Influence of etching mode and composite resin type on bond strength to dentin using universal adhesive system

Bond strength and marginal adaptation of resin composites and correlations with clinical results

OBJECTIVES

Due to innumerable confounding factors and a high number of types and brands of dental restorative materials, the clinical performance of restorative materials are sought predicted by various in vitro tests. However, only few such tests have been found to correlate well with clinical findings. Thus, the present study determined the in vitro dentin bond strength and marginal adaptation of Class II restorations and correlated the results to their clinical outcomes.

METHODS

Dentin bond strength (µTBS and µSBS) and marginal gap formation of Class II restorations (replica technique and SEM) were measured after 24 h and 6 m water storage using eight combinations of adhesive and resin composite. Clinical outcomes (mean survival time, Hazard Ratio, annual failure rate; n = 10.695) were gained from a data set of a retrospective multicenter study of direct restorations.

RESULTS

Significant differences were found for dentin bond strength and marginal gap formation between the restorative material groups, and negative effects of long-term storage were observed. µTBS correlated significantly with certain clinical outcomes of Class I restorations, while µSBS correlated with certain clinical outcomes of Class II, III, IV and V restorations. Marginal gap formation in enamel and number of paramarginal fractures correlated with certain clinical outcomes of Class II restorations.

SIGNIFICANCE

Using the same restorative materials in vitro as in vivo, gave significant, but weak correlations between in vitro bond strength or marginal adaptation and clinical outcomes, lending support to the use of in vitro tests in early stages of material selection.

Equivalence study of the resin-dentine interface of internal tunnel restorations when using an enamel infiltrant resin with ethanol-wet dentine bonding

This preregistered ex vivo investigation examined the dentinal hybrid layer formation of a resinous infiltrant (Icon), with reference to both thickness (HLT) and homogeneity when combined with modified tunnel preparation (occlusal cavity only) and internal/external caries infiltration. The adhesives Syntac and Scotchbond MP were used as controls (Groups 1 and 3) or in combination with Icon (Groups 2 and 4). A split-tooth design using healthy third molars from 20 donors resulted in 20 prepared dentine cavities per experimental group. The cavity surfaces (n = 80) were etched (37% H3PO4), rinsed, and air-dried. Rewetting with ethanol was followed by application of the respective primers. After labeling with fluorescent dyes, either Syntac Adhesive/Heliobond or Scotchbond MP Adhesive was used alone or supplemented with Icon. HLT, as evaluated by scanning electron microscopy, did not significantly differ (P > 0.05), and confocal laser scanning microscopy revealed homogeneously mixed/polymerized resin-dentine interdiffusion zones in all groups. Icon can be successfully integrated into an ethanol-wet dentine bonding strategy, and will result in compact and homogeneous hybrid layers of comparable thickness considered equivalent to the non-Icon controls, thus allowing for preservation of the tooth's marginal ridge and interdental space in the case of internal/external infiltration of proximal caries.

Repair of monolithic zirconia restorations with different direct resin composites: effect on the fatigue bonding and mechanical performance

OBJECTIVE

The study aims to evaluate the shear bond and flexural strength fatigue behavior of yttrium-stabilized zirconia (4YSZ) repaired using different resin composites.

MATERIALS AND METHODS

Cylindric specimens of 4YSZ were obtained for the bond strength (Ø = 6 mm, 1.5 mm of thickness) and biaxial flexural strength (Ø = 15 mm, 1 mm of thickness) fatigue tests and divided into 3 groups according to the repair resin composite: EVO (nanohybrid), BULK (bulk-fill), and FLOW (flowable). The zirconia surface was air-abraded with alumina particles, a 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) primer was applied, and the resin composite was build-up over the zirconia. Fatigue shear bond strength and flexural fatigue strength tests were performed (n = 15). One-way ANOVA and Tukey post hoc tests were carried out for both outcomes, besides scanning electron microscopy and finite element analysis.

RESULTS

The repair material affected the fatigue shear bond strength of zirconia ceramic. The BULK group (18.9 MPa) depicted higher bond strength values than FLOW (14.8 MPa) (p = 0.04), while EVO (18.0 MPa) showed similar results to both groups. No effect was observed for the mechanical behavior (p = 0.53). The stress distribution was similar for all groups.

CONCLUSION

The repair of yttrium-stabilized zirconia (4YSZ) ceramics with bulk-fill resin composites was the best option for high fatigue bond strength. However, the fatigue mechanical performance was similar regardless of the applied repair material.

CLINICAL RELEVANCE

The repair of yttrium-stabilized zirconia (4YSZ) monolithic restorations may be performed with nanohybrid and bulk-fill resin composites in order to promote longevity in the treatment.

Do bioactive materials show greater retention rates in restoring permanent teeth than non-bioactive materials? A systematic review and network meta-analysis of randomized controlled trials

OBJECTIVES

To answer the following research question: does the clinical evaluation of restorations on permanent teeth with bioactive materials show greater retention rates than those with non-bioactive materials?

MATERIALS AND METHODS

A search strategy was used in the following databases: MEDLINE via PubMed, Scopus, Web of Science, LILACS, BBO, Embase, The Cochrane Library, and OpenGrey. Randomized controlled trials (RCTs), with a minimum of 2-year follow-up and evaluating at least one bioactive material in permanent teeth were included. Risk of bias was detected according to the Cochrane Collaboration tool for assessing the risk of bias (RoB 2.0), and network meta-analysis was performed using a random-effects Bayesian-mixed treatment comparison model.

RESULTS

Twenty-seven studies were included. The success of the restorations was assessed using modified USPHS system in 24 studies and the FDI criteria in 3 studies. Network meta-analysis revealed three networks based on restoration preparations. Resin composites were ranked with higher SUCRA values, indicating a greater likelihood of being the preferred treatment for class I, II, and III restorations. In class V, resin-modified glass ionomer cement was ranked with the highest value.

CONCLUSION

Bioactive restorative materials showed similar good clinical performance in terms of retention similarly to conventional resin composites.

CLINICAL SIGNIFICANCE

The findings must be interpreted with caution because many RCT on restorative materials aim to verify the equivalence of new materials over the gold standard material rather than their superiority. The present systematic review also suggests that new RCT with longer follow-up periods are necessary.

Five-Year Clinical Performance of Complex Class II Resin Composite and Amalgam Restorations-A Retrospective Study

The aim of this retrospective study was to investigate the clinical performance of posterior complex resin composite (RC) and amalgam (AM) restorations after a five-year period. One hundred and nineteen complex Class II restorations placed by dental students were evaluated using the USPHS criteria. Data were analyzed using Chi-square, Mann-Whitney, and Wilcoxon tests at a 0.05 level of significance. After five years, the percentages of clinically satisfactory complex Class II RC and AM restorations were 78% and 76.8%, respectively. The main reasons for the failure of AM restorations included secondary caries (Bravo-10.1%), defective marginal adaptation (Charlie-8.7%), and fracture of the tooth (Bravo-7.2%). RC restorations presented failures related to the fracture of the restoration (Bravo-16%) and defective marginal adaptation (Charlie-8.2%). There was a significantly higher incidence of secondary caries for AM restorations (AM-10.1%; RC-0%; p = 0.0415) and a higher number of fractures for RC restorations (AM-4.3%; RC-16%; p = 0.05). Regarding anatomy, AM restorations presented a significantly higher number of Alfa scores (49.3%) compared to RC restorations (22.4%) (p = 0.0005). The results of the current study indicate that complex class II RC and AM restorations show a similar five year clinical performance.

Effect of pretreatment with matrix metalloproteinase inhibitors on the durability of bond strength of fiber posts to radicular dentin

Objectives

Application of matrix metalloproteinases inhibitors has been suggested to improve the durability of resin–dentin bonding. The purpose of this study was to evaluate the effect of dimethyl sulfoxide (DMSO), carbodiimide (EDC), and chlorhexidine (CHX) treatment on the push‐out bond strength of fiber posts to radicular dentin.

Materials and Methods

24 extracted premolars were assigned randomly to 4 groups after root canal treatment and post space preparation (n = 6). In the first, second, and third groups, radicular dentin was treated with 1 ml of 5% DMSO, 0.3 M EDC, and 2% CHX, respectively. The fourth group (control) received no treatment. The root canals were primed with ED primer II, and the fiber posts were cemented with Panavia F2.0. In each group, half of the specimens were subjected to the push‐out test and the other half to 3000 thermal cycles before testing. Data were analyzed using two‐way analysis of variance via SPSS version 20 (p < .05).

Results

Among the nonthermocycled specimens, the values of push‐out bond strength were observed in the control, EDC, CHX, and DMSO groups, in decreasing order. Among the thermocycled specimens, the values were observed in the control, EDC, DMSO, and CHX groups in decreasing order. Thermocycling had a significant adverse effect on the push‐out bond strength (p = .015), but the effect of material (p = .375), and the interaction effect of material and thermocycling (p = .998) were not significant.

Conclusions

Application of CHX, DMSO, and EDC had no significant effect on the bond strength of fiber posts to radicular dentin.

In Vitro Study of Mechanical Properties of Teeth Restored with Bulk-fill and Universal Composites Using Different Dentin Adhesives

Background: The most common dental materials are resin composite direct restorative materials and dentin adhesives, which are marketed with different techniques, application recommendations, and compositions, making it difficult to choose the most suitable material and method for different cases.

The present study aimed to investigate mechanical properties of teeth restored with universal and bulk-fill composites, by using different dentin adhesives and techniques, under in vitro conditions.

Material and methods: The study was carried out on freshly extracted premolar and molar teeth. After cavity preparation, the teeth were restored with conventional and bulk-fill resin composites, using different adhesive techniques. To assess the effect of the cavity preparation, the direct restoration, and the adhesive protocol on the tooth structure, a transillumination method and Vickers’ microhardness measurements were carried out.

Results: The universal composite showed an average hardness of 55.35 HV at the occlusal level of the restoration, while the bulk-fill composite showed an average of 79.93 HV at the same level. A statistically significant difference was found between the hardness values of the two composites (p = 0.02). The transillumination test revealed micro-fissures in the tooth structure in the first phase after cavity preparation and also after polymerization.

Conclusions: The bulk-fill composite showed higher hardness values than the universal composite. The tested dentin adhesives did not significantly affect the hardness of the dentin at the level of the adhesive interface. Fissures can appear in any phase of the direct restoration, after cavity preparation and polymerization.

Bonding Performance of Universal Adhesives Applied to Nano-Hydroxyapatite Desensitized Dentin Using Etch-and-Rinse or Self-Etch Mode

The study assessed the bonding performance of three universal adhesives on desensitized dentin with etch-and-rinse mode or self-etch mode after nano-hydroxyapatite (nHAp)-based desensitizers application. Simulated sensitive dentin specimens were prepared and separated into four groups: no treatment as the negative control, groups desensitized by Biorepair toothpaste, Dontodent toothpaste, or nHAp paste. Three universal adhesives of All-Bond Universal, Single Bond Universal, and Clearfil Universal Bond with etch-and-rinse or self-etch mode were bonded to the desensitized dentin specimens separately, followed by resin composite build-ups. Micro-tensile bond strength was measured using a micro-tensile tester. The wettability of desensitized dentin was evaluated by the contact angle of the adhesives. Resin infiltration was observed by confocal laser scanning microscopy. Dentin tubular occlusion and nanoleakage were observed by scanning electron microscope. The results showed that the etch-and-rinse or self-etch mode of each adhesive showed similar bond strength when bonding to nHAp-based desensitized dentin. The dentin surface was partially covered by desensitizers after desensitization. Compared with the self-etch mode, stronger demineralization and more reopened dentin tubules were observed in the etch-and-rinse mode after acid etching; longer resin tags and more nanoleakage in the resin-dentin interface were observed when using the etch-and-rinse mode. When bonding to nHAp-based desensitized dentin with universal adhesives, no significant difference in bond strength was found between self-etch mode or etch-and-rinse mode; while the latter produced more nanoleakage in the resin-dentin interfaces.