Bioactive glass and high‐intensity lasers as a promising treatment for dentin hypersensitivity: An in vitro study

A novel mussel-inspired desensitizer based on radial mesoporous bioactive nanoglass for the treatment of dentin exposure: An in vitro study

OBJECTIVES

The dentin exposure always leads to dentin hypersensitivity and the acid-resistant/abrasion-resistant stability of current therapeutic approaches remain unsatisfatory. Inspired by the excellent self-polymerization/adherence activity of mussels and the superior mineralization ability of bioactive glass, a novel radial mesoporous bioactive nanoglass coated with polydopamine (RMBG@PDA) was developed for prevention and management of dentin hypersensitivity.

METHODS

Radial mesoporous bioactive nanoglass (RMBG) was synthesized by the sol-gel process combined with the cetylpyridine bromide template self-assembly technique. RMBG@PDA was synthesized by a self-polymerization process involving dopamine and RMBG in an alkaline environment. Then, the nanoscale morphology, chemical structure, crystalline phase and Zeta potential of RMBG and RMBG@PDA were characterized. Subsequently, the ion release ability, bioactivity, and cytotoxicity of RMBG and RMBG@PDA in vitro were investigated. Moreover, an in vitro experimental model of dentin hypersensitivity was constructed to evaluate the effectiveness of RMBG@PDA on dentinal tubule occlusion, including resistances against acid and abrasion. Finally, the Young's modulus and nanohardness of acid-etched dentin were also detected after RMBG@PDA treatment.

RESULTS

RMBG@PDA showed a typical nanoscale morphology and noncrystalline structure. The use of RMBG@PDA on the dentin surface could effectively occlude dentinal tubules, reduce dentin permeability and achieve excellent acid- and abrasion-resistant stability. Furthermore, RMBG@PDA with excellent cytocompatibility held the capability to recover the Young's modulus and nanohardness of acid-etched dentin.

CONCLUSION

The application of RMBG@PDA with superior dentin tubule occlusion ability and acid/abrasion-resistant stability can provide a therapeutic strategy for the prevention and the management of dentin hypersensitivity.

Evaluation of dentinal tubule occlusion and pulp tissue response after using 980-nm diode laser for dentin hypersensitivity treatment

OBJECTIVES

To evaluate the effectiveness of the 980-nm diode laser for dentinal tubule occlusion, measure the intrapulpal temperature, and investigate the dental pulp response.

MATERIALS AND METHODS

The dentinal samples were randomly divided into G1-G7 groups: control; 980-nm laser irradiation (0.5 W, 10 s; 0.5 W, 10 s × 2; 0.8 W, 10 s; 0.8 W, 10 s × 2; 1.0 W, 10 s; 1.0 W, 10 s × 2). The dentin discs were applied for laser irradiation and analyzed by scanning electron microscopy (SEM). The intrapulpal temperature was measured on the 1.0-mm and 2.0-mm thickness samples, and then divided into G2-G7 groups according to laser irradiation. Moreover, forty Sprague Dawley rats were randomly divided into the laser-irradiated group (euthanized at 1, 7, and 14 days after irradiation) and the control group (non-irradiated). qRT-PCR, histomorphology, and immunohistochemistry analysis were employed to evaluate the response of dental pulp.

RESULTS

SEM indicated the occluding ratio of dentinal tubules in the G5 (0.8 W, 10 s × 2) and G7 (1.0 W, 10 s × 2) were significantly higher than the other groups (p < 0.05). The maximum intrapulpal temperature rises in the G5 were lower than the standard line (5.5 ℃). qRT-PCR showed that the mRNA expression level of TNF-α and HSP-70 upregulated significantly at 1 day (p < 0.05). Histomorphology and immunohistochemistry analysis showed that, compared with the control group, the inflammatory reaction was slightly higher at the 1 and 7 days (p < 0.05) and decreased to the normal levels at 14 days (p > 0.05).

CONCLUSIONS

A 980-nm laser at a power of 0.8 W with 10 s × 2 defines the best treatment for dentin hypersensitivity in terms of compromise between the efficacy of the treatment and the safety of the pulp.

CLINICAL RELEVANCE

The 980-nm laser is an effective option for treating dentin sensitivity. However, we need to ensure the safety of the pulp during laser irradiation.

The Local Release of Teriparatide Incorporated in 45S5 Bioglass Promotes a Beneficial Effect on Osteogenic Cells and Bone Repair in Calvarial Defects in Ovariectomized Rats

With the increase in the population's life expectancy, there has also been an increase in the rate of osteoporosis, which has expanded the search for strategies to regenerate bone tissue. The ultrasonic sonochemical technique was chosen for the functionalization of the 45S5 bioglass. The samples after the sonochemical process were divided into (a) functionalized bioglass (BG) and (b) functionalized bioglass with 10% teriparatide (BGT). Isolated mesenchymal cells (hMSC) from femurs of ovariectomized rats were differentiated into osteoblasts and submitted to in vitro tests. Bilateral ovariectomy (OVX) and sham ovariectomy (Sham) surgeries were performed in fifty-five female Wistar rats. After a period of 60 days, critical bone defects of 5.0 mm were created in the calvaria of these animals. For biomechanical evaluation, critical bone defects of 3.0 mm were performed in the tibias of some of these rats. The groups were divided into the clot (control) group, the BG group, and the BGT group. After the sonochemical process, the samples showed modified chemical topographic and morphological characteristics, indicating that the surface was chemically altered by the functionalization of the particles. The cell environment was conducive to cell adhesion and differentiation, and the BG and BGT groups did not show cytotoxicity. In addition, the experimental groups exhibited characteristics of new bone formation with the presence of bone tissue in both periods, with the BGT group and the OVX group statistically differing from the other groups (p < 0.05) in both periods. Local treatment with the drug teriparatide in ovariectomized animals promoted positive effects on bone tissue, and longitudinal studies should be carried out to provide additional information on the biological performance of the mutual action between the bioglass and the release of the drug teriparatide.

Sol-gel bioactive glass containing biomaterials for restorative dentistry: A review

OBJECTIVE

Bioactive glasses (BAGs) have been researched extensively for dentistry due to their favourable biocompatibility and hard tissue bonding ability. However, the specific application of BAGs produced through sol-gel synthesis in restorative dentistry has not been reviewed previously. This review provides a comprehensive account of the principles behind sol-gel derived BAGs and their investigation for dental tissue restoration materials.

METHODS

A search for in vitro and in vivo studies was performed using the databases Web of Science®, Medline®, Scopus® and Google Scholar®. Articles published over the past 20 years were selected and data on the BAG composition and morphology was extracted. Analysis of the effect of specific BAG additives on the properties of experimental dental materials was also performed.

RESULTS

A majority of BAG particles investigated were spheres ranging in size from 5 nm to ~650 µm. Sol-gel BAGs are mainly applied in the treatment of hypersensitive dentine and for pulp-dentine tissue engineering, while a handful have been used in target drug delivery. BAG fillers are promising additives that result in improved biological properties, antibacterial effects, hardness, acid buffering and remineralization. Unfortunately, some detrimental effects on optical properties have been observed with BAG addition. Additionally, in vivo data, investigations into radiopacity and standardization of test protocols are identified as areas for improvement and further studies.

SIGNIFICANCE

Future work should consider the pertinent issues raised in order to improve the quality of available data and expand knowledge in this area of dental biomaterials research and development.

Bioactive glasses incorporating less-common ions to improve biological and physical properties

Bioactive glasses (BGs) have been a focus of research for over five decades for several biomedical applications. Although their use in bone substitution and bone tissue regeneration has gained important attention, recent developments have also seen the expansion of BG applications to the field of soft tissue engineering. Hard and soft tissue repair therapies can benefit from the biological activity of metallic ions released from BGs. These metallic ions are incorporated in the BG network not only for their biological therapeutic effects but also in many cases for influencing the structure and processability of the glass and to impart extra functional properties. The "classical" elements in silicate BG compositions are silicon (Si), phosphorous (P), calcium (Ca), sodium (Na), and potassium (K). In addition, other well-recognized biologically active ions have been incorporated in BGs to provide osteogenic, angiogenic, anti-inflammatory, and antibacterial effects such as zinc (Zn), magnesium (Mg), silver (Ag), strontium (Sr), gallium (Ga), fluorine (F), iron (Fe), cobalt (Co), boron (B), lithium (Li), titanium (Ti), and copper (Cu). More recently, rare earth and other elements considered less common or, some of them, even "exotic" for biomedical applications, have found room as doping elements in BGs to enhance their biological and physical properties. For example, barium (Ba), bismuth (Bi), chlorine (Cl), chromium (Cr), dysprosium (Dy), europium (Eu), gadolinium (Gd), ytterbium (Yb), thulium (Tm), germanium (Ge), gold (Au), holmium (Ho), iodine (I), lanthanum (La), manganese (Mn), molybdenum (Mo), nickel (Ni), niobium (Nb), nitrogen (N), palladium (Pd), rubidium (Rb), samarium (Sm), selenium (Se), tantalum (Ta), tellurium (Te), terbium (Tb), erbium (Er), tin (Sn), tungsten (W), vanadium (V), yttrium (Y) as well as zirconium (Zr) have been included in BGs. These ions have been found to be particularly interesting for enhancing the biological performance of doped BGs in novel compositions for tissue repair (both hard and soft tissue) and for providing, in some cases, extra functionalities to the BG, for example fluorescence, luminescence, radiation shielding, anti-inflammatory, and antibacterial properties. This review summarizes the influence of incorporating such less-common elements in BGs with focus on tissue engineering applications, usually exploiting the bioactivity of the BG in combination with other functional properties imparted by the presence of the added elements.

The Antibacterial and Remineralization Effect of Silver-Containing Mesoporous Bioactive Glass Sealing and Er-YAG Laser on Dentinal Tubules Treated in a Streptococcus mutans Cultivated Environment

The aim of this study was to evaluate the remineralization and antibacterial effect of silver-containing mesoporous bioactive glass (MBG-Ag) sealing combined with Er:YAG laser irradiation on human demineralized dentin specimens in a Streptococcus mutans cultivated environment. A total of 48 human dentin specimens were randomly divided into four groups. The characteristics of MBG-Ag and the occlusion efficiency of the dentinal tubules were analyzed using X-ray diffraction patterns, Fourier-transform infrared spectroscopy, scanning electron microscope images and energy dispersive X-ray spectroscopy. Moreover, the antibacterial activity against Streptococcus mutans was evaluated by colony formation assay. The results showed that the dentin specimens with Er:YAG laser irradiation can form a melted occlusion with a size of 3–4 µm. MBG-Ag promoted the deposition of numerous crystal particles on the dentinal surface, reaching the deepest penetration depth of 70 μm. The results suggested that both MBG-Ag and laser have the ability to enhance the remineralization and precipitation of hydroxyapatite crystals. While the results showed that MBG-Ag sealing combined with the thermomechanical subablation mode of Er:YAG laser irradiation-induced dense crystalline deposition, reaching a penetration depth of more than 300 µm, silver nanoparticles without good absorption of the Er:YAG laser resulted in a heterogeneous radiated surface. Er:YAG laser irradiation with a low energy and pulse rate cannot completely inhibit the growth of S. mutans, but MBG-Ag sealing reached the bactericidal concentration. It was concluded that the simultaneous application of MBG-Ag sealing and Er:YAG laser treatment can prevent the drawbacks of their independent uses, resulting in a superior form of treatment for dentin hypersensitivity.

In vitro study on how cold plasma affects dentin surface characteristics

PURPOSE

Studies evaluating different features of cold plasma action on dentin surface characteristics are lacking. Thus, this in vitro study aimed to determine the effect of cold plasma under different protocols of exposure time, distance to plasma source, and the association of argon gas with distinct concentrations of oxygen on the wettability, surface energy, total free interaction energy, surface roughness, morphology and chemical composition of dentin.

MATERIAL AND METHODS

One hundred and twenty-five bovine dentin samples were used and divided into twenty-five groups according to the exposure time to plasma (15, 30, or 60 s); distance between plasma source and dentin surface (3 or 6 mm); argon gas without plasma generation; and plasma generated by argon gas and association of argon gas with distinct concentrations of oxygen (2 % or 3 %) (n = 5). Contact angle (θ), surface energy (γs) and total free interaction energy (ΔG) were measured using a goniometer (Krüss), while surface roughness (Ra) was evaluated by a profilometer (Mitutoyo). Representative samples were submitted to scanning electron microscopy (JEOL) to ilustrate the morphology and chemical composition of dentin. Data comparing control group with all experimental groups were submitted to ANOVA followed by Tukey's test (α = .05). Data comparing oxygen gas action at different concentrations and argon gas on dentin characteristics were submitted to non-parametric Kruskal-Wallis test, followed by Dunn test for comparison between the groups and methods (α = 0.05).

RESULTS

In general, argon gas without plasma generation promoted no significant difference on dentin surface characteristics compared to control group (P > .05), differently for the cold plasma that significantly reduced contact angle values and increased total free interaction energy of dentin surface (P < .05). Overall, feeding of oxygen at distinct concentrations promoted significant difference on dentin surface characteristics compared to control group (P < .05). Exposure time and distance protocols interfered with contact angle, surface energy and total free interaction energy analyses for each gas. There was no significant difference on surface roughness (P > .05), morphology and chemical composition of dentin submitted to argon gas, cold plasma, and distinct concentrations of oxygen.

CONCLUSION

In conclusion, plasma generated by argon gas and its feeding with 2 % and 3 % oxygen gas improved the dentin surface characteristics about wettability, surface energy and total free interaction energy. Such treatments preserved the surface roughness, morphology and chemical composition of dentin. The protocols of groups Ar-6mm-15sec, ArO2-3mm-30sec and ArO3-3mm-15sec are recommended for improvement of dentin surface characteristics.

Assessment of Demineralization Inhibition Effects of Dentin Desensitizers Using Swept-Source Optical Coherence Tomography

The purpose of this study was to evaluate the mechanism of action and the inhibiting effects of two types of desensitizers against dentin demineralization using pre-demineralized hypersensitivity tooth model in vitro. In this study, we confirmed that a hypersensitivity tooth model from our preliminary experiment could be prepared by immersing dentin discs in an acetic acid-based solution with pH 5.0 for three days. Dentin discs with three days of demineralization were prepared and applied by one of the desensitizers containing calcium fluoro-alumino-silicate glass (Nanoseal, NS) or fluoro-zinc-silicate glass (Caredyne Shield, CS), followed by an additional three days of demineralization. Dentin discs for three days of demineralization (de3) and six days of demineralization (de6) without the desensitizers were also prepared. The dentin discs after the experimental protocol were scanned using swept-source optical coherence tomography (SS-OCT) to image the cross-sectional (2D) view of the samples and evaluate the SS-OCT signal. The signal intensity profiles of SS-OCT from the region of interest of 300, 500, and 700 µm in depth were obtained to calculate the integrated signal intensity and signal attenuation coefficient. The morphological differences and remaining chemical elements of the dentin discs were also analyzed using scanning electron microscopy and energy-dispersive X-ray spectroscopy. SS-OCT images of CS and NS groups showed no obvious differences between the groups. However, SS-OCT signal profiles for both the CS and NS groups showed smaller attenuation coefficients and larger integrated signal intensities than those of the de6 group. Reactional deposits of the desensitizers even after the additional three days of demineralization were observed on the dentin surface in NS group, whereas remnants containing Zn were detected within the dentinal tubules in CS group. Consequently, both CS and NS groups showed inhibition effects against the additional three days of demineralization in this study. Our findings demonstrate that SS-OCT signal analysis can be used to monitor the dentin demineralization and inhibition effects of desensitizers against dentin demineralization in vitro.

Holmium-Containing Bioactive Glasses Dispersed in Poloxamer 407 Hydrogel as a Theragenerative Composite for Bone Cancer Treatment

Holmium-containing bioactive glasses can be applied in bone cancer treatment because the holmium content can be neutron activated, having suitable properties for brachytherapy applications, while the bioactive glass matrix can regenerate the bone alterations induced by the tumor. To facilitate the application of these glasses in clinical practice, we proposed a composite based on Poloxamer 407 thermoresponsive hydrogel, with suitable properties for applications as injectable systems. Therefore, in this work, we evaluated the influence of holmium-containing glass particles on the properties of Poloxamer 407 hydrogel (20 w/w.%), including self-assembly ability and biological properties. 58S bioactive glasses (58SiO₂-33CaO-9P₂O₅) containing different Ho₂O₃ amounts (1.25, 2.5, 3.75, and 5 wt.%) were incorporated into the hydrogel. The formulations were characterized by scanning electron microscopy, differential scanning calorimetry, rheological tests, and [3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide] MTT cell viability against pre-osteoblastic and osteosarcoma cells. The results evidenced that neither the glass particles dispersed in the hydrogel nor the holmium content in the glasses significantly influenced the hydrogel self-assembly ability (T_mic ~13.8 °C and T_gel ~20 °C). Although, the glass particles considerably diminished the hydrogel viscosity in one order of magnitude at body temperature (37 °C). The cytotoxicity results evidenced that the formulations selectively favored pre-osteoblastic cell proliferation and osteosarcoma cell death. In conclusion, the formulation containing glass with the highest fraction of holmium content (5 wt.%) had the best biological results outcomes aiming its application as theragenerative materials for bone cancer treatment.

Bioactivity assessment of bioactive glasses for dental applications: A critical review

OBJECTIVE

In the context of minimally invasive dentistry and tissue conservation, bioactive products are valuable. The aim of this review was to identify, clarify, and classify the methodologies used to quantify the bioactive glasses bioactivity.

METHODS

Specific search strategies were performed in electronic databases: PubMed, Embase, Cochrane Library, and Scopus. Papers were selected after a review of their title, abstract, and full text. The following data were then examined for final selection: BAG investigated, objectives, criteria, methods, and outcomes.

RESULTS

Sixty-one studies published from 2001 to 2019, were included. The bioactivity of BAG can be evaluated in vitro in contact with solutions, enamel, dentin, or cells. Other studies have conducted in vivo evaluation by BAG contact with dentin and dental pulp. Studies have used various analysis techniques: evaluation of apatite with or without characterization or assessment of mechanical properties. Reprecipitation mechanisms and pulp cell stimulation are treated together through the term 'bioactivity'.

SIGNIFICANCE

Based on these results, we suggested a classification of methodologies for a better understanding of the bioactive properties of BAG. According to all in vitro studies, BAG appear to be bioactive materials. No consensus has been reached on the results of in vivo studies, and no comparison has been conducted between protocols to assess the bioactivity of other bioactive competitor products.