Nanoparticle Formulation of AEA and BAEA Cellulose Carbamates Increases Biocompatibility and Antimicrobial Activity

Protein repellent anti-coagulative mixed-charged cellulose derivative coatings

This study describes the formation of cellulose based polyelectrolyte charge complexes on the surface of biodegradable polycaprolactone (PCL) thin films. Anionic sulphated cellulose (CS) and protonated cationic amino cellulose (AC) were used to form these complexes with a layer-by-layer coating technique. Both polyelectrolytes were analyzed by charge titration methods to elucidate their pH-value dependent protonation behavior. A quartz crystal microbalance with dissipation (QCM-D) in combination with X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM) were used to follow the growth, stability and water content of up to three AC/CS bi-layers in aqueous environment. This was combined with coagulation studies on one, two and three bilayers of AC/CS, measuring the thrombin formation rate and the total coagulation time of citrated blood plasma with QCM-D. Stable mixed charged bilayers could be prepared on PCL and significantly higher masses of AC than of CS were present in these complexes. Strong hydration due to the presence of ammonium and sulphate substituents on the backbone of cellulose led to a significant BSA repellent character of three bilayers of AC/CS coatings. The total plasma coagulation time was increased in comparison to neat PCL, indicating an anticoagulative nature of the coatings. Surprisingly, a coating solely composed of an AC layer significantly prolonged the total coagulation time on the surfaces although it did not prevent fibrinogen deposition. It is suggested that these cellulose derivative-based coatings can therefore be used to prevent unwanted BSA deposition and fibrin clot formation on PCL to foster its biomedical application.

Preparation and Properties of Stereocomplex of Poly(lactic acid) and Its Amphiphilic Copolymers Containing Glucose Groups

The stereocomplex of poly(lactic acid) containing glucose groups (sc-PLAG) was prepared by solution blending from equal amounts of poly(l-lactic acid) (PLLA) and poly(d-lactic acid-co-glucose) (PDLAG), which were synthesized from l- and d-lactic acid and glucose by melt polycondensation. The methods, including 1H nuclear magnetic resonance spectroscopy (1H NMR), gel permeation chromatography (GPC), differential scanning calorimetry (DSC), X-ray diffraction (XRD), fourier transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), polarizing microscope (POM), scanning electron microscope (SEM), transmission electron microscope (TEM), and contact angle were used to determine the effects of the stereocomplexation of enantiomeric poly(lactic acid) (PLA) units, the amphiphilicity due to glucose residues and lactic acid units, and the interaction of glucose residues with lactic units on the crystallization performance, hydrophilicity, thermal stability, and morphology of samples. The results showed PDLAG was multi-armed, and partial OH groups of glucose residues in PDLAG might remain unreacted. The molecular weight (Mw), dispersity (Ɖ), and glucose proportion in the chain of PDLAG thereby had significant effects on sc-PLAG. There were the stereocomplexation of enantiomeric lactic units and the amphiphilic self-assembly of PDLAG in sc-PLAG, which resulted in glucose groups mainly in the surface phase and lactic units in the bulk phase. The sc-PLAG only possessed the stereocomplex crystal owing to the interaction between nearly equimolar of l-lactic units of PLLA and d-lactic units of PDLAG, and had no homo-crystallites of l- or d-lactic units, which improved the melting temperature (Tm) of sc-PLAG about 50 °C higher than that of PLLA. Glucose groups in sc-PLAG played an important role by forming heterogeneous nucleation, promoting amphiphilic self-assembly, and affecting the ordered arrangement of lactic units. The glass transition temperature (Tg), the melting temperature (Tm), crystallinity, crystallization rate, and water absorption of sc-PLAG showed similar changes with the increased glucose content in feeding. All these parameters increased at first, and the maximum appeared as glucose content in feeding about 2%, such as the maximum crystallinity of 48.8% and the maximum water absorption ratio being 11.7%. When glucose content in feeding continued increasing, all these performances showed a downward trend due to the decrease of arrangement regularity of lactic acid chains caused by glucose groups. Moreover, the contact angle of sc-PLAG decreased gradually with the increased glucose content in feeding to obtain the minimum 77.5° as the glucose content in feeding being 5%, while that of PLLA was 85.0°. The sc-PLAG possessed a regular microsphere structure, and its microspheres with a diameter of about 200 nm could be observed. In conclusion, sc-PLAG containing proper glucose amount could effectively enhance the crystallinity, hydrophilicity, and thermal stability of PLA material, which is useful for drug delivery, a scaffold for tissue engineering, and other applications of biomedicine.

Recent Advances on Cellulose-Based Nano-Drug Delivery Systems: Design of Prodrugs and Nanoparticles

BACKGROUND

Cellulose being the first abundant biopolymers in nature has many fascinating properties, including low-cost, good biodegradability, and excellent biocompatibility, which made cellulose a real potential material to create nano-drug delivery systems (nano-DDS). This review aims to present and discuss some remarkable recent advances on the drug delivery applications of cellulosebased prodrugs and nanoparticles.

METHODS

By searching the research literatures over last decade, a variety featured studies on cellulosebased nano-DDS were summarized and divided into prodrugs, prodrug nanoparticles, solid or derivative nanopartilces, amphiphilic copolymer nanoparticles, and polyelectrolyte complex nanoparticles. Various methods employed for the functionalization, pharmacodynamic actions and applications were described and discussed.

RESULTS

Many types of cellulose-based nano-DDS can ensure efficient encapsulation of various drugs and then overcome the free drug molecule shortcomings. Among all the method described, cellulosebased amphiphilic nanoparticles are most frequently used. These formulations have the higher drug loading capability, a simple and flexible way to achieve multi-functional. Apart from hydrophilic or hydrophobic modification, cellulose or its derivatives can form nanoparticles with different small molecules and macromolecules, leading to a large spectrum of cellulose-based nano-DDS and providing some unexpected advantages.

CONCLUSION

Thorough physicochemical characterization and profound understanding of interactions of the cellulose-based nano-DDS with cells and tissues is indispensable. Moreover, studies toward technics parameter optimization and scale up from the laboratory to production level should be undertaken. The development of intravenous and orally applicable cellulose-based nano-DDS will be an important research area, and these systems will have more commercial status in the market.

Chitosan: The One and Only? Aminated Cellulose as an Innovative Option for Primary Amino Groups Containing Polymers

The aim of this study was the synthesis and in vitro characterization of aminated cellulose as alternative excipient to chitosan. The aldehyde form of cellulose was generated via the oxidative cleavage of vicinal diols by the addition of increasing concentrations of sodium periodate. The insertion of primary amines was achieved by reductive amination with ammonia. The degree of substitution was calculated via primary amino group quantification using a 2,4,6-trinitrobenzenesulfonic acid assay. Mucoadhesiveness was examined by adopting the rotating-cylinder method and tensile studies using porcine intestinal mucosa. Hydration was evaluated at pH 2-11. The successful formation of aldehydes as well as a subsequent introduction of up to 311.61 micromoles per gram of primary amines were proven to correlate with the amount of added periodate. There was a 3- to 14-fold prolongation in the mucosal residence time of the new polymer in comparison to chitosan, as measured by the rotating-cylinder method. Although cationic cellulose did not reach the maximum detachment force of chitosan, the total work of adhesion of the newly synthesized cellulose derivate was higher than that of chitosan. The higher the degree of amination, the higher the degree of hydration in neutral and alkaline aqueous media was. Compared to chitosan, the novel cationic cellulose derivative displays improved mucoadhesive properties as well as sufficient hydration at physiological pH. Therefore, aminated cellulose is a promising alternative to the cationic polymers, such as chitosan, used thus far.