(Ti, O)/Ti and (Ti, O, N)/Ti composite coatings fabricated via PIIID for the medical application of NiTi shape memory alloy

Study of nitrogen implantation in Ti surface using plasma immersion ion implantation & deposition technique as biocompatible substrate for artificial membranes

The present investigation reports the modification of Ti substrates by a plasma technique to enhance their physio-chemical properties as biocompatible substrates for the deposition of artificial membranes. For that purpose, nitrogen ions are implanted into Ti substrate using the plasma immersion ion implantation & deposition (PIII&D) technique in a capacitively coupled radio frequency plasma. The plasma was characterized using optical emission spectroscopy, together with radio frequency compensated Langmuir probe, while the ion current towards the substrate was measured during the implantation process using an opto-electronic device. X-ray photoelectron spectroscopy (XPS) was used for chemical analysis of the surface, confirming the presence of δ-TiN. The penetration depth of the nitrogen ions into the Ti substrate was measured using secondary ions mass spectroscopy (SIMS) while the morphological changes were observed using atomic force microscopy (AFM). A calorimetric assay was used to prove that the TiN samples maintain the biocompatibility of the untreated Ti surface with its native oxide layer. The ion implantation increases the load bearing ability of Ti surface by the formation of α-Ti(N) and δ-TiN phases on the sub-surface of Ti, and maintains the bio compatibility of Ti surface. After the plasma treatment a thin layer of chitosan (CH) was deposited in order to provide a moisturizing matrix for the artificial membrane of 1,2-dipalmitoyl-sn-3- phosphor glycerocholine (DPPC). The CH and subsequently the DPPC were deposited on the plasma deposited TiN substrate by using physical vapor deposition. The formation of artificial membranes was confirmed by AFM, measuring the topography at different temperatures and performing force curves.

Influence of various fluoride agents on working properties and surface characteristics of uncoated, rhodium coated and nitrified nickel-titanium orthodontic wires

OBJECTIVE

To analyze the effect of various fluoride formulations in commercially available agents on working properties of various nickel-titanium orthodontic wires.

MATERIALS AND METHODS

Uncoated (NiTi), rhodium coated (RhNiTi) and nitrified (NNiTi) wires were immersed to dH2O, MiPaste, Elmex and Mirafluor for 1 h. Unloading slope characteristics (average force, bending action of the force and average plateau length) and the percentage of useable constant force during unloading were observed. Surface roughness (Ra) was measured. SEM and EDS were used for observation of the surface.

RESULTS

NiTi had decreased loading and unloading elastic modulus (E) and yield strength (YS) after immersion to MIPaste and Mirafluor. The unloading YS decreased in the RhNiTi by the MIPaste. The loading and unloading YS of the NNiTi increased in Elmex and increased average plateau force. RhNiTi showed higher average plateau length and the percentage of useful constant force during unloading in Mirafluor and the average plateau force lowered after immersion to MIPaste. The unloading slope characteristics for NiTi were affected by all three prophylactic agents, mostly by Mirafluor, and produced significantly lower forces during both loading and unloading, similarly to the NNiTi wires. The RhNiTi had the lowest forces during both loading and unloading in MIPaste. All results were at significance; p<0.05. Difference in Ra was observed for RhNiTi after immersion to the MI Paste (p<0.001; η2=0.761).

CONCLUSION

The NiTi and NNiTi wires lose less working force when combined with Elmex. The RhNiTi improve their working properties with Mirafluor and deteriorate when combined with MiPaste.

Influence of surface layer on mechanical and corrosion properties of nickel-titanium orthodontic wires

OBJECTIVE

To analyze the effect of various coating formulations on the mechanical and corrosion properties of nickel-titanium (NiTi) orthodontic wires.

MATERIALS AND METHODS

Uncoated, rhodium-coated, and nitrified NiTi wires were observed with a three-point-bend test, surface roughness (Ra) measurement, scanning electron microscopy, energy dispersive spectroscopy, and electrochemical testing (open circuit potential, electrochemical impedance spectroscopy, and cyclic polarization scan). Differences in the properties of tested wire types were analyzed with analysis of variance and Tukey post hoc test.

RESULTS

Uncoated and nitrified NiTi wires showed similar mechanical and anticorrosive properties, while rhodium-coated NiTi wires showed the highest Ra and significantly higher modulus of elasticity, yield strength, and delivery of forces during loading but not in unloading. Rhodium-coated NiTi wires also had the highest corrosion current density and corrosion potential, lowest impedance modulus, and two time constants on Bode plot, one related to the Rh/Au coating and the other to underlying NiTi.

CONCLUSION

Working properties of NiTi wires were unaffected by various coatings in unloading. Nitrification improved corrosion resistance. Rhodium coating reduced corrosion resistance and pronounced susceptibility to pitting corrosion in artificial saliva because of galvanic coupling between the noble coating and the base alloy.