Evaluation of surface characteristic and bacterial adhesion of low-shrinkage resin composites

3D-printed denture base resins: Glazing as an alternative to improve surface, mechanical, and microbiological properties

PURPOSE

To evaluate the impact of glazing denture base resins (heat-polymerized and 3D-printed) on surface, mechanical, and microbiological properties.

MATERIALS AND METHODS

Discs (10 × 3 mm) and bars (64 × 10 × 3.3 ± 0.2 mm) were manufactured using heat-polymerized denture base resin (CT) and 3D-printed denture base resin (Yller [YL], Prizma [PZ] and PrintaX [PX]). These were divided into two groups: unglazed and glazed. Surface roughness (Ra), wettability (contact angle), brightness (GU), and topography (via scanning electron microscopy) were assessed, along with microbiological analysis of dual-species biofilms (Streptococcus mitis and Candida albicans) and Knoop microhardness on discs (n = 10). Flexural strength testing was conducted separately on bars (n = 20). Half of the specimens subjected to surface and mechanical characterizations were thermocycled (10,000 cycles). Mann-Whitney test (p < 0.05) and simple and multiple linear regression analysis (p < 0.20) were employed to evaluate the impact of glazing on denture base resins.

RESULTS

The application of glaze reduced roughness by 0.33 µm and water contact angle by 8.47º, while increasing brightness by 21.30 units (p < 0.001) for 3D-printed resins compared to CT. After thermal cycling, roughness and wettability increased, while brightness decreased (p < 0.05). The glaze also increased hardness, with no adverse effects from thermal cycling (p < 0.001), and enhanced flexural strength for PZ compared to CT (p < 0.001). Additionally, C. albicans colonization decreased by 7.79 log CFU/mL in mixed biofilms for 3D-printed resins compared to CT (p < 0.05).

CONCLUSIONS

The application of glaze resulted in smoother, brighter, and harder surfaces for the 3D-printed resins, while also reducing biofilm colonization.

Surface characteristics and bacterial adhesion on single-shade composite resins: A comparative in vitro study of one-step versus multi-step polishing techniques

This study evaluated the effects of two polishing systems, OptraGloss (G; one-step) and OptiDisc (D; multi-step), on surface roughness (SR), contact angle (CA), surface free energy (SFE), and bacterial adhesion on three single-shade composite resins: Omnichroma (O), ZenChroma (Z), and Charisma Diamond One (C). Data for SR, CA, SFE, and adhesion of Streptococcus mutans (S. mutans) and Streptococcus mitis (S. mitis) were analyzed using one-way ANOVA, Tukey post-hoc tests, and Pearson correlation (α=0.05). Multi-step polishing groups (OD, ZD, and CD) exhibited significantly lower SR (0.18, 0.18, and 0.29 µm, respectively) compared to OG (0.46 µm), ZG (0.30 µm), and CG (0.44 µm) (p<0.05). The highest CA was observed in ZG (91.6º). S. mitis adhesion was greater than S. mutans in all groups except OG. A significant correlation was observed between SR and the adhesion of S. mutans (r=0.693, p<0.001). Polishing systems applied to single-shade composite resins did not impact the SFE but affected SR, and bacterial adhesion.

Effect of different polishing systems on surface roughness and gloss values of single-shade resin composites

BACKGROUND

The aim of this study was to evaluate variations in the surface roughness and gloss of different single-shade resin composites after polishing with a range of systems.

METHODS

In total, 120 specimens were prepared from three different types of single-shade resin composites (supra-nanospherical-Omnichroma, nanohybrid-Charisma Diamond One, and microhybrid- Essentia Universal). The specimens were placed in distilled water and stored at 37 °C for 24 h. Each resin composite (n = 40) was divided into four groups (n = 10) according to the finishing/polishing (F/P) system: Mylar strip (control), Sof-Lex (multi-step), Twist Dia (two-step), and OneGloss (one-step). Surface roughness and gloss were measured. Surface characteristics were evaluated by atomic force microscopy (AFM) and a scanning electron microscope (SEM). A two-way analysis of variance (ANOVA) and Tukey's honestly significant difference test were used for statistical analysis (p < 0.05).

RESULTS

Among all the composites, both the highest surface roughness and lowest gloss values were obtained in the groups treated with the OneGloss polishing system (p < 0.05). Compared with all the composites, Omnichroma had the lowest surface roughness and highest gloss values (except Twist Dia) both unpolished and after polishing with all the F/P systems (p < 0.05). All composites treated with the Twist Dia F/P system had similar gloss values. The results of the AFM and SEM analyses were consistent with the surface roughness measurements.

CONCLUSIONS

The gloss values of both the microhybrid and nanohybrid composites after F/P using the two-step system was superior to that of the traditional multistep system. The surface of the supra-nanofilled resin-based composite was smoother than that of both the microhybrid and nanohybrid composites.

Bacterial adhesion to composite resins produced by additive and subtractive manufacturing

The aim of this study was to evaluate the surface roughness and contact angle of composite resins produced by CAD/CAM milling and three-dimensional (3D) printing for permanent restorations as well as the adhesion of S. mutans and S. sanguinis bacteria to these composites. Three CAD/CAM milling composite resins (Vita Enamic-VE, Cerasmart-CE, Lava Ultimate-LU) and three 3D printing resins (Varseo Smile Crown plus-VSC, Saremco print Crowntech-SPC, Formlabs 3B Permanent crown-FLP) were selected. Twenty samples were prepared for each group. Using a contact profilometer, the surface roughness was determined, and an optical goniometer was used to quantify the contact angle. To evaluate the bacterial adhesion, composite specimens were immersed in mucin containing artificial saliva. All samples were incubated for 24 h at 37°C in 5% CO2. CFUs were determined by counting colonies after the incubation period. Surface roughness values of test samples were the highest in the Group VSC [0.46 (0.14) µm], whereas the lowest values were found in the Group LU [0.23 (0.05) µm]. There was no statistically significant difference between the groups in contact angle values (p > 0.05). The S. mutans adhesion extent on the Group SPC was statistically higher compared to all other materials with p < 0.05. For S. sanguinis, the lowest bacterial adhesion value was recorded in Group CE (3.00 × 104 CFU/ml) and statistically significant differences were found with Group VE and VSC (p < 0.05). Different digital manufacturing techniques and material compositions can affect the surface roughnesses of composite resins. All composite resin samples have hydrophobic characteristics. Microbial adhesion of the tested composite resins may be varied depending on the bacterial species. S. mutans showed much more adhesion to these materials than S. sanguinis.

Interaction between microorganisms and dental material surfaces: general concepts and research progress

Bacterial adhesion to dental materials’ surfaces is the initial cause of dental materials-related infections. Therefore, inhibiting bacterial adhesion is a critical step in preventing and controlling these infections. To this end, it is important to know how the properties of dental materials affect the interactions between microorganisms and material surfaces to produce materials without biological contamination. This manuscript reviews the mechanism of bacterial adhesion to dental materials, the relationships between their surface properties and bacterial adhesion, and the impact of bacterial adhesion on their surface properties. In addition, this paper summarizes how these surface properties impact oral biofilm formation and proposes designing intelligent dental material surfaces that can reduce biological contamination.

Tests of Dental Properties of Composite Materials Containing Nanohybrid Filler

Complex composite materials are used in many areas of dentistry. Initially, chemically hardened materials were also used, and in this group nanohybrid composites are highly valued. They are often used today, mainly for the direct reconstruction of damaged hard tooth tissue materials for rebuilding damaged tissues using indirect adhesive techniques. The research was conducted to determine the mechanical properties of materials with nanofillers. The article focuses on methods of important test methods for dental prosthetics: resilience, abrasion, wear test, impact strength, hardness, SEM, and chemical analysis. As part of this work, five different series of hybrid composites with nano-fillers were tested. The mechanical properties of composites, such as compressive strength, microhardness, flexural strength, and modulus of elasticity, depend mainly on the type, particle size, and amount of filler introduced. The obtained test results showed that the type and amount of nanofiller have a significant influence on the mechanical and tribological properties. The introduction of nanofillers allowed us to obtain higher mechanical properties compared to classic materials discussed by other researchers. The study observed a change in vibrations in the IR spectrum, which allowed a comparison of the organic structures of the studied preparations.

Growth control agent for filamentous fungi: FDM based 3D printed cubes for suspended Aspergillus sojae fermentation

The main problem for submerged fermentation of filamentous fungi is the nutrition limitation with high cell density or cell leakage by the uncontrollable hyphae, clusters, or pellets. There are several techniques such as microparticle, immobilization, pH shifting, substrate limitation etc. for controlling filamentous fungi growth on submerged fermentation. In this research, FDM (Fused Deposition Modelling) based 3D printed cubes is used for growth control agent of recombinant Aspergillus sojae for the first time. Lattice structure sizes, number of cubes and pH were chosen to be main factors of fermentation in order to study the combine effect of the factors on A. sojae fermentation. The results revealed that specific activity values are improved from 2045.96 U/mg (the highest control activity) to 3291.67 U/mg with lower pellet sizes and controllable growth. FDM based 3D printed cubes was successfully controlled the recombinant Aspergillus sojae fermentation and enhanced β-mannanase production. In addition, this research was also showed that FDM based 3D printed cubes also have the potential to be used as immobilization materials like SLS based 3D printed products in further research.