Repeatable procedure for evaluating taper damage on femoral stems with modular necks

The effect of manufacturing tolerances on the mechanical environment of taper junctions in modular TKR

Taper design is known to influence corrosive behavior in taper junctions used in modular orthopaedic devices. Manufacturing tolerance of bore-cone tapers is a critical design parameter due to the effect on taper fit, but the effect of variations in manufacturing tolerance on the mechanics of taper junctions has not been well characterized, particularly in modular total knee replacement (TKR). The purpose of this study was to investigate the effect of manufacturing tolerance on stress and micromotion of modular TKR taper junctions. A 3D finite element (FE) model of a modular TKR taper junction was developed and assigned elastoplastic material properties. Model taper geometry was varied by perturbing the angle mismatch by 0.05° between ±0.25° and represented expected variation in manufacturing tolerance. Stress and micromotion were calculated during dynamic FE simulations for each taper junction geometry under varying activity loads and material combinations. Although an increase in angle mismatch generally resulted in higher stress and micromotion, plastic material behavior disrupted this trend for larger angle mismatches. Model predictions corresponded with corrosion behavior evident in vitro. If the FE results obtained here apply in vivo, the absence of elastoplastic material properties in a taper model may grossly overestimate the micromotion and underestimate corrosion behavior and ion release. It is recommended that manufacturing tolerances of bore-cone tapers in modular TKR designs should produce angle mismatches within 0.1° at the taper junction.

The influence of contact conditions and micromotions on the fretting behavior of modular titanium alloy taper connections

Modularity of femoral stems and neck components has become a more frequently used tool for an optimized restoration of the hip joint center and improvement of patient biomechanics. The additional taper interface increases the risk of mechanical failure due to fretting and crevice corrosion. Several failures of titanium alloy neck adapters have been documented in case-reports. An experimental fretting device was developed in this study to systematically investigate the effect of micromotion and contact pressure on fretting damage in contact situations similar to taper interfaces of modular hip prostheses under cyclic loading representative of in vivo load conditions. As a first application, the fretting behavior of Ti-6Al-4V titanium alloy components was investigated. Micromotions were varied between 10μm and 50μm, maximum contact pressures between 400 and 860N/mm(2). All modes of fretting damage were observed: Fretting wear was found for high micromotions in combination with low contact pressures. Fretting fatigue occurred with reduced movement or increased contact pressures. With small micromotions or high normal pressures, low fretting damage was observed. The developed device can be used to evaluate taper design (and especially contact geometry) as well as different materials prior to clinical use.