Synthesis of a Degradable High-Performance Epoxy-Ended Hyperbranched Polyester

Degradation and recycling of cured thermosetting epoxy resins are major challenges to the industry. Here, a low-viscosity, degradable epoxy-ended hyperbranched polyester (DEHP) is synthesized by a reaction between epichlorohydrin and a carboxyl-ended hyperbranched polyester (DCHP) obtained from an esterification between citric acid and maleic anhydride. The chemical structures of DCHP and DEHP were characterized by Fourier transform infrared and ¹H NMR. DEHP has a positive effect on reinforcing and toughening of the diglycidyl ether of bisphenol-A (DGEBA). With an increase in the content and molecular weight of DEHP, the mechanical performances of the cured DEHP/DGEBA composites, including the tensile, flexural, and impact strengths, increase first and then decrease. The improvements on the tensile, flexural, and impact strengths were 34.2-43.4%, 35.6-48.1%, and 117.9-137.8%, respectively. Moreover, the DEHP also promotes degradation of the cured DEHP/DGEBA composites. The degree of degradation of the cured DEHP/DGEBA composites increases with an increase of the DEHP content and molecular weight. The composites containing 12 wt % DEHP can be degraded completely in only about 2 h at about 90 °C, compared with the degradation degree (35%) of cured DGEBA, indicating good degradation and recycling properties of the DEHP.

A starch based sustainable tough hyperbranched epoxy thermoset

A starch based sustainable high performing tough hyperbranched epoxy thermoset with exceptionally high tensile adhesive strength, and biodegradability was demonstrated.

Self-assembly of amido-ended hyperbranched polyester films with a highly ordered dendritic structure

Self-assemblies fabricated from dendrimers and amphiphilic polymers have demonstrated remarkable performances and a wide range of applications. Direct self-assembly of hyperbranched polymers into highly ordered macrostructures with heat-resistance remains a big challenge due to the weak amphiphilicity of the polymers. Here, we report the self-assembly of amphiphilic amido-ended hyperbranched polyester (HTDA-2) into millimeter-size dendritic films using combined hydrogen bond interaction and solvent induction. The self-assembly process and mechanism have been studied. Hydrogen bond interaction between amido-ended groups assists the aggregation of inner and outer chains of the HTDA-2, resulting in phase separation and micelle formation. Some micelles attach to and grow on the glass substrate like seedlings. Other micelles move to the seedlings and connect with their branches via solvent induction and hydrogen bond interaction, leading to the fabrication of highly ordered crystalline dendritic films that show high heat-resistance. HTDA-2 can further self-assemble into sheet crystals on the dendritic films.

Surface hybrid self-assembly, mechanism, and crystalline behavior of a carboxyl-ended hyperbranched polyester/platinum complex

The self-assembly of hyperbranched polymers has attracted much attention because of their wide application. In this article, we report a new facile surface self-assembly method for a carboxyl-ended hyperbranched polyester/platinum complex (HTD-3-Pt) and obtain ordered structural microrods with a length of 10-20 μm and a width of 1 μm. The length and diameter of the self-assembled microrods could be increased to 300-600 μm and 4-5 μm, respectively, by hierarchical self-assembly. The main factors affecting the morphology of the self-assemblies, including temperature, time, solvent and solubility parameter, and relative humidity were discussed by transmission/reflection polarizing optical microscopy (TRPOM), SEM, and HRSEM. The indications for the coordination bond (-COOPt) included the appearance of a new peak at 1606 cm(-1) and its shifting to 1634 cm(-1) in the FT-IR spectra, the disappearance of the C 1s peak at about 288.6 eV, and the increase in the O 1s electron binding energy in the XPS spectra. Furthermore, an interesting crystal property of the HTD-3-Pt self-assemblies was discovered and confirmed by XRD. The study results from the surface self-assembly mechanism suggest that the coordination induction of the platinum ion play a key role in driving microphase separation between the intermolecular chains and end groups of the HTD-3-Pt to form the microrod self-assemblies. Another interesting finding was that HTD-3-Pt showed a higher catalytic activity for hydrosilylation than did a traditional homogeneous catalyst.