Linking the Gold Nanoparticles Formation Kinetics with Their Morphology

The Kinetics of the Redox Reaction of Platinum(IV) Ions with Ascorbic Acid in the Presence of Oxygen

In this work, the kinetics of the redox reaction between platinum(IV) chloride complex ions and ascorbic acid is studied. The reduction process of Pt(IV) to Pt(II) ions was carried out at different reagent concentrations and environmental conditions, i.e., pH (2.2-5.1), temperature (20-40 °C), ionic strength (I = 0.00-0.40 M) and concentrations of chloride ions (0.00-0.40 M). The kinetic traces during the reduction process were registered using stopped-flow spectrophotometry. Based on the kinetic traces, the rate constants were determined, and the kinetic equations were proposed. It was shown that in the mild acidic medium (pH = 2.5), the reduction process of Pt(IV) to Pt(II) ions is more complex in the presence of oxygen dissolved in the aqueous solutions. For these processes, the values of the enthalpy and entropy of activation were determined. Moreover, the mechanism of the reduction of Pt(IV) to Pt(II) ions was proposed. The presented results give an overview of the process of the synthesis of platinum nanoparticles in the solution containing oxygen, in which the reduction process of Pt(IV) to Pt(II) ions is the first step.

Batch Reactor vs. Microreactor System for Efficient AuNP Deposition on Activated Carbon Fibers

The process of noble metals ions recovery and the removal small fraction of nanoparticles from waste solution is an urgent topic not only from the economic but also ecology point of view. In this paper, the use of activated carbon fibers (ACF) as a “trap” for gold nanoparticles obtained by a chemical reduction method is described. The synthesized nanoparticles were stabilized either electrostatically or electrosterically and then deposited on carbon fibers or activated carbon fibers. Moreover, the deposition of metal on fibers was carried out in a batch reactor and a microreactor system. It is shown, that process carried out in the microreactor system is more efficient (95%) as compared to the batch reactor and allows for effective gold nanoparticles removal from the solution. Moreover, for similar conditions, the adsorption time of the AuNPs on ACF is shortened from 11 days for the process carried out in the batch reactor to 2.5 min in the microreactor system.

Green method for efficient PdNPs deposition on carbon carrier in the microreactor system

The synthesis of palladium nanoparticles and conditions of their deposition on active carbon fibers in the microreactor was described. All processes related with metal ion reduction, nucleation, and autocatalytic growth of particles as well as their deposition were carried out in the microreactor in only one cycle. Synthesis of palladium nanoparticles was carried out under different conditions, i.e., changing the initial concentration of metal ions and the reductant, at 40 °C. Depending on the conditions imposed, the nanoparticles of different size (hydrodynamic radius change from 12 to 37 nm) and shape (spherical, cube, pyramid) were obtained. It was also shown that flow conditions allow for much more efficient Pd deposition on active carbon fibers than the process carried out in the batch. It was observed that for concentrations of Pd(II) ions higher than 0.2 mM, the degree of fiber surface coverage increased significantly in comparison with the batch process.