1
|
Mondal K, Rockne KJ, Drummond JL, O'Brien EP, Chen CC, Hanley L. Dental composite biodeterioration in the presence of oral Streptococci and extracellular metabolic products. J Dent 2024; 142:104861. [PMID: 38278316 DOI: 10.1016/j.jdent.2024.104861] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 12/09/2023] [Revised: 01/21/2024] [Accepted: 01/23/2024] [Indexed: 01/28/2024] Open
Abstract
OBJECTIVE Secondary caries is a primary cause of early restoration failure. While primary dental caries has been extensively researched, our knowledge about the impact of secondary caries on dental restorations is relatively limited. In this study, we examined how different clinically relevant microbially-influenced environments impact the degradation of nano-filled (FIL) and micro-hybrid (AEL) dental composites. METHODS Material strength of two commercial dental composites was measured following incubation in aqueous media containing: i) cariogenic (Streptococcus mutans) and non-cariogenic bacteria (Streptococcus sanguinis) grown on sucrose or glucose, ii) abiotic mixtures of artificial saliva and sucrose and glucose fermentation products (volatile fatty acids and ethanol) in proportions known to be produced by these microorganisms, and iii) abiotic mixtures of artificial saliva and esterase, a common oral extracellular enzyme. RESULTS Nano-filled FIL composite strength decreased in all three types of incubations, while micro-hybrid AEL composite strength only decreased significantly in biotic incubations. The strength of both composites was statistically significantly decreased in all biotic incubations containing both cariogenic and non-cariogenic bacteria beyond that induced by either abiotic mixtures of fermentation products or esterase alone. Finally, there were no statistically significant differences in composite strength decrease among the tested biotic conditions. CONCLUSIONS The results show that conditions created during the growth of both cariogenic and non-cariogenic oral Streptococci substantially reduce commercial composite strength, and this effect warrants further study to identify the mechanism(s). CLINICAL SIGNIFICANCE Dental biofilms of oral Streptococci bacteria significantly affect the mechanical strength of dental restorations.
Collapse
Affiliation(s)
- Karabi Mondal
- Department of Civil, Materials, and Environmental Engineering, University of Illinois-Chicago, Chicago, IL, USA
| | - Karl J Rockne
- Department of Civil, Materials, and Environmental Engineering, University of Illinois-Chicago, Chicago, IL, USA.
| | - James L Drummond
- Professor Emeritus of Restorative Dentistry, University of Illinois Chicago, Chicago, IL, USA
| | - Evan P O'Brien
- Department of Civil, Materials, and Environmental Engineering, University of Illinois-Chicago, Chicago, IL, USA
| | - Chien-Chia Chen
- Department of Chemistry, University of Illinois-Chicago, Chicago, IL, USA
| | - Luke Hanley
- Department of Chemistry, University of Illinois-Chicago, Chicago, IL, USA
| |
Collapse
|
2
|
Mokeem LS, Garcia IM, Melo MA. Degradation and Failure Phenomena at the Dentin Bonding Interface. Biomedicines 2023; 11:biomedicines11051256. [PMID: 37238927 DOI: 10.3390/biomedicines11051256] [Citation(s) in RCA: 4] [Impact Index Per Article: 4.0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/04/2023] [Revised: 04/20/2023] [Accepted: 04/22/2023] [Indexed: 05/28/2023] Open
Abstract
Damage in the bonding interface is a significant factor that leads to premature failure of dental bonded restorations. The imperfectly bonded dentin-adhesive interface is susceptible to hydrolytic degradation and bacterial and enzyme attack, severely jeopardizing restorations' longevity. Developing caries around previously made restorations, also called "recurrent or secondary caries," is a significant health problem. The replacement of restorations is the most prevailing treatment in dental clinics, leading to the so-called "tooth death spiral". In other words, every time a restoration is replaced, more tooth tissue is removed, increasing the size of the restorations until the tooth is eventually lost. This process leads to high financial costs and detriment to patients' quality of life. Since the complexity of the oral cavity makes prevention a challenging task, novel strategies in Dental Materials and Operative fields are required. This article briefly overviews the physiological dentin substrate, features of dentin bonding, challenges and clinical relevance. We discussed the anatomy of the dental bonding interface, aspects of the degradation at the resin-dentin interface, extrinsic and intrinsic factors affecting dental bonding longevity, perspectives on resin and collagen degradation and how these subjects are connected. In this narrative review, we also outlined the recent progress in overcoming dental bonding challenges through bioinspiration, nanotechnology and advanced techniques to reduce degradation and improve dental bonding longevity.
Collapse
Affiliation(s)
- Lamia Sami Mokeem
- Ph.D. Program in Biomedical Sciences, University of Maryland School of Dentistry, Baltimore, MD 21201, USA
| | - Isadora Martini Garcia
- Division of Operative Dentistry, Department of General Dentistry, University of Maryland School of Dentistry, Baltimore, MD 21201, USA
| | - Mary Anne Melo
- Division of Operative Dentistry, Department of General Dentistry, University of Maryland School of Dentistry, Baltimore, MD 21201, USA
| |
Collapse
|
3
|
Mansouri M, O'Brien EP, Mondal K, Chen CC, Drummond JL, Hanley L, Rockne KJ. Stoichiometric models of sucrose and glucose fermentation by oral streptococci: Implications for free acid formation and enamel demineralization. Dent Mater 2023; 39:351-361. [PMID: 36906504 PMCID: PMC10162441 DOI: 10.1016/j.dental.2023.03.001] [Citation(s) in RCA: 2] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/26/2022] [Accepted: 03/01/2023] [Indexed: 03/12/2023]
Abstract
OBJECTIVES The objective of this study is to develop stoichiometric models of sugar fermentation and cell biosynthesis for model cariogenic Streptococcus mutans and non-cariogenic Streptococcus sanguinis to better understand and predict metabolic product formation. METHODS Streptococcus mutans (strain UA159) and Streptococcus sanguinis (strain DSS-10) were grown separately in bioreactors fed brain heart infusion broth supplemented with either sucrose or glucose at 37 °C. Cell mass concentration and fermentation products were measured at different hydraulic residence times (HRT) to determine cell growth yield. RESULTS Sucrose growth yields were 0.080 ± 0.0078 g cell/g and 0.18 ± 0.031 g cell/g for S. sanguinis and S. mutans, respectively. For glucose, this reversed, with S. sanguinis having a yield of 0.10 ± 0.0080 g cell/g and S. mutans 0.053 ± 0.0064 g cell/g. Stoichiometric equations to predict free acid concentrations were developed for each test case. Results demonstrate that S. sanguinis produces more free acid at a given pH than S. mutans due to lesser cell yield and production of more acetic acid. Greater amounts of free acid were produced at the shortest HRT of 2.5 hr compared to longer HRTs for both microorganisms and substrates. SIGNIFICANCE The finding that the non-cariogenic S. sanguinis produces greater amounts of free acids than S. mutans strongly suggests that bacterial physiology and environmental factors affecting substrate/metabolite mass transfer play a much greater role in tooth or enamel/dentin demineralization than acidogenesis. These findings enhance the understanding of fermentation production by oral streptococci and provide useful data for comparing studies under different environmental conditions.
Collapse
Affiliation(s)
- Marzieh Mansouri
- Department of Civil, Materials, and Environmental Engineering, University of Illinois Chicago, Chicago, IL, USA
| | - Evan P O'Brien
- Department of Civil, Materials, and Environmental Engineering, University of Illinois Chicago, Chicago, IL, USA
| | - Karabi Mondal
- Department of Civil, Materials, and Environmental Engineering, University of Illinois Chicago, Chicago, IL, USA
| | - Chien-Chia Chen
- Department of Chemistry, University of Illinois Chicago, Chicago, IL, USA
| | - James L Drummond
- Professor Emeritus of Restorative Dentistry, University of Illinois Chicago, Chicago, IL, USA
| | - Luke Hanley
- Department of Chemistry, University of Illinois Chicago, Chicago, IL, USA
| | - Karl J Rockne
- Department of Civil, Materials, and Environmental Engineering, University of Illinois Chicago, Chicago, IL, USA.
| |
Collapse
|
4
|
Chen CC, Mondal K, Vervliet P, Covaci A, O'Brien EP, Rockne KJ, Drummond JL, Hanley L. Logistic Regression Analysis of LC-MS/MS Data of Monomers Eluted from Aged Dental Composites: A Supervised Machine-Learning Approach. Anal Chem 2023; 95:5205-5213. [PMID: 36917068 DOI: 10.1021/acs.analchem.2c04362] [Citation(s) in RCA: 2] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 03/16/2023]
Abstract
Compound identification by database searching that matches experimental with library mass spectra is commonly used in mass spectrometric (MS) data analysis. Vendor software often outputs scores that represent the quality of each spectral match for the identified compounds. However, software-generated identification results can differ drastically depending on the initial search parameters. Machine learning is applied here to provide a statistical evaluation of software-generated compound identification results from experimental tandem MS data. This task was accomplished using the logistic regression algorithm to assign an identification probability value to each identified compound. Logistic regression is usually used for classification, but here it is used to generate identification probabilities without setting a threshold for classification. Liquid chromatography coupled with quadrupole-time-of-flight tandem MS was used to analyze the organic monomers leached from resin-based dental composites in a simulated oral environment. The collected tandem MS data were processed with vendor software, followed by statistical evaluation of these results using logistic regression. The assigned identification probability to each compound provides more confidence in identification beyond solely by database matching. A total of 21 distinct monomers were identified among all samples, including five intact monomers and chemical degradation products of bisphenol A glycidyl methacrylate (BisGMA), oligomers of bisphenol-A ethoxylate methacrylate (BisEMA), triethylene glycol dimethacrylate (TEGDMA), and urethane dimethacrylate (UDMA). The logistic regression model can be used to evaluate any database-matched liquid chromatography-tandem MS result by training a new model using analytical standards of compounds present in a chosen database and then generating identification probabilities for candidates from unknown data using the new model.
Collapse
Affiliation(s)
- Chien-Chia Chen
- Chemistry, University of Illinois Chicago, Chicago, Illinois 60607, United States
| | - Karabi Mondal
- Materials and Environmental Engineering, University of Illinois Chicago, Chicago, Illinois 60607, United States
| | | | - Adrian Covaci
- Toxicological Center, University of Antwerp, 2610 Wilrijk, Belgium
| | - Evan P O'Brien
- Materials and Environmental Engineering, University of Illinois Chicago, Chicago, Illinois 60607, United States
| | - Karl J Rockne
- Materials and Environmental Engineering, University of Illinois Chicago, Chicago, Illinois 60607, United States
| | - James L Drummond
- Restorative Dentistry, University of Illinois Chicago, Chicago, Illinois 60607, United States
| | - Luke Hanley
- Chemistry, University of Illinois Chicago, Chicago, Illinois 60607, United States
| |
Collapse
|
5
|
Biodegradation of Dental Resin-Based Composite—A Potential Factor Affecting the Bonding Effect: A Narrative Review. Biomedicines 2022; 10:biomedicines10092313. [PMID: 36140414 PMCID: PMC9496159 DOI: 10.3390/biomedicines10092313] [Citation(s) in RCA: 12] [Impact Index Per Article: 6.0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/28/2022] [Revised: 09/04/2022] [Accepted: 09/15/2022] [Indexed: 12/02/2022] Open
Abstract
In recent years, although resin composite has played an important role in the restoration of tooth defects, it still has several disadvantages, including being biodegraded by saliva, bacteria and other enzymes in the oral cavity, which may result in repair failure. This factor is not conducive to the long-term survival of the prosthesis in the mouth. In this article, we review the causes, influencing factors and prevention methods of resin biodegradation. Biodegradation is mainly caused by esterase in saliva and bacteria, which breaks the ester bond in resin and causes the release of monomers. The mechanical properties of the prosthesis can then be affected. Meanwhile, cathepsin and MMPs are activated on the bonding surface, which may decompose the dentin collagen. In addition, neutrophils and residual water on the bonding surface can also aggravate biodegradation. Currently, the primary methods to prevent biodegradation involve adding antibacterial agents to resin, inhibiting the activity of MMPs and enhancing the crosslinking of collagen fibers. All of the above indicates that in the preparation and adhesion of resin materials, attention should be paid to the influence of biodegradation to improve the prosthesis’s service life in the complex environment of the oral cavity.
Collapse
|
6
|
Kumar D, Bolskar RD, Mutreja I, Jones RS. Methacrylate Polymers With “Flipped External” Ester Groups: A Review. FRONTIERS IN DENTAL MEDICINE 2022. [DOI: 10.3389/fdmed.2022.923780] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/13/2022] Open
Abstract
Current resin composites have favorable handling and upon polymerization initial physical properties that allow for efficient material replacement of removed carious tooth structure. Dental resin composites have long term durability limitations due to the hydrolysis of ester bonds within the methacrylate based polymer matrix. This article outlines the importance of ester bonds positioned internal to the carbon-carbon double bond in current methacrylate monomers. Water and promiscuous salivary/bacterial esterase activity can initiate ester bond hydrolysis that can sever the polymer backbone throughout the material. Recent studies have custom synthesized, with the latest advances in modern organic chemical synthesis, a novel molecule named ethylene glycol bis (ethyl methacrylate) (EGEMA). EGEMA was designed to retain the reactive acrylate units. Upon intermolecular polymerization of vinyl groups, EGEMA ester groups are positioned outside the backbone of the polymer chain. This review highlights investigation into the degradation resistance of EGEMA using buffer, esterase, and microbial storage assays. Material samples of EGEMA had superior final physical and mechanical properties than traditional ethylene glycol dimethacrylate (EGDMA) in all degradation assays. Integrating bioinformatics-based biodegradation predictions to the experimental results of storage media analyzed by LC/GC-MS revealed that hydrolysis of EGEMA generated small amounts of ethanol while preserving the strength bearing polymer backbone. Prior studies support investigation into additional custom synthesized methacrylate polymers with “flipped external” ester groups. The long term goal is to improve clinical durability compared to current methacrylates while retaining inherent advantages of acrylic based chemistry, which may ease implementation of these novel methacrylates into clinical practice.
Collapse
|
7
|
Utilizing a degradation prediction pathway system to understand how a novel methacrylate derivative polymer with flipped external ester groups retains physico-mechanical properties following esterase exposure. Dent Mater 2022; 38:251-265. [PMID: 34933759 PMCID: PMC8828700 DOI: 10.1016/j.dental.2021.12.008] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 06/16/2021] [Revised: 08/25/2021] [Accepted: 12/08/2021] [Indexed: 02/03/2023]
Abstract
OBJECTIVE The region of failure for current methacrylates (i.e. derivatives of acrylates) are ester bond linkages that hydrolyze in the presence of salivary and bacterial esterases that break the polymer network backbone. This effect decreases the mechanical properties of methacrylate-based materials. METHODS The ethylene glycol dimethacrylate (EGDMA) or novel ethylene glycol ethyl methacrylate (EGEMA) discs were prepared using 40 µL of the curing mixture containing photo/co-initiators for 40 s in a PTFE mold at 1000 mW/cm2. The degree of conversion was used as a quality control measure for the prepared discs, followed by physical, mechanical, and chemical characterization of discs properties before and after cholesterol esterase treatment. RESULTS After 9 weeks of standardized cholesterol esterase (CEase) exposure, EGDMA discs showed exponential loss of material (p = 0.0296), strength (p = 0.0014) and increased water sorption (p = 0.0002) compared to EGEMA discs. We integrated a degradation prediction pathway system to LC/MS and GC/MS analyses to elucidate the degradation by-products of both EGEMA and EGDMA polymers. GC/MS analysis demonstrated that the esterase catalysis was directed to central polymer backbone breakage, producing ethylene glycol, for EGDMA, and to side chain breakage, producing ethanol, for EGEMA. The flipped external ester group linkage design is attributed to EGEMA showing higher resistance to esterase biodegradation and changes in mechanical and physical properties than EGDMA. SIGNIFICANCE EGEMA is a potential substitute for common macromer diluents, such as EGDMA, based on its resistance to biodegradation effects. This work inspires the flipped external group design to be applied to analogs of current larger, hydrophobic strength bearing macromers used in future dental material formulations.
Collapse
|
8
|
Lima VP, Machado JB, Zhang Y, Loomans BAC, Moraes RR. Laboratory methods to simulate the mechanical degradation of resin composite restorations. Dent Mater 2022; 38:214-229. [PMID: 34949477 PMCID: PMC9903973 DOI: 10.1016/j.dental.2021.12.006] [Citation(s) in RCA: 14] [Impact Index Per Article: 7.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 06/23/2021] [Revised: 12/07/2021] [Accepted: 12/08/2021] [Indexed: 01/21/2023]
Abstract
OBJECTIVES This study reviewed the literature to identify in vitro approaches that have been used to simulate the mechanical degradation and fatigue of resin composite restorations. METHODS A search for articles was carried out in 4 databases and included studies in which composite restorations were bonded to teeth and subject to cyclic loading. Articles were assessed for eligibility, and the following items were the extracted from the included studies: authors, country, year, materials tested, simulation device and details including load magnitude and frequency, number of cycles, type of antagonist, test medium, and temperature. Data were analyzed descriptively. RESULTS The 49 studies included showed a high level of heterogeneity in methods, devices, and test parameters. Nineteen different simulation devices were used, applying loads varying between 30 and 2900 N, and frequencies varying between 0.4 and 12 Hz. The load and frequency used most often were ~ 50 N (63.3%) and 1.5-1.7 Hz (32.7%). The number of cycles varied between 10 K and 2.4 M, 1.2 M was the most prevalent (40.8%). The majority of studies combined cyclic loading with at least one additional aging method: static liquid storage, thermo-mechanical cycling applied simultaneously, and thermal cycling as a discrete aging step were the three most frequent methods. The overall evidence indicated reporting problems, and suggested a lack of clinical validation of the research methods used. SIGNIFICANCE Validation studies, underlying clinical supporting data, and better reporting practices are needed for further improving research on the topic. Specific suggestions for future studies are provided.
Collapse
Affiliation(s)
- Veronica P Lima
- Universidade Federal de Pelotas, Pelotas, RS, Brazil; Radboud University Medical Center, Radboud Institute for Health Sciences, Department of Dentistry, Nijmegen, The Netherlands
| | | | - Yu Zhang
- Department of Preventive and Restorative Sciences, School of Dental Medicine, University of Pennsylvania, USA
| | - Bas A C Loomans
- Radboud University Medical Center, Radboud Institute for Health Sciences, Department of Dentistry, Nijmegen, The Netherlands
| | | |
Collapse
|
9
|
Kumar D, Ghose D, Bolskar RD, Mutreja I, Jones RS. A novel methacrylate derivative polymer that resists bacterial cell-mediated biodegradation. J Biomed Mater Res B Appl Biomater 2021; 110:991-1000. [PMID: 34855282 DOI: 10.1002/jbm.b.34972] [Citation(s) in RCA: 2] [Impact Index Per Article: 0.7] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 04/26/2021] [Revised: 11/02/2021] [Accepted: 11/16/2021] [Indexed: 01/25/2023]
Abstract
This study tests biodegradation resistance of a custom synthesized novel ethylene glycol ethyl methacrylate (EGEMA) with ester bond linkages that are external to the central polymer backbone when polymerized. Ethylene glycol dimethacrylate (EGDMA) with internal ester bond linkages and EGEMA discs were prepared in a polytetrafluoroethylene (PTFE) mold using 40 μl macromer and photo/co-initiator mixture cured for 40 s at 1000 mW/cm2 . The discs were stored in the constant presence of Streptococcus mutans (S. mutans) in Todd Hewitt Yeast + Glucose (THYE+G) media up to 9 weeks (n = 8 for each macromer type) and physical/mechanical properties were assessed. Initial measurements EGEMA versus EGDMA polymer discs showed equivalent degree of conversion (45.69% ± 2.38 vs. 46.79% ± 4.64), diametral tensile stress (DTS; 8.12± 2.92 MPa vs. 6.02 ± 1.48 MPa), and low subsurface optical defects (0.41% ± 0.254% vs. 0.11% ± 0.074%). The initial surface wettability (contact angle) was slightly higher (p ≤ .012) for EGEMA (62.02° ± 3.56) than EGDMA (53.86° ± 5.61°). EGDMA showed higher initial Vicker's hardness than EGEMA (8.03 ± 0.88 HV vs. 5.93 ± 0.69 HV; p ≤ .001). After 9 weeks of S. mutans exposure, EGEMA (ΔDTS-1.30 MPa) showed higher resistance to biodegradation effects with a superior DTS than EGDMA (ΔDTS-6.39 MPa) (p = .0039). Visible and scanning electron microscopy images of EGEMA show less surface cracking and defects than EGDMA. EGDMA had higher loss of material (18.9% vs. 8.5%, p = .0009), relative changes to fracture toughness (92.5% vs. 49.2%, p = .0022) and increased water sorption (6.1% vs. 1.9%, p = .0022) compared to EGEMA discs. The flipped external ester group linkage design is attributed to EGEMA showing higher resistance to bacterial degradation effects than an internal ester group linkage design methacrylate.
Collapse
Affiliation(s)
- Dhiraj Kumar
- Department of Surgical and Developmental Sciences, School of Dentistry, University of Minnesota, Minneapolis, Minnesota, USA
| | - Debarati Ghose
- Department of Surgical and Developmental Sciences, School of Dentistry, University of Minnesota, Minneapolis, Minnesota, USA
| | | | - Isha Mutreja
- Minnesota Dental Research Center for Biomaterials and Biomechanics, Department of Restorative Sciences, School of Dentistry, University of Minnesota, Minneapolis, Minnesota, USA
| | - Robert S Jones
- Department of Surgical and Developmental Sciences, School of Dentistry, University of Minnesota, Minneapolis, Minnesota, USA
| |
Collapse
|
10
|
Cavalcante LM, Ferraz LG, Antunes KB, Garcia IM, Schneider LFJ, Collares FM. Silane content influences physicochemical properties in nanostructured model composites. Dent Mater 2020; 37:e85-e93. [PMID: 33243439 DOI: 10.1016/j.dental.2020.10.022] [Citation(s) in RCA: 6] [Impact Index Per Article: 1.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/05/2020] [Revised: 05/12/2020] [Accepted: 10/24/2020] [Indexed: 11/16/2022]
Abstract
OBJECTIVE To determine the effect of organosilane content on the physicochemical properties of model composites formulated with nano-sized fillers. METHODS Model composites were formulated with dimethacrylate-based monomers, a photoinitiator/co-initiator system and silicon dioxide nano-sized fillers treated with different amounts of 3-methacryloxypropyltrimethoxysilane (MPTS): 1.0 (G1%), 2.0 (G2%), 5.0 (G5%), 7.5 (G7.5%) and 10 (G10%) wt.% relative to SiO2. Non-silanized fillers (G0%) were used in the control group. Degree of conversion (DC) was assessed by Fourier-transformed infrared spectroscopy (ATR-FTIR). Knoop hardness (KHN) and elastic modulus were determined before and after water storage for 4 months. Water sorption (Wsp) and solubility (Wsl) were calculated by successive mass determinations in analytical balance. Surface gloss and roughness were characterized before and after toothbrushing simulation. RESULTS With the exception of those fillers treated with 1% MPTS, DC was not dependent on the silane content. Within the silanized groups, G1% showed the lowest initial and final KHN, without statistical difference from G0%. The elastic modulus was not affected by the silane content, regardless of the storage condition, but those groups formulated with at least 5% silane presented improved values after storage. Silane content did not affect the WSl, but affected Wsp, in which those groups formulated with at least 2 wt.% of MPTS produced a more resistant material than G0%. The use of treated particles with at least 2 wt.% of silane was able to produce materials that did not change their gloss after the brushing process. Additionally, these materials presented lower surface roughness than G0% after the brushing process (p < 0.05). SIGNIFICANCE The concentration of MPTS affected the physicochemical properties of nano-filled composites. Therefore, 2 wt.% of silane was the optimized quantity to produce materials resistant to degradation, both in bulk and surface properties.
Collapse
Affiliation(s)
- Larissa Maria Cavalcante
- School of Dentistry, Federal Fluminense University, Niterói, RJ, Brazil; Nucleus for Dental Biomaterials Research, School of Dentistry, Veiga de Almeida University, Rio de Janeiro, RJ, Brazil.
| | | | - Karinne Bueno Antunes
- Nucleus for Dental Biomaterials Research, School of Dentistry, Veiga de Almeida University, Rio de Janeiro, RJ, Brazil
| | - Isadora Martini Garcia
- Dental Materials Laboratory, School of Dentistry, Federal University of Rio Grande do Sul, Porto Alegre, RS, Brazil
| | - Luis Felipe Jochims Schneider
- School of Dentistry, Federal Fluminense University, Niterói, RJ, Brazil; Nucleus for Dental Biomaterials Research, School of Dentistry, Veiga de Almeida University, Rio de Janeiro, RJ, Brazil
| | - Fabrício Mezzomo Collares
- Dental Materials Laboratory, School of Dentistry, Federal University of Rio Grande do Sul, Porto Alegre, RS, Brazil
| |
Collapse
|
11
|
Influences of Different Air-Inhibition Coatings on Monomer Release, Microhardness, and Color Stability of Two Composite Materials. BIOMED RESEARCH INTERNATIONAL 2019; 2019:4240264. [PMID: 31211136 PMCID: PMC6532316 DOI: 10.1155/2019/4240264] [Citation(s) in RCA: 16] [Impact Index Per Article: 3.2] [Reference Citation Analysis] [Abstract] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 02/11/2019] [Revised: 04/08/2019] [Accepted: 04/18/2019] [Indexed: 12/11/2022]
Abstract
The aim of this study was to evaluate the effect of light-curing protocols on two modern resin composites using different air-inhibition coating strategies. This was accomplished by assessing the amount of monomer elution, surface microhardness, and composite discoloration in different storage conditions. A total of 120 specimens were prepared using Filtek Supreme XTE (3M ESPE, Seefeld, Germany) and CeramX Universal (Dentsply DeTrey, Konstanz, Germany). Specimens were light-cured in air as per manufacturer's instructions or in the absence of oxygen. This latter condition was achieved using three different approaches: (i) transparent polyester strip; (ii) glycerin; (iii) argon gas. Specimens were assessed for release of monomers, Vickers hardness, and discoloration after storage in different solutions. The results were analyzed with ANOVA one-way test followed by Student-Newman-Keuls test. Moreover, multiple comparisons of means were performed using the Student t-test (p<0.05). The amount of monomers released from the tested specimens was very low in all conditions. The presence of oxygen induced some decrease in microhardness. The highest discoloration values, for both materials, were obtained after ageing in red wine. In case finish and polish procedures are awkward to achieve in posteriors composite restoration, light-curing in the absence of oxygen should be considered, especially when performing composite restoration in esthetic areas.
Collapse
|