Remineralization effects of self-assembling peptide P11 -4 associated with three materials on early enamel carious lesions: An in vitro study

Effect of self-assembling peptide and other remineralizing agents on preventing initial enamel lesions around orthodontic brackets: An in vitro comparative study

OBJECTIVE

To investigate and compare the effect of self-assembling peptide SAP (P_11-4), casein phosphopeptide-amorphous calcium phosphate fluoride paste (CPP-ACPF), and fluoride varnish (FV) on preventing enamel demineralization around orthodontic brackets.

MATERIAL AND METHODS

Orthodontic brackets were bonded to the buccal surfaces of 80 freshly extracted human maxillary premolars. Teeth were randomly assigned to four groups (n=20) according to the remineralizing agent used as follows: SAP (P_11-4) group (Curodont™ Protect/Credentis), CPP-ACPF group (MI Paste Plus®/Recaldent™), fluoride varnish group (Profluoride varnish®/VOCO), and control group. All products were applied according to the manufacturer's instructions. Specimens were cycled in daily refreshed demineralizing and remineralizing solutions for 8h and 16h, respectively, for 28 days. The calcium/phosphorus ratio (Ca/P) and surface microhardness (SMH) were evaluated at baseline and at two and four weeks. Two-way ANOVA (analysis of variance), one-way ANOVA and repeated measures ANOVA were used for statistical analysis.

RESULTS

Two-way ANOVA demonstrated significant differences between remineralizing agents and time points. After 4 weeks, the SAP (P_11-4) group had had significantly higher Ca/P ratio and SMH (1.68±0.11 and 346.47±55.38) compared to other groups, followed by CPP-ACPF (1.52±0.19 and 283.53±64.75), FV (1.37±0.14 and 262.80±82.98), and the control group (1.31±0.10 and 213.00±41.95). Significantly higher Ca/P ratio and SMH were observed at 2 weeks in the control group (1.44±0.10 and 269.63±57.37) and FV group (1.52±0.09 and 321.17±55.24) compared to 4 weeks. No significant differences were found regarding Ca/P ratio and SMH at 2 weeks in the CPP-ACPF (1.55±0.15 and 295.14±53.88) and SAP P_11-4 groups (1.64±0.10 and 320.18±58.04) compared to 4 weeks.

CONCLUSION

SAP (P_11-4) had the greatest remineralizing efficacy compared to FV and CPP-ACPF. Moreover, extended period of time improved the preventive efficacy of SAP (P_11-4) compared to the other regimens.

Adhesion and whitening efficacy of P11-4 self-assembling peptide and HAP suspension after using NaOCl as a pre-treatment agent

Background

This study evaluated the adhesion and whitening efficacy of a mixture of hydroxyapatite and P11-4 self-assembling peptide (HAP-peptide) on bovine enamel after pre-treatment with low-concentrated sodium hypochlorite (NaOCl).

Methods

Fifty-two caries-free bovine incisors were selected. 50 teeth were randomly allocated to five groups (n = 10). The first group was treated with a mixture of 6.25 wt% HAP and 5 ml P11-4 peptide, using NaOCl 3% as pre-treatment. Second, third and fourth groups were treated with 6.25 wt% HAP, 5 ml P11-4 peptide, and NaOCl 3%, respectively. In the fifth group, only water was applied (control group). The color of samples was measured using a spectrophotometer (USB4000-VIS-NIR-ES, Ostfildern, Germany). To evaluate color changes, ΔE values were statistically analyzed. Finally, adherence of HAP particles on two enamel surfaces with and without pre-treatment with NaOCl was analyzed with SEM.

Results

It was observed that the ΔE of the HAP-peptide suspension after pre-treatment with NaOCl was significantly stronger than the control group. In contrast, the overall color changes of separate applications of HAP, peptide, and NaOCl did not differ notably from the control group. SEM observations confirmed that pre-treatment with NaOCl resulted in a more pronounced coverage of HAP on the enamel surface.

Conclusions

Pre-treatment with a low-concentrated NaOCl enhanced the adherence of the HAP layer on the enamel surface, resulting in a stronger whitening effect.

Trial registration

The peptide-HAP suspension is effective in improving tooth whiteness.

Effectiveness of Self-Assembling Peptide (P11-4) in Dental Hard Tissue Conditions: A Comprehensive Review

The limitations on the use of fluoride therapy in dental caries prevention has necessitated the development of newer preventive agents. This review focusses on the recent and significant studies on P11-4 peptide with an emphasis on different applications in dental hard tissue conditions. The self-assembling peptide P11-4 diffuses into the subsurface lesion assembles into aggregates throughout the lesion, supporting the nucleation of de novo hydroxyapatite nanocrystals, resulting in increased mineral density. P11-4 treated teeth shows more remarkable changes in the lesion area between the first and second weeks. The biomimetic remineralisation facilitated in conjunction with fluoride application is an effective and non-invasive treatment for early carious lesions. Despite, some studies have reported that the P11-4 group had the least amount of remineralised enamel microhardness and a significantly lower mean calcium/phosphate weight percentage ratio than the others. In addition, when compared to a low-viscosity resin, self-assembling peptides could neither inhibit nor mask the lesions significantly. Moreover, when it is combined with other agents, better results can be achieved, allowing more effective biomimetic remineralisation. Other applications discussed include treatment of dental erosion, tooth whitening and dentinal caries. However, the evidence on its true clinical potential in varied dental diseases still remains under-explored, which calls for future cohort studies on its in vivo efficacy.