Effect of a modified adhesive system with encapsulated arginine and calcium carbonate on dentin permeability

Novel resin-based material containing β-tricalcium phosphate nanoparticles for the reduction of dentin permeability

OBJECTIVES

To synthesize and characterize a novel dentin adhesive containing Beta-Tricalcium Phosphate (β-TCP) nanoparticles and test its ability to reduce dentin permeability (dP).

METHODS

Experimental adhesives were prepared by mixing Bis-GMA, TEGDMA, HEMA (50/25/25 wt.%), photo-initiators, and inhibitors. The following groups were tested: Experimental adhesives without β-TCP (Exp.); with 10 wt.% β-TCP (Exp.10 wt.% β-TCP); with 15 wt.% β-TCP (Exp.15 wt.% β-TCP), Scotchbond Multi-Purpose (SBMP) and Clearfil SE Protect Bond (CFPB). Degree of conversion (DC%, 10 and 20 s); Flexural Strength (FS), Knoop Hardness (KHN), and Cell Viability (OD%) tests were performed. dP was evaluated by hydraulic conductance, using human dentin disks (n=12), at three-time intervals: post-EDTA (T0); post-treatment (T1); and post-erosion/abrasion cycling (T2). Data were statistically analyzed (α=0.05).

RESULTS

For all groups, exposure time for 20 s presented a higher DC% than for 10 s. For FS, filled adhesives did not differ from unfilled and from CFPB. Experimental adhesives did not differ among them and showed lower KHN than the commercial products. Cell viability did not differ among adhesives, except Exp. 15 wt.%, which showed lower OD% than Exp., Exp. 10% and, CFPB. For dP, only Exp.10 and 15 wt.% β-TCP did not present difference between the times T1 and T2. After cycling, Exp.10 wt.% β-TCP presented lower permeability than Exp. and CFPB.

CONCLUSIONS

The incorporation of 10 wt.% β-TCP nanoparticles into the resin-based dental material did not affect its mechanical properties and biocompatibility, and promoted the greatest reduction in dentin permeability, sustaining this effect under erosive/abrasive challenges.

CLINICAL SIGNIFICANCE

A novel resin-based dental material containing β-TCP nanoparticles was able to reduce dentin permeability, maintaining its efficacy after erosive/abrasive challenges. The synthesized material did not affect dental pulp cell viability and might be promising for other conditions that require dental remineralization, such as tooth wear and dental caries.

Performance of self-etching adhesives on caries-affected primary dentin treated with glutaraldehyde or silver diamine fluoride

OBJECTIVES

to evaluate the quality and stability of adhesive interfaces established by self-etching adhesives on caries-affected primary dentin (CAD) treated with glutaraldehyde (GA) or silver diamine fluoride (SDF).

METHODS

42 primary molars were exposed to a microbiological caries-inducing protocol and divided into 6 groups according to the adhesive system (Clearfil SE - CL or FL Bond II - FL) and pretreatment (water, GA or SDF) applied on CAD. One tooth from each group was analyzed for surface modification using infrared spectroscopy. Crowns were restored with resin composite (n = 36) and cut into beams and slices. The beams were subjected to microtensile testing, Raman spectroscopy and SEM after 24 h and 6 months of storage. The slices were analyzed using Micro-Raman spectroscopy to determine the diffusion zone thickness (DZ) in each period. Data were analyzed by ANOVA and Tukey or Kruskal-Wallis and Dunn tests (α = 0.05%).

RESULTS

SDF reduced the immediate bond strength for both adhesives. The control groups showed a decrease in BS after 6 months in artificial saliva. GA increased immediate DZ for FL, while SDF had the opposite effect on CL. GA decreased the DZ for FL at 6 months. There was a predominance of adhesive failures with areas of cohesive dentin fractures within control groups.

SIGNIFICANCE

Modifications caused by dentin surface treatments may directly affect the performance of adhesive systems and the quality and stability of adhesive restorations.