cured Resin Cement Polymerized Beneath Three Different Cusp Inclinations of Zirconia

The aim of the present study was to evaluate the in vitro cytotoxicity of self-adhesive dual-cured resin cement (SADRC) polymerized beneath three different cusp inclinations of zirconia with different light curing time. A commercial SADRC (Multilink Speed) was polymerized beneath zirconia (ZrO₂) with three different cusp inclinations (0°, 20°, and 30°) for 20 s or 40 s. After being stored in light-proof box for 24 h, the ZrO₂-SADRC specimens were immersed in DMEM for 72 h and then we got the extract solution, cultured the human gingival fibroblasts (HGF, 8 × 10³ per well) with 100% or 50% concentrations of the extract solution for 24 h, 72 h, and 120 h, respectively, and evaluated cytotoxicity of the polymerized SADRC with CCK-8 assay in optical density (OD) values, relative growth rates (RGR), and cytotoxicity grades. Statistical analysis was conducted using a two-way ANOVA followed by post hoc Student–Newman–Keuls test. The OD values varied from 0.8930 to 3.2920, the RGR varied from 33.93% to 98.68%, and the cytotoxicity grades varied from 0 to 2. There was significant difference in the OD values among the different cusp inclinations of zirconia (P < 0.001), and there was significant difference in the OD values between the different light curing times in some situations (P < 0.05). The cusp inclination of zirconia affects the in vitro cytotoxicity of SADRC. Prolonging the light curing time from 20 s to 40 s can reduce the in vitro cytotoxicity of SADRC when the cusp inclination of zirconia is smaller than 20°.

The effect of the polymerization initiator and light source on the elution of residual Bis-GMA and TEGDMA monomers: A study using liquid chromatography with UV detection

A method for the extraction and quantification of two residual monomers, bisphenol glycidyl dimethacrylate (Bis-GMA) and triethylene glycol dimethacrylate (TEGDMA), that were evaluated using high efficiency liquid chromatography with UV detection was developed and validated in this study. Three types of solvents were applied in the extraction of the monomers (methanol, ethanol and acetonitrile), where the highest extraction efficiency was obtained using acetonitrile. The different resins were prepared by photoactivation of Bis-GMA and TEGDMA monomers. Additionally, the effects of the addition of two photoinitiators (camphorquinone (CQ) and phenyl propanodione (PPD) and that of a co-initiator (N,N-dimethyl-p-toluidine) were also analyzed. When only the CQ photoinitiator was used, a smaller amount of residual monomers was obtained, whereas a larger amount was obtained with PPD. When the two photoinitiators were used in the same matrix, however, no significant changes were observed in relation to the amount of residual TEGDMA monomers. For the addition of the co-initiator, there were no large changes in the extraction of residual monomers. The effect of the two photoactivation sources (halogen lamp and LED) led to small differences in the elution of the two monomers, although all of the resins differed significantly when photoactivated with a LED. Quantum chemical calculations using Density Functional Theory were carried out to characterize several molecular properties of each monomer.

Effect of increased exposure times on amount of residual monomer released from single-step self-etch adhesives

BACKGROUND

The aim of this study was to evaluate the effect of increased exposure times on the amount of residual Bis-GMA, TEGDMA, HEMA and UDMA released from single-step self-etch adhesive systems.

METHODS

Two adhesive systems were used. The adhesives were applied to bovine dentin surface according to the manufacturer's instructions and were polymerized using an LED curing unit for 10, 20 and 40 seconds (n = 5). After polymerization, the specimens were stored in 75% ethanol-water solution (6 mL). Residual monomers (Bis-GMA, TEGDMA, UDMA and HEMA) that were eluted from the adhesives (after 10 minutes, 1 hour, 1 day, 7 days and 30 days) were analyzed by high-performance liquid chromatography (HPLC). The data were analyzed using 1-way analysis of variance and Tukey HSD tests.

RESULTS

Among the time periods, the highest amount of released residual monomers from adhesives was observed in the 10th minute. There were statistically significant differences regarding released Bis-GMA, UDMA, HEMA and TEGDMA between the adhesive systems (p&lt;0.05). There were no significant differences among the 10, 20 and 40 second polymerization times according to their effect on residual monomer release from adhesives (p&gt;0.05).

CONCLUSIONS

Increasing the polymerization time did not have an effect on residual monomer release from single-step self-etch adhesives.

Evaluation of HEMA released from four different adhesive systems by HPLC

PURPOSE

This study evaluated the elution of 2-hydroxyethyl methacrylate (HEMA) from 4 different adhesives, using high-performance liquid chromatography (HPLC).

MATERIALS AND METHODS

The adhesives were applied on a bovine dentin surface and polymerized using an LED curing unit (n=5). After polymerization, specimens were stored in 75% ethanol solution (6 mL). Residual HEMA that was eluted from adhesives (after 10 minutes, 1 hour, 24 hours, 7 days and 30 days) was analyzed using HPLC. Statistical analyses were performed using 1-way ANOVA, Tukey HSD test and paired 2-sample t-test.

RESULTS

There were statistically significant differences among adhesive systems for the cumulative released HEMA and among the time periods (p&lt;0.05). Clearfil SE Bond showed the highest amount of HEMA released, while Easy Bond showed the lowest. Among the time periods, the highest eluted HEMA value was detected in 10 minutes for all adhesives, and elution continued for up to 30 days.

CONCLUSIONS

The HEMA eluted from adhesives was in different amounts, and the elution continued for a long time. The amount of eluted HEMA from adhesives used in this study was not viewed as critical for toxic reactions in biological tissues.

Monomer elution from nanohybrid and ormocer-based composites cured with different light sources

OBJECTIVES

To study monomer elution from four resin-based composites (RBCs) cured with different light sources.

METHODS

Twenty-eight premolars were randomly allocated to four groups. Standardized cavities were prepared and restored with a nanohybrid (Filtek Supreme XT or Tetric EvoCeram), an ormocer (Admira) or a microhybrid RBC (Filtek Z250) which served as control. Buccal restorations were cured with a halogen and oral restorations with an LED light-curing unit. Elution of diurethane dimethacrylate (UDMA), Bisphenol A diglycidylether methacrylate (BisGMA), triethylene glycol dimethacrylate (TEGDMA) and 2-hydroxyethyl methacrylate (HEMA) was analyzed using high-performance liquid chromatography (HPLC) 1h to 28 days post-immersion in 75% ethanol. Data were analyzed using multivariate and repeated measures analysis of variance (α = 0.05).

RESULTS

The greatest elution of UDMA and BisGMA occurred from Tetric EvoCeram and the least from Filtek Z250 (p < 0.05). LED and halogen light-curing units gave similar results for all RBCs (p > 0.05) except Tetric EvoCeram which showed greater elution for the LED unit (p < 0.05). TEGDMA was below the limit of quantification. HEMA eluted in similar concentrations from Filtek Supreme and Tetric EvoCeram (p > 0.05).

SIGNIFICANCE

The two nanohybrid RBCs eluted more cross-linking monomers than the ormocer and the control microhybrid RBC. Continuous elution over 28 days indicates that RBCs act as a chronic source of monomers in clinical conditions. Light source may affect monomer elution since differences were found for one out of four RBCs. Mathematical models for elution kinetics of UDMA and BisGMA indicated two elution mechanisms.