Adsorption of Chitosan onto Poly(D,L-lactic acid) Particles: A Physico-Chemical Investigation

In Vitro Characterization of Inhalable Cationic Hybrid Nanoparticles as Potential Vaccine Carriers

In this study, PGA-co-PDL nanoparticles (NPs) encapsulating model antigen, bovine serum albumin (BSA), were prepared via double emulsion solvent evaporation. In addition, chitosan hydrochloride (CHL) was incorporated into the external phase of the emulsion solvent method, which resulted in surface adsorption onto the NPs to form hybrid cationic CHL NPs. The BSA encapsulated CHL NPs were encompassed into nanocomposite microcarriers (NCMPs) composed of l-leucine to produce CHL NPs/NCMPs via spray drying. The CHL NPs/NCMPs were investigated for in vitro aerosolization, release study, cell viability and uptake, and stability of protein structure. Hybrid cationic CHL NPs (CHL: 10 mg/mL) of particle size (480.2 ± 32.2 nm), charge (+14.2 ± 0.72 mV), and BSA loading (7.28 ± 1.3 µg/mg) were produced. The adsorption pattern was determined to follow the Freundlich model. Aerosolization of CHL NPs/NCMPs indicated fine particle fraction (FPF: 46.79 ± 11.21%) and mass median aerodynamic diameter (MMAD: 1.49 ± 0.29 µm). The BSA α-helical structure was maintained, after release from the CHL NPs/NCMPs, as indicated by circular dichroism. Furthermore, dendritic cells (DCs) and A549 cells showed good viability (≥70% at 2.5 mg/mL after 4–24 h exposure, respectively). Confocal microscopy and flow cytometry data showed hybrid cationic CHL NPs were successfully taken up by DCs within 1 h of incubation. The upregulation of CD40, CD86, and MHC-II cell surface markers indicated that the DCs were successfully activated by the hybrid cationic CHL NPs. These results suggest that the CHL NPs/NCMPs technology platform could potentially be used for the delivery of proteins to the lungs for immunostimulatory applications such as vaccines.

Understanding the adsorption mechanism of chitosan onto poly(lactide-co-glycolide) particles

Polyelectrolyte-coated nanoparticles or microparticles interact with bioactive molecules (peptides, proteins or nucleic acids) and have been proposed as delivery systems for these molecules. However, the mechanism of adsorption of polyelectrolyte onto particles remains unsolved. In this study, cationic poly(lactide-co-glycolide) (PLGA) nanoparticles were fabricated by adsorption of various concentrations of a biodegradable polysaccharide, chitosan (0-2.4g/L), using oil-in-water emulsion and solvent evaporation techniques. The particle diameter, zeta-potential, and chitosan adsorption of chitosan-coated PLGA nanoparticles confirmed the increase of polyelectrolyte adsorption. Five adsorption isotherm models (Langmuir, Freundlich, Halsey, Henderson, and Smith) were applied to the experimental data in order to better understand the mechanism of adsorption. Both particle diameter and chitosan adsorption increased with chitosan concentration during adsorption. A good correlation was obtained between PLGA-chitosan nanoparticle size and adsorbed chitosan on the surface, suggesting that the increased particle size was primarily due to the increased chitosan adsorption. The zeta-potential of chitosan-coated PLGA nanoparticles was positive and increased with chitosan adsorbed until a maximum value (+55mV) was reached at approximately 0.4-0.6g/L; PLGA nanoparticles had a negative zeta-potential (-20mV) prior to chitosan adsorption. Chitosan adsorption on PLGA nanoparticles followed a multilayer adsorption behavior, although the Langmuir monolayer equation held at low concentrations of chitosan. The underlying reasons for adsorption of chitosan on PLGA nanoparticles were thought to be the cationic nature of chitosan, high surface energy and microporous non-uniform surface of PLGA nanoparticles.