Effect of ionizing radiation on mechanical properties and translucency of monolithic zirconia

Translucency of recent zirconia materials and material-related variables affecting their translucency: a systematic review and meta-analysis

BACKGROUND

Recent forms of translucent zirconia material have been developed, offering a wide range of options and varieties for enhancing aesthetics, making it a preferred choice in the field of prosthetic dentistry. However, there is insufficient understanding regarding the recent types of zirconia materials and their optical behavior. Understanding the variables that influence the translucency of zirconia and identifying strategies to enhance its esthetics are crucial.

PURPOSE

The current systemic review highlights a comprehensive understanding of different zirconia generations in relation to their optical characteristics and evaluates material-related variables affecting their translucency.

METHODS

The present review studied in-vitro studies that evaluated the optical characteristics of different yttria content of yttria stabilized materials. The topics explored were: (1) the different zirconia material generations and their optical behavior; (2) material-related factors that affect their translucency. The research was restricted to online publication in the English language from July 1, 2010, to July 31, 2023, using PubMed, Scopus, and Science Direct resources. The search key terms and their combinations were "zirconia," "translucent zirconia," "cubic zirconia," "highly translucent zirconia," "yttria partially stabilized zirconia," "monolithic zirconia," "translucency," "optical properties," and "light transmission."

RESULTS

The data obtained from fifty-three studies addressed the optical characteristics of various zirconia generations. They reported that changing yttria content had a significant impact on translucency. Different kinds of zirconia ceramics of the same generation have varying translucencies. Achieving optimum aesthetics with monolithic zirconia is challenging due to factors related to material aspects such as the presence of additives, point defects, microstructure, thickness, phase distribution, and sintering conditions.

CONCLUSIONS

Newly developed monolithic dental zirconia ceramics have improved aesthetics and translucency. However, additional research is necessary to evaluate their performance and long-term durability.

TRIAL REGISTRATION

This systematic review was registered in PROSPERO, under number CRD42023474482.

Surface and bulk properties of zirconia as a function of composition and aging

Yttria-stabilized zirconia (Y-SZ) materials with different levels of translucency have been used for indirect dental restorations. Y-SZ composition and microstructure are modified to improve translucency, and it is not clear how these materials respond to aging. This study evaluated the effect of hydrothermal aging (HA) performed in an autoclave on the properties of four dental Y-SZ materials with different compositions. Sintered bar-shaped specimens (14 x 4 x 2 mm) were prepared from four different zirconia-based materials (n = 40): low translucency 3 mol % Y-SZ (3Y-LT; Ceramill ZI, Amann Girrbach); high translucency 4 mol % Y-SZ (4Y-HT; Ceramill Zolid); and two high translucency 5 mol % Y-SZ (5Y-HT - Lava Esthetic, 3M; 5Y-SHT - Ceramill Zolid FX). Fully sintered specimens were exposed to HA for different times (control - 0 h, 5 h, 10 h, or 15 h at 134 °C, 2 bar pressure) and characterized for surface roughness, flexural strength (three-point bending), hardness and elastic modulus (nanoindentation), surface wettability (sessile drop technique) and crystalline content (x-ray diffraction, XRD). Data was analyzed by two-way ANOVA and Tukey HSD (p < 0.05). Zirconia composition significantly affected roughness (p = 0.016). Zirconia*aging interaction affected flexural strength (p = 0.012), surface wettability (p < 0.001), and hardness (p = 0.002). Zirconia composition (p = 0.011) and aging (p = 0.001) affected elastic modulus, while the interaction effect was not significant (p = 0.94). HA affects zirconia-based materials in different degrees. For 3Y-LT and 4Y-HT, surface and bulk properties were affected by aging to a similar extent. However, surface and bulk properties may change during clinical use as a result of prolonged degradation of Y-SZ.

Surface characterization of different surface treatments associations with plasma and bonding analysis of Y-TZP and the veneering ceramic

OBJECTIVES

To characterize the surface of zirconia (Y-TZP) submitted to different surface treatments (with and without plasma associations) and to evaluate the shear bond strength (SBS) between veneering ceramic (VC) and Y-TZP after different aging methods.

METHODS

301 Y-TZP specimens were fabricated and distributed into 7 groups: C (control): no treatment; Al: airborne abrasion with 27 μm Al₂O₃ particle; L: liner; P: plasma; Al + L: airborne + liner; Al + P: airborne + plasma; P + L: plasma + liner. The Y-TZP surface was characterized by SEM, EDS, AFM, surface profilometry, surface-free energy (SFE), and XRD. SBS between Y-TZP and VC was verified after three aging protocols: initial, after hydrothermal aging (autoclave for 5 h), or thermal fatigue (30,000 baths - 5-55 °C). One- (profilometry, SFE) and two-way ANOVA (SBS), and Tukey's HSD test were used.

RESULTS

For the plasma groups, a full globular surface coverage was observed (SEM, AFM). Si was found for Al, L, Al + L, and P + L. Roughness was lower for C, P, and Al + P. For SFE, the highest values were found when the liner was applied (>74.59 nm/Nm). The highest monoclinic content was observed for Al + L (6.96%) and Al + P (5.86%). For the initial period, Al and P + L presented the lowest SBS values (<5.85 MPa; P > 0.331). The highest SBS values were found for L, P, and P + L (hydrothermal aging) and for P, L, Al + L, and Al + P (thermal fatigue).

SIGNIFICANCE

Changes in Y-TZP topography and the SBS with the VC were found, according to treatments performed. Plasma treatment improved SBS and did not cause phase transformation.

Mechanical performance of a hybrid zirconia developed through hydrothermal treatment and Room-Temperature Atomic Layer Deposition (RT-ALD)

OBJECTIVE

A silica-based nanofilm has been successfully deposited via Room-Temperature Atomic Layer Deposition (RT-ALD) on the surface of a glass. The purpose of this study was to evaluate the mechanical performance of a hybrid interface created between yttria-stabilized zirconia (Y-PSZ) transformed layer and silica-based nanofilm via RT-ALD.

MATERIAL AND METHODS

Fully-sintered Y-PSZ (14 × 4.0 × 1.5 mm) specimens in different translucencies (MO, MT, LT; IPS e.max Zircad, Ivoclar Vivadent) were distributed in 5 groups: control (C - no treatment); hydrothermal treatment (HT- 15h, 134°C, 2 bar); alumina blasting (B - 50 μm Al₂O₃); RT-ALD silica deposition (S); HT followed by silica deposition (HTS). RT-ALD cycles consisted of the sequential exposure of specimens to tetramethoxysilane orthosilicate (TMOS - 60s) and ammonium hydroxide (NH₄OH - 10 min) vapors in 40 cycles. Mechanical performance was analyzed by flexural strength (FS) (n = 10) and fatigue failure load (staircase method; n = 20) tests. Surface hardness (H) and Young's modulus (YM) were analyzed by nanoindentation. For surface chemical and topographical characterization, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) were performed. Data from surface H, YM, FS, and fatigue limit (FL) were analyzed by two-way analysis of variance (ANOVA).

RESULTS

The interaction between material and treatment had a significant effect on FS (p < 0.001). The FS values ranged from 436.23 MPa to 856.65 MPa. HT resulted in the highest FS (856.65 MPa) for LT and the lowest FS (436.23 MPa) for MO zirconia. For all materials, S and B treatments resulted in similar FS values (p > 0.410). S did not affect FL when compared to the C group (p > 0.277) for any material investigated. HTS resulted in higher FL than S for LT and MO materials (p < 0.001). Surface hardness and modulus were similar between control and S-treated specimens for all materials analyzed. XPS analysis showed homogeneous silica content after 20 and 40 RT-ALD cycles, and SEM did not show significant changes in surface morphology between C and S-treated specimens.

CONCLUSION

RT-ALD resulted in effective silica deposition without any deleterious effect on zirconia-based materials mechanical properties. Alumina blasting promoted higher alteration on surface topography. HT prior to S resulted in superior FL (for MO and MT) and flexural strength (MO) for some of the materials investigated.

Influence of the chemical composition of monolithic zirconia on its optical and mechanical properties. Systematic review and meta-regression

PURPOSE

This systematic review set out to investigate the influence of chemical composition and specimen thickness of monolithic zirconia on its optical and mechanical properties. Meta-analysis and meta-regression analyzed the effects of variations in percentages of yttrium, aluminum, and specimen thickness of monolithic zirconia.

STUDY SELECTION

The review followed recommendations put forward in the PRISMA checklist. An electronic search for relevant articles published up to October 2019 was conducted in the Pubmed, Cochrane, Scopus, Scielo, and Web of Science databases, with no language limits and articles published in the last 10 years. From 167 relevant articles; applying inclusion criteria based on the review's PICO question, 26 articles were selected for qualitative synthesis (systematic review) and 24 for quantitative synthesis (meta-analysis). Experimental in vitro studies published were selected and their quality was assessed using the modified Consort scale for in vitro studies of dental materials.

RESULTS

The variables yttrium, aluminum and thickness were analyzed in random effects models, observing high heterogeneity ( > 75%), and finding statistically significant influences on the properties of monolithic zirconia (p<0.05).

CONCLUSIONS

Within the review's limitations, it may be concluded that variations in the percentage of yttrium and aluminum influence the optical and mechanical properties of monolithic zirconia, making it more or less esthetic and resistant in relation to each variable. The clinical implications of these findings can help select the most appropriate type of zirconia to meet the different clinical needs when restoring different regions (posterior or anterior).