In situ synthesis of molecularly imprinted nanoparticles in porous support membranes using high-viscosity polymerization solvents

Green molecularly imprinted polymers for sustainable sample preparation

The use of molecularly imprinted polymers in sample preparation as selective sorbent materials has received great attention during the last years leading to analytical methods with unprecedented selectivity. However, with the progressive implementation of Green Analytical Chemistry principles, it is necessary to critically review the greenness of synthesis and further use of molecularly imprinted polymers in sample preparation. Accordingly, in the present review, the different steps and strategies for the preparation of molecularly imprinted polymers, the used reagents, as well as their incorporation to microextraction techniques are reviewed from a green perspective and recent alternatives to make the use of molecularly imprinted polymers more sustainable are provided.

Microsphere Polymers in Molecular Imprinting: Current and Future Perspectives

Molecularly imprinted polymers (MIPs) are specific crosslinked polymers that exhibit binding sites for template molecules. MIPs have been developed in various application areas of biology and chemistry; however, MIPs have some problems, including an irregular material shape. In recent years, studies have been conducted to overcome this drawback, with the synthesis of uniform microsphere MIPs or molecularly imprinted microspheres (MIMs). The polymer microsphere is limited to a minimum size of 5 nm and a molecular weight of 10,000 Da. This review describes the methods used to produce MIMs, such as precipitation polymerisation, controlled/'Living' radical precipitation polymerisation (CRPP), Pickering emulsion polymerisation and suspension polymerisation. In addition, some green chemistry aspects and future perspectives will also be given.

Preparation of Molecularly Imprinted Microspheres by Precipitation Polymerization

Molecularly imprinted polymers (MIPs) gained an expansively growing interest in the past few decades. After an initial, explorative period of preparing MIPs exclusively with bulk polymerization, new polymer synthesis routes have been adapted to overcome the drawbacks of the traditional method. Among these the most appealing is precipitation polymerization that results in nano- and microspheres with narrow size distribution and makes the production of MIPs more straightforward. Here, we describe a precipitation polymerization protocol for a common small molecule template, propranolol that is carried out in the conventional way, in dilute monomer solution. Moreover, a modified precipitation polymerization protocol from concentrated monomer solution is presented for a diclofenac imprinted polymer which makes the synthesis even more versatile and circumvents the disadvantages of the dilute solution conditions.

Molecularly imprinted microspheres prepared by precipitation polymerization at high monomer concentrations

Highly crosslinked polymer microparticles have been prepared by precipitation polymerization using high monomer loadings (≥25 v/v %) which generally would lead to bulk monoliths. The microparticle format was achieved by the use of non-solvating diluents either alone or in combination with co-solvents. Two distinct morphologies were observed. Monodisperse smooth microspheres were obtained using a thermodynamically good co-solvent whereas segmented irregular particles were formed with poorer co-solvents. It has been found that during polymerization the forming polymer particles were enriched in the co-solvent and this effect was more pronounced when good co-solvents were used. The type of functional monomer, crosslinker and co-solvent, and the non-solvent/co-solvent ratio were identified as influential parameters on the microparticle morphology. With the proposed methodology molecularly imprinted microparticles have been prepared successfully for three different templates, naproxen, diclofenac and toltrazuril using various functional monomers, crosslinkers and polymerization solvent mixtures.